No-cracking Ru porcelain tableware and no-cracking manufacture method of Ru porcelain tableware

A production method and tableware technology, which can be applied to household utensils, clay products, other household utensils, etc., and can solve problems such as inability to achieve results.

Inactive Publication Date: 2018-03-16
汝州市宣和坊汝瓷有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, jade-green and white-bodied porcelain, the Ru porcelain made of Ru porcelain is open on the outside and not on the inside, but in the use of high-end tableware, it cannot achieve good results, and can only achieve the inside without opening. The formula and process of non-opening Ru porcelain developed by tableware, and the whole body without opening

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The raw material of the embryo body is composed of 25 parts of Tanggou soil, 25 parts of Banpo soil and 50 parts of black stone according to the weight ratio. The glaze raw materials are composed of 40 parts of mica, 28 parts of horseshoe stone, 5 parts of agate stone, 25 parts of plant ash and 2 parts of sheep bone powder according to the weight ratio.

[0038] A method for making Ru porcelain tableware without opening pieces, which is used to make the above-mentioned Ru porcelain tableware without opening pieces, specifically comprising the following steps:

[0039] S1: Grinding the raw material of the embryo body, and adding water for wet grinding, adjusting the water content of the raw material slurry of the embryo body to 30%;

[0040] S2: Grinding the glaze raw material, adding water to wet grinding, draining water after sedimentation, and adjusting the water content of the glaze raw material slurry to 60%;

[0041] S3: inject the embryo body raw material slurry ...

Embodiment 2

[0048] The raw material of the embryo body is composed of 5 parts of Tanggou soil, 3 parts of Banpo soil and 30 parts of black wool soil according to the weight ratio. The glaze raw materials are composed of 20 parts of mica, 10 parts of horseshoe stone, 3 parts of agate stone, 30 parts of plant ash and 5 parts of sheep bone powder according to the weight ratio.

[0049] A specific embodiment of the present invention also provides a method for making Ru porcelain tableware without opening pieces, which is used to make the above-mentioned Ru porcelain tableware without opening pieces, specifically comprising the following steps:

[0050] S1: Grinding the raw material of the embryo body, and adding water for wet grinding, adjusting the water content of the raw material slurry of the embryo body to 27%;

[0051] S2: Grinding the glaze raw material, adding water to wet grinding, draining water after sedimentation, and adjusting the water content of the glaze raw material slurry to...

Embodiment 3

[0059] The raw material of the embryo body is composed of 30 parts of Tanggou soil, 35 parts of Banpo soil and 30 parts of black wool soil according to the weight ratio. The glaze raw materials are composed of 50 parts of mica, 35 parts of horseshoe stone, 3 parts of agate stone, 30 parts of plant ash and 5 parts of sheep bone powder according to the weight ratio.

[0060] A specific embodiment of the present invention also provides a method for making Ru porcelain tableware without opening pieces, which is used to make the above-mentioned Ru porcelain tableware without opening pieces, specifically comprising the following steps:

[0061] S1: Grinding the raw material of the embryo body, and adding water for wet grinding, adjusting the water content of the raw material slurry of the embryo body to 32%;

[0062] S2: Grinding the glaze raw material, adding water to wet grinding, draining after sedimentation, and adjusting the water content of the glaze raw material slurry to 62%...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses no-cracking Ru porcelain tableware and a no-cracking manufacture method of the Ru porcelain tableware. The porcelain comprises: a blank body and glaze materials which are usedfor manufacturing tableware; the blank body raw materials comprise Tanggou soil, Banpo soil and Heimao soil; the glaze raw materials comprise mica, horseshoe stones, agate stones, plant ash and sheepbone meal; the blank body raw materials and the glaze raw materials are crushed, water is added, wet grinding is carried out, and water is discharged after precipitation; slurry of the blank body rawmaterial is injected into a mold, and firing is carried out for forming a biscuit; glazing is carried out on the outer surface of the blank body raw material biscuit; and the blank body is placed intoa kiln, the furnace temperature of the kiln is raised to 1050 DEG C, heating is carried out at a speed of 1 DEG C every two minutes, when temperature is increased to 1280-1300 DEG C, heat preservation and firing are carried out on the blank body under a condition of 1280-1300 DEG C, and then firing is finished. Through the mode, according to the porcelain provided by the invention, the formula ofthe porcelain and the manufacturing method are improved, the expansion coefficients of the glaze materials and the biscuit are consistent, so that the phenomenon that existing Ru porcelain is crackedand the glaze surface of the surface is cracked is changed, no cracks and no fracture exist on the porcelain, and the manufactured porcelain can be made into high-grade tableware.

Description

technical field [0001] The invention relates to porcelain and a method for making porcelain, in particular to non-split Ru porcelain tableware and a method for making Ru porcelain tableware without splits. Background technique [0002] Ru porcelain ranks first among the five famous porcelains of "Ru, Guan, Jun, Ge and Ding" in the Song Dynasty in my country, and it is named after it was produced in ancient Ruzhou. Ru porcelain began in the Tang Dynasty and flourished in the Northern Song Dynasty. Because of its typical characteristics of "blue as the sky, face like jade, cicada wing pattern, sparse stars, and sesame nail glaze", it was designated as a tribute by the Song royal family and is strictly prohibited from being used by the people. [0003] Ru kiln porcelain is exquisite in quality, hard in fetal bone, fine in workmanship, full of glaze and branch-fired, with agate in the glaze, and moist glaze color. "The praise. Cao Zhao, a literati in the Ming Dynasty, pointed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C03C8/00C04B41/86C04B33/34
CPCC03C8/00C04B33/13C04B33/34C04B41/5022C04B41/86C04B41/0072
Inventor 杨云超仝利军
Owner 汝州市宣和坊汝瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products