Low-odor red phosphorus flame-retardant reinforced polyamide material

A polyamide, low-odor technology, applied in the field of red phosphorus flame-retardant polyamide materials, can solve the problems of dark yellow, unclear effect of red phosphorus flame-retardant nylon, dark gray, etc., to achieve improved odor level, clear effect, visual comfortable effect

Active Publication Date: 2018-03-13
CGN JUNER NEW MATERIALS +1
View PDF11 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the deep red limit of red phosphorus, most of the products made of red phosphorus flame-retardant reinforced polyamide materials are formulated into dark colors such as black or deep red. At the same time, the high-energy laser b

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-odor red phosphorus flame-retardant reinforced polyamide material
  • Low-odor red phosphorus flame-retardant reinforced polyamide material
  • Low-odor red phosphorus flame-retardant reinforced polyamide material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0053] Each embodiment and comparative example all adopt following preparation technology:

[0054] Step (1): Pre-dry PA6 and microcapsule red phosphorus masterbatch. PA6 is dried at a drying temperature of 110-120°C for 4-8 hours; the microcapsule red phosphorus masterbatch is dried at a drying temperature of 90°C. The time is 2 to 4 hours.

[0055] Step (2): Mix other components except the alkali-free glass fiber with the PA6 pre-dried in the step (1) and the microcapsule red phosphorus masterbatch in parts by weight to obtain a mixture.

[0056] Step (3): Put the above-mentioned mixture and alkali-free glass fiber into the main feeding hopper and side feeding hopper of the twin-screw extruder respectively, melt and extrude at a processing temperature of 200-250°C, and cool and form , pelletizing, and preparing the low-odor red phosphorus flame-retardant reinforced polyamide material.

[0057] The metal cationic salt surfactant modified diatomite used in the preparation pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-odor red phosphorus flame-retardant reinforced polyamide material. The low-odor red phosphorus flame-retardant reinforced polyamide material comprises polyamide resin, areinforced component and a red phosphorus flame retardant, and further comprises an odor absorption inhibitor. The odor absorption inhibitor is selected from modified diatomite or a compound of the modified diatomite and at least one of metallic oxide and an acid absorbent. The low-odor red phosphorus flame-retardant reinforced polyamide material is provided, generation of phosphine is inhibited in all directions and at multiple angles by addition of the odor absorption inhibitor, generated gas such as the phosphine is adsorbed fully, the odor grade of the red phosphorus flame-retardant reinforced polyamide material can be increased remarkably, and meanwhile, quite high mechanical property and flame retardant property are maintained.

Description

technical field [0001] The invention relates to the field of red phosphorus flame-retardant polyamide materials, in particular to a low-odor red phosphorus flame-retardant reinforced polyamide material. Background technique [0002] The red phosphorus flame retardant reinforced polyamide material has the following significant advantages: less addition, high flame retardant efficiency, and the flame retardant system can maintain excellent mechanical properties; in addition, the red phosphorus flame retardant polyamide system has a higher CTI value, which is It is widely used in electrical switches, low-voltage circuit breakers, connection contactors, sockets and other fields. [0003] However, due to the strong hygroscopicity of red phosphorus, under the action of water and oxygen, it is easily oxidized into a variety of oxyacids of viscous phosphorus (reacting with some inorganic minerals in the material to produce phosphate). These acids and salts are not only Migration fr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/02C08L51/06C08L51/04C08K13/06C08K9/10C08K3/02C08K3/38C08K5/134C08K5/526C08K3/34C08K7/14C08K5/098C08K3/22C08K9/02C08K9/04
CPCC08K2003/026C08K2003/222C08K2003/2227C08K2003/2244C08K2003/2248C08K2003/2296C08K2003/387C08L77/02C08L2201/02C08L2203/20C08L51/06C08L51/04C08L51/003C08K13/06C08K9/10C08K3/02C08K3/38C08K5/1345C08K5/526C08K3/34C08K7/14C08K5/098C08K3/22C08K9/02C08K9/04C08K3/346
Inventor 黄涛林立陈晓敏田际波杜晓华刘浪郑友明
Owner CGN JUNER NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap