Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Cup Multilayer Container

A technology for containers and interlayers, which is applied in containers, household containers, and anti-rot containers. It can solve the problems of polyester resin transparency damage, etc., and achieve the prevention of interlayer peeling, excellent interlayer adhesion, and excellent mechanical properties. The effect of intensity

Active Publication Date: 2020-08-14
TOYO SEIKAN GRP HLDG LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, when a polyester resin and a polyamide resin, especially an aromatic polyamide resin such as polym-xylylene adipamide (MDX6) having particularly excellent gas barrier properties among polyamide resins are used together, When the resin composition of the mixture is used as the intermediate layer, there is a problem that the excellent transparency of the polyester resin is impaired

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cup Multilayer Container
  • Cup Multilayer Container
  • Cup Multilayer Container

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0126] A multi-layer sheet was made by using PET to form the inner and outer layers, dry blending APET1 and PA together at a ratio of 70:30 to form the middle layer, and setting the temperature of the molding machine at 280°C.

[0127] The sheet was made to have a thickness of 1.2 mm, and the intermediate layer was 10% by weight of the entire sheet. Next, the sheet was heated again at 100° C. to form a cup, and thus a multilayer container having a drawing ratio of 1.67 and an inner volume of 350 cc was produced. The resulting container was measured for side haze, occurrence of delamination, and oxygen barrier property according to the methods described above.

[0128] Furthermore, the dried APET1 was fed into a hopper of an injection molding machine, and injection molded while setting the temperature of the cylinder at 280° C. to obtain an injection molded plate having a size of 90×90×1.5 mm. The injection-molded plate was uniaxially stretched 3 times by the above method to o...

Embodiment 2

[0130] By using APET1 as a base material, the granular masterbatch resin (MB1) which contained an oxidation catalyst in the resin composition in the amount of 500 ppm of metal conversion was prepared by the said method. Here, the temperature of the barrel was maintained at 280°C.

[0131] By using a multilayer sheet-forming machine, a multilayer container and a stretch sheet were fabricated in the same manner as in Example 1, except that an intermediate layer was formed by using a dry blend of MB1 and PA in a ratio of 70:30. Then measure their properties.

Embodiment 3

[0133] A multilayer container was produced in the same manner as in Example 1 except that APET2 was used instead of APET1, and its properties were measured.

[0134] In addition, a stretched sheet was produced in the same manner as in Example 1, except that dry APET2 was supplied to the hopper of an injection molding machine to form an injection-molded sheet thereof. The refractive index of the produced stretched sheet was measured.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hazingaaaaaaaaaa
hazingaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a multilayer container obtained by thermoforming a multilayer precursor comprising: an inner layer and an outer layer obtained from an ethylene terephthalate-based polyester resin; At least one intermediate layer obtained from a crystalline ethylene terephthalate-based polyester resin and a gas-barrier aromatic polyamide resin. The difference in refractive index (ΔRI) represented by the formula (1) between the low-crystalline ethylene terephthalate-based polyester resin and the gas-barrier aromatic polyamide resin is 0.03 or less, ΔRI=∣RI E –RI A ∣(1), where RI E and RI A Represents the refractive index after uniaxial stretching of an injection molded plate obtained from a low-crystalline ethylene terephthalate-based polyester resin and a gas-barrier aromatic polyamide resin, respectively, after 3 times, and the haze on the side of the container is 5% or less. As a result, the container has a multilayer structure obtained from inner and outer layers made of polyester resin and an intermediate layer made of a blend of polyester resin and aromatic polyamide resin, and satisfies excellent transparency , gas barrier and interlayer adhesion requirements.

Description

technical field [0001] The present invention relates to a multilayer container including a polyester resin, and more particularly, to a cup-type multilayer container excellent in gas barrier properties, interlayer adhesion, and transparency. Background technique [0002] Polyester resins represented by polyethylene terephthalate have excellent properties such as moldability, transparency, mechanical strength, and chemical resistance, and thus are widely used in the field of packaging containers. In order to improve the gas barrier properties of containers including polyester resins to gases such as oxygen, it is proposed to form a saponified product of ethylene-vinyl acetate copolymer or a layer of polyamide as an intermediate layer between an inner layer and an outer layer of a polyester resin. Packaging materials with multi-layer structure. In order to further improve the gas barrier properties of the packaging material of the above multilayer structure, it has also been ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B65D1/28B32B27/36B65D65/40B65D81/24
CPCB32B27/36B65D1/28B65D81/24B32B27/08B32B27/34B32B2250/24B32B2250/40B32B2270/00B32B2307/414B32B2307/516B65D65/40B32B2307/51B32B2307/704B32B2439/02B32B1/00B32B2307/7242B32B2307/412B32B2439/00B32B7/023
Inventor 平山由纪子山田俊树石原隆幸田代裕树
Owner TOYO SEIKAN GRP HLDG LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com