Thrust bearing nitriding system and process for iron-based powder metallurgy

An iron-based powder metallurgy and thrust bearing technology is applied in the field of iron-based powder nitriding process, which can solve the problems of lack of iron-based powder metallurgy thrust bearing nitriding treatment process, low powder metallurgy products, etc., so as to improve the effective utilization efficiency, save energy, and improve the effect of hardness

Inactive Publication Date: 2018-04-17
无锡佳力欣精密机械有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the increasing use of turbochargers, the types and requirements of thrust bearings for turbochargers are increasing, and the requirements for wear resistance and strength of thrust bearings are also increasing, but the hardness of powder metallurgy products itself Relatively low, how to improve the hardness of iron-based powder metallurgy thrust bearings to improve wear resistance and strength performance, nitriding process is an effective method, but there is currently no special method for iron-based powder metallurgy thrust bearings Nitriding treatment process, and to ensure safe discharge, environmental protection and energy saving as much as possible is also an extremely important issue in the current nitriding process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thrust bearing nitriding system and process for iron-based powder metallurgy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] As shown in the attached figure, an iron-based powder metallurgy thrust bearing nitriding system includes liquid ammonia tank 1, pressure reducing valve 2, glass rotameter 3, heat treatment resistance furnace 4, valve one 5, valve two 6, ammonia Decomposition furnace 7, ignition port one 8 and ignition port two 9, the liquid ammonia tank 1 communicates with the heat treatment resistance furnace 4 through the pressure reducing valve 2, and the glass rotameter 3 is connected in series between the pressure reducing valve 2 and the heat treatment resistance furnace Between 4, the heat treatment resistance furnace 4 is provided with a valve one 5 and a valve two 6, and the valve one 5 is provided with an ignition port one 8, and the valve two 6 communicates with the ammonia decomposition furnace 7, and the ammonia decomposition furnace The 7 is provided with an ignition port 2 9.

[0020] A kind of ferrous powder metallurgy thrust bearing nitriding process, comprises the ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a nitriding process for iron-based powder metallurgy, in particular to a thrust bearing nitriding system and process for iron-based powder metallurgy. By the thrust bearing nitriding system and process for iron-based powder metallurgy, safe discharge is implemented, energy consumption is low, and the nitriding efficiency is high. The thrust bearing nitriding system comprises a liquid ammonia tank (1), a pressure reducing valve (2), a glass rotor flowmeter (3), a heat treatment resistance furnace (4), a first valve (5), a second valve (6), an ammonia decomposition furnace (7), a first ignition opening (8) and a second ignition opening (9), wherein the liquid ammonia tank (1) communicates with the heat treatment resistance furnace (4) through the pressure reducing valve (2); the glass rotor flowmeter (3) is serially connected between the pressure reducing valve (2) and the heat treatment resistance furnace (4); the first valve (5) and the second valve (6) are arranged on the heat treatment resistance furnace (4); the first ignition opening (8) is formed in the first valve (5); the second valve (6) communicates with the ammonia decomposition furnace (7); and the second ignition opening (9) is formed in the ammonia decomposition furnace (7).

Description

technical field [0001] The invention relates to an iron-based powder nitriding process, in particular to an iron-based powder metallurgy thrust bearing nitriding system and its process. Background technique [0002] Nitriding is a chemical heat treatment process that infiltrates nitrogen atoms into the surface of the workpiece in a certain medium at a certain temperature. The nitriding of the prior art is to put the workpiece into a sealed container, pass through ammonia gas and heat it. After a long time of heat preservation, the ammonia gas thermally decomposes to generate active nitrogen atoms, which are continuously adsorbed to the surface of the workpiece and diffuse into the surface of the workpiece. Thereby changing the chemical composition and organization of the surface to obtain a suitable surface hardness. [0003] With the increasing use of turbochargers, the types and requirements of thrust bearings for turbochargers are increasing, and the requirements for wea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C8/26B22F3/24
CPCC23C8/26B22F3/24B22F2003/241
Inventor 王承秋张辉沈锡荣
Owner 无锡佳力欣精密机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products