Flexible mannequin and making method thereof

A flexible, mannequin technology, applied in the field of mannequins, can solve the unfavorable clothing production, the development of the sales market, the garment display effect, the unfavorable design and technical personnel's mannequin clothing making, sewing and processing, and the lack of softness of human skin on mannequins And elasticity and other issues, to achieve the effect of improving the realism of fitting, good waterproof effect and good elasticity

Active Publication Date: 2018-03-16
HONGJI UNDERWEAR CO LTD
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the hard material of the current hard mannequin reduces the hand feeling of the mannequin, and makes the display effect of the mannequin more rigid after dressing; at the same time, the mannequin after dressing lacks the softness and elasticity of human skin, which reduces the test effect. The realism of wearing clothes reduces the similarity between avatars and human skin, which is not conducive to designers and technicians using avatars for clothing making, sewing and processing, and often leads people to think that the feeling of dressing after buying clothes is the same as that of avatars. The effect of dressing display is quite different, which is not conducive to the production of clothing, the development of the sales market and the display effect of ready-made clothing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flexible mannequin and making method thereof
  • Flexible mannequin and making method thereof
  • Flexible mannequin and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] See Figure 1-2 , a flexible mannequin, the flexible mannequin 1 includes a mannequin body 11 and a flexible outer layer 12, the flexible outer layer 12 includes a silicone cotton layer 121, a memory foam layer 122 and a waterproof cotton layer connected sequentially from the inside to the outside 124 , the inner surface of the silicone cotton layer 121 is connected to the outer surface of the mannequin body 11 , and a viscose layer 123 is arranged between the memory foam layer 122 and the waterproof cotton layer 124 .

[0044] The thickness of the silica gel cotton layer 121 is 0.5 cm, and the thickness of the memory foam layer 122 is 4 cm.

[0045] The waterproof cotton layer 124 is a PVC waterproof cotton layer.

[0046] The memory foam layer is made of polyurethane and nano-silicon particles in a weight ratio of 3:1, and the polyurethane is made of the following raw materials in parts by weight:

[0047]

[0048] Described memory foam layer is made by following...

Embodiment 2

[0068] The difference between this embodiment and the above-mentioned embodiment 1 is:

[0069] The thickness of the silica gel cotton layer 121 is 0.85 cm, and the thickness of the memory foam layer 122 is 3.5 cm.

[0070] The memory foam layer is made of polyurethane and nano-silicon particles in a weight ratio of 3.8:1, and the polyurethane is made of the following raw materials in parts by weight:

[0071]

[0072]

[0073] Described memory foam layer is made by following preparation method:

[0074] Step 1: Dissolving dibutyltin dilaurate in water, then adding polyoxypropylene diol and toluene diisocyanate, and stirring at 48°C for 45 minutes to obtain a polyurethane prepolymer;

[0075] Step 2: Heat the polyurethane prepolymer prepared in step 1 to 80°C, then add zinc diethyldithiophosphate, polydimethylsiloxane and azodicarbonamide in sequence, at a speed of 300-1000rpm Stir for 25 minutes, add nano-silicon particles while stirring, and form and cool to obtain a...

Embodiment 3

[0091] The difference between this embodiment and the above-mentioned embodiment 1 is:

[0092] The thickness of the silica gel cotton layer 121 is 1.25 cm, and the thickness of the memory foam layer 122 is 3 cm.

[0093] The memory foam layer is made of polyurethane and nano-silicon particles in a weight ratio of 4.5:1, and the polyurethane is made of the following raw materials in parts by weight:

[0094]

[0095] Described memory foam layer is made by following preparation method:

[0096] Step 1: Dissolving dibutyltin dilaurate in water, then adding polyoxypropylene diol and toluene diisocyanate, and stirring at 52°C for 40 minutes to obtain a polyurethane prepolymer;

[0097] Step 2: Heat the polyurethane prepolymer prepared in step 1 to 90°C, then add zinc diethyldithiophosphate, polydimethylsiloxane and azodicarbonamide in sequence, and stir at 825rpm After 30 minutes, add nano-silicon particles while stirring, and form and cool to obtain a memory foam layer.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of mannequins, and in particular to a flexible mannequin and a making method thereof. The flexible mannequin comprises a mannequin main body and a flexibleouter layer, wherein the flexible outer layer comprises a silicone cotton layer, a memory cotton layer and a waterproof cotton layer which are sequentially connected from inside to outside; the innersurface of the silicone cotton layer is connected to the outer surface of the mannequin main body; and an adhesive layer is arranged between the memory cotton layer and the waterproof cotton layer. The flexible mannequin provided by the invention, by arranging the flexible outer layer on the surface of the mannequin main body, is relatively good in softness, elasticity, air permeability, hand-feeling and truth, so that the hand feeling of the flexible mannequin is closer to human skin in elasticity and softness; a finished product, which is obtained on the basis of the flexible mannequin andis obtained from clothes making, tailoring and clothes processing, can fit more to human curve, and the finished product is more comfortable to wear; and the making method provided by the invention issimple to operate, convenient to operate and control, stable in quality, high in production efficiency and low in production cost.

Description

technical field [0001] The invention relates to the technical field of mannequins, in particular to a flexible mannequin and a preparation method thereof. Background technique [0002] Mannequins refer to mannequins made according to the proportions of the human body. When making clothing, technicians use mannequins to measure and make clothes, and it is convenient for technicians to use mannequins to sew and process clothes. It is often used to display new clothes and test For the effect of wearing new clothes, the existing mannequins are mainly hard mannequins made of glass fiber as the main material, and the texture is relatively hard. [0003] However, the hard material of the current hard mannequin reduces the hand feeling of the mannequin, and makes the display effect of the mannequin more rigid after dressing; at the same time, the mannequin after dressing lacks the softness and elasticity of human skin, which reduces the test effect. The realism of wearing clothes r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A41H5/00C08L75/08C08K3/36C08G18/76C08G18/61C08G18/48C08J9/10C09J129/14C09J11/04C09J11/06C09J11/08C08G101/00
CPCA41H5/00C08G18/4825C08G18/61C08G18/7614C08G2101/00C08G2280/00C08J9/103C08J2203/04C08J2375/08C08K3/36C08K2003/2227C08K2003/2241C08L2201/12C08L2205/035C09J11/04C09J11/06C09J11/08C09J129/14C08L75/08C08L71/02C08L33/26C08L33/08C08K3/22C08K5/12
Inventor 简柳文黄福开李小红陈国强金华邱锦钊谢伟广翁创杰
Owner HONGJI UNDERWEAR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com