A thermally induced self-healing UV-curable adhesive based on stepwise polymerization mechanism

A technology of gradual polymerization and ultraviolet light, applied in the direction of non-polymer organic compound adhesives, adhesives, etc., can solve problems such as bonding failure and microscopic cracks, achieve reliable bonding performance, avoid internal stress concentration, and have a wide range of applications Effect

Active Publication Date: 2021-03-30
YANTAI DARBOND TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that light-cured pressure-sensitive adhesives are prone to produce microscopic cracks and cause bonding failure in harsh environments, especially under the action of external stress, the present invention provides a thermally induced self-healing UV adhesive based on a gradual polymerization mechanism. Light-curing adhesives to achieve the purpose of solving the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A thermally induced self-healing UV-curable adhesive based on stepwise polymerization mechanism
  • A thermally induced self-healing UV-curable adhesive based on stepwise polymerization mechanism
  • A thermally induced self-healing UV-curable adhesive based on stepwise polymerization mechanism

Examples

Experimental program
Comparison scheme
Effect test

Embodiment and comparative example

[0026] ①Synthesis of (meth)acrylate random prepolymer

[0027] Add (meth)acrylate viscous monomer, internal polymer monomer, functional monomer, rosin acrylate, blocked isocyanate acrylate and photoinitiator into the three-necked flask in proportion, start stirring at the same time, and purge with high-purity nitrogen solution for 30 minutes until the photoinitiator is completely dissolved, with a light intensity of 0.5 mW / cm 2 The solution is irradiated with ultraviolet light for 30-60s to obtain (meth)acrylate random prepolymer.

[0028] ②Add the multifunctional (meth)acrylate crosslinking agent and photoinitiator in proportion to the above-mentioned (meth)acrylate random prepolymer in sequence, stir and mix evenly to obtain the finished product.

[0029] Table 1: Raw material proportioning of embodiment and comparative example

[0030]

[0031]Description: The raw materials used in the test are EA-ethyl acrylate, BA-n-butyl acrylate, 2-EHA-isooctyl acrylate, MMA-methyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a heat-induced self-healing UV-curable pressure-sensitive adhesive based on a step-by-step polymerization mechanism. ) 0.5-5 parts of acrylate crosslinking agent, 0.1-5 parts of photoinitiator; wherein, the mass fraction of (meth)acrylate random prepolymer is: 40-100 parts of viscous monomer, 40-100 parts of internal polymer monomer 10-50 parts, functional monomer 10-40 parts, rosin acrylate 5-40 parts, blocked isocyanate acrylate 10-40 parts, photoinitiator 0.1-0.5 parts. The UV-curable pressure-sensitive adhesive prepared by the present invention has a simple synthesis process, low energy consumption, 100% active ingredients, and is environmentally friendly. More importantly, the UV-curable pressure-sensitive adhesive prepared by the present invention has thermal Self-healing properties.

Description

technical field [0001] The invention relates to a self-healing light-curing adhesive and a preparation method thereof, belonging to the technical field of light-curing materials. Background technique [0002] Polymer materials are susceptible to aging due to external light, heat, water, stress, chemical substances or the combined effects of these external factors during use, resulting in micro-cracks on the surface or inside. The existence of these micro-cracks makes the performance of the material And the service life is greatly reduced, and even catastrophic accidents may occur due to the expansion of microcracks. Self-healing polymer materials can realize the self-healing of the microcracks of the material itself by simulating the mechanism of biological damage healing, avoiding further damage and prolonging the service life of the material. Self-healing technology has shown good application prospects and application value in the field of microelectronics, biomedical mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J4/06C09J4/02C08F289/00C08F220/14C08F220/18C08F220/20C08F220/36C08F2/48
CPCC09J4/06C08F2/48C08F289/00C09J2301/302C08F220/1808C08F220/18C08F220/1802C08F220/36
Inventor 王博潘光君王建斌陈田安解海华
Owner YANTAI DARBOND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com