Antibacterial artificial quartz stone plate

An artificial quartz stone and antibacterial technology, which is applied in the field of antibacterial artificial quartz stone slabs, can solve the problems of artificial quartz stone surface bacterial pollution, killing, and bacteria are not inhibited, so as to improve curing efficiency, enhance antibacterial activity, and improve dispersion sexual effect

Inactive Publication Date: 2018-03-30
佛山市欧泊石业有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the artificial quartz stone in the prior art also has its inherent disadvantages. For example, the surface of the artificial quartz stone will inevitably be polluted by bacteria when it is used, but ordinary artificial quartz stone has no effect on inhibiting or killing bacteria.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] An antibacterial artificial quartz stone plate, which is made of the following raw materials in parts by weight: 45 parts of 5-20 mesh quartz sand, 25 parts of 200-300 mesh quartz powder, 10 parts of resin, 2 parts of antibacterial agent, and 0.4 parts of colorant 1 part, 1 part of curing agent, 1 part of accelerator, 0.6 part of coupling agent.

[0022] Wherein, the resin is composed of the following components by weight percentage: 80% epoxy resin, 20% chlorinated unsaturated polyester resin; the coupling agent γ-(2,3-glycidyloxy)propyltrimethoxy base silane.

[0023] Wherein, the preparation method of described antibacterial agent is:

[0024] (1) Pulverize the tourmaline with a pulverizer and pass through a 65-75 mesh sieve to obtain tourmaline powder; add an appropriate amount of deionized water to the tourmaline powder and stir evenly to make the material a paste; (2) Put the above paste material into In the container, use 2.7 kg of steam pressure to keep warm f...

Embodiment 2

[0028] An antibacterial artificial quartz stone plate, which is made of the following raw materials in parts by weight: 40 parts of 5-20 mesh quartz sand, 30 parts of 200-300 mesh quartz powder, 8 parts of resin, 2 parts of antibacterial agent, and 0.3 parts of coloring material 1 part, 1 part of curing agent, 0.8 part of accelerator, 0.5 part of coupling agent.

[0029]Wherein, the resin is composed of the following components by weight percentage: 80% epoxy resin, 20% chlorinated unsaturated polyester resin; the coupling agent γ-(2,3-glycidyloxy)propyltrimethoxy base silane.

[0030] Wherein, the preparation method of described antibacterial agent is:

[0031] (1) Pulverize the tourmaline with a pulverizer and pass through a 65-75 mesh sieve to obtain tourmaline powder; add an appropriate amount of deionized water to the tourmaline powder and stir evenly to make the material a paste; (2) Put the above paste material into In the container, use 2.6 kg of steam pressure to ke...

Embodiment 3

[0035] An antibacterial artificial quartz stone plate is made of the following raw materials in parts by weight: 50 parts of 5-20 mesh quartz sand, 20 parts of 200-300 mesh quartz powder, 12 parts of resin, 3 parts of antibacterial agent, and 0.5 parts of colorant 2 parts, 2 parts of curing agent, 1.5 parts of accelerator, 0.8 parts of coupling agent.

[0036] Wherein, the resin is composed of the following components by weight percentage: 80% epoxy resin, 20% chlorinated unsaturated polyester resin; the coupling agent γ-(2,3-glycidyloxy)propyltrimethoxy base silane.

[0037] Wherein, the preparation method of described antibacterial agent is:

[0038] (1) Pulverize the tourmaline with a pulverizer and pass through a 65-75 mesh sieve to obtain tourmaline powder; add an appropriate amount of deionized water to the tourmaline powder and stir evenly to make the material a paste; (2) Put the above paste material into In the container, use 2.8 kg of steam pressure to insulate for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibacterial artificial quartz stone plate made from the following raw materials in parts by weight: 40 to 50 parts of quartz sand of 5 to 20 mesh, 20 to 30 parts of quartzpowder of 200 to 300 mesh, 8 to 12 parts of resin, 2-3 parts of antibacterial agent, 0.3-0.5 part of pigment, 1-2 parts of curing agent, 0.8-1.5 parts of accelerator, and 0.5-0.8 part of coupling agent. According to the antibacterial artificial quartz stone plate, optimization and improvement of a raw material formula and mutual cooperation of different raw materials effectively improve the mechanical properties such as hardness and toughness of the artificial quartz stone plate, improve the curing efficiency, enable the antibacterial artificial quartz stone plate to have strong antibacterialpower and durable antibacterial effect, and improve the overall performance of the antibacterial artificial quartz stone plate.

Description

technical field [0001] The invention relates to the technical field of architectural decoration, in particular to an antibacterial artificial quartz stone plate. Background technique [0002] Artificial quartz stone (or diamond / corundum) originated in Spain. It was called Celite when it entered China in 2005. When artificial quartz stone was recognized by more and more consumers, in 2006, some people in China began to develop artificial quartz. Stone, in 2007, many manufacturers have launched domestic artificial quartz stone. As a new type of artificial building material, artificial quartz stone has incomparable advantages of natural stone in terms of moisture resistance, acid resistance, and splicability. Today, as natural stone resources are becoming increasingly depleted, artificial quartz stone is the best substitute. At the same time, artificial quartz stone can use waste glass as raw material, thus realizing resource reuse while protecting the environment. These adva...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/18C04B20/02C04B24/00C04B103/67C04B111/54C04B111/20
CPCC04B20/023C04B26/18C04B40/0039C04B2103/67C04B2111/2092C04B2111/542C04B24/281C04B14/06C04B24/42C04B14/041C04B24/00C04B24/30C04B24/121C04B24/122C04B2103/0068C04B2103/54
Inventor 陆顺欢
Owner 佛山市欧泊石业有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com