Surface treatment method of stamping die
A stamping die and surface treatment technology, applied in the field of die treatment, can solve the problems of high stamping working temperature, stamping die wear, oil contamination, etc., and achieve the effects of improving surface hardness, improving service life, and improving activity.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] A surface treatment method for a stamping die, comprising the following steps:
[0019] (1) Put the steel ball into a resistance furnace and heat it to 820°C, keep it warm for 30 minutes, then adjust the temperature to 400°C, keep it warm for 15 minutes, then cool down to room temperature with the furnace, then put the steel ball into the activation solution to soak for 2 hours, then take it out , using deionized water to wash to neutrality, and drying to constant weight to obtain an activated steel bullet; the activation solution is made of the following components in parts by weight: phosphoric acid 5, phosphate 8, sodium molybdate 3, nitric acid 2, Nano silicon dioxide 1, deionized water 80;
[0020] (2) Soak the stamping die in cleaning solution for 10 minutes, and then use plasma discharge to treat the surface of the stamping die for 5 minutes;
[0021] (3) The activated steel bullet obtained in step (1) is uniformly shot peened on the surface of the stamping die ...
Embodiment 2
[0030] A surface treatment method for a stamping die, comprising the following steps:
[0031] (1) Put the steel ball into a resistance furnace and heat it to 850°C, keep it warm for 30 minutes, then adjust the temperature to 400°C, keep it warm for 15 minutes, then cool down to room temperature with the furnace, then put the steel ball into the activation solution for 2 hours, then take it out , using deionized water to wash to neutrality, and drying to constant weight to obtain an activated steel bullet; the activation solution is made of the following components in parts by weight: phosphoric acid 5, phosphate 8, sodium molybdate 3, nitric acid 2, Nano silicon dioxide 1, deionized water 80;
[0032] (2) Soak the stamping die in cleaning solution for 10 minutes, and then use plasma discharge to treat the surface of the stamping die for 10 minutes;
[0033] (3) The activated steel bullet obtained in step (1) is uniformly shot peened on the surface of the stamping die for 30-...
Embodiment 3
[0042] A surface treatment method for a stamping die, comprising the following steps:
[0043] (1) Put the steel ball into a resistance furnace and heat it to 830°C, keep it warm for 30 minutes, then adjust the temperature to 400°C, keep it warm for 15 minutes, then cool down to room temperature with the furnace, then put the steel ball into the activation solution to soak for 2 hours, then take it out , using deionized water to wash to neutrality, and drying to constant weight to obtain an activated steel bullet; the activation solution is made of the following components in parts by weight: phosphoric acid 5, phosphate 8, sodium molybdate 3, nitric acid 2, Nano silicon dioxide 1, deionized water 80;
[0044] (2) Soak the stamping die in cleaning solution for 10 minutes, and then use plasma discharge to treat the surface of the stamping die for 8 minutes;
[0045] (3) The activated steel bullet obtained in step (1) is uniformly shot peened on the surface of the stamping die ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com