Wear-resistant inflatable swimming pool

A technology for swimming pools and fumed white carbon black, applied in the field of polymer materials, can solve the problems affecting the appearance and service life of inflatable swimming pools, swimming pool bumps and frictions, health hazards of consumers, etc., to increase thickness, avoid falls and wear strong effect

Inactive Publication Date: 2018-05-11
刘辉
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Inflatable swimming pool is a portable swimming pool for children and families to bathe and entertain in summer. At present, the traditional inflatable swimming pool is made of PVC and mesh, which is relatively light. However, inflatable swimming pools are generally used outdoors, and the bumps and frictions on the swimming pool are serious. Therefore, air leakage often occurs and needs to be repaired, which affects the appearance and service life of the inflatable swimming pool. Moreover, when the swimming pool is used by a large number of people, coupled with external environmental pollution, it is easy to cause germs to multiply and cause skin allergies to users. Consumers' health poses a great risk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant inflatable swimming pool

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A wear-resistant inflatable swimming pool, made of the following raw materials in parts by weight: PVC resin 120, chlorinated paraffin 2, fumed white carbon black 1, nano-titanium dioxide 1, zinc oxide 1, antibacterial sepiolite 1, stabilizer 0.7, poly Methyl methacrylate 0.7, aminophylline 0.3.

[0019] The fumed white carbon black is hydrophobic fumed white carbon black.

[0020] For the antibacterial sepiolite, after mixing nano-silver and sepiolite powder, add water in an amount 90 times the weight of sepiolite powder, heat and boil until there is no obvious moisture, then place it at 800°C for 15 minutes and then cool it down to 400°C. After keeping warm for 30 minutes, take it out and crush it to 60~70nm to get antibacterial sepiolite.

[0021] Described nanometer silver, weight is 10% of sepiolite weight.

[0022] Described stabilizer is graphene.

[0023] A method for preparing a wear-resistant inflatable swimming pool, comprising the following steps:

[002...

Embodiment 2

[0029] A wear-resistant inflatable swimming pool is made of the following raw materials in parts by weight: PVC resin 125, chlorinated paraffin 2.5, fumed white carbon black 1.5, nano titanium dioxide 1.5, zinc oxide 1.5, antibacterial sepiolite 1.5, stabilizer 0.8, poly Methyl methacrylate 0.8, aminophylline 0.4.

[0030] The fumed white carbon black is hydrophobic fumed white carbon black.

[0031] For the antibacterial sepiolite, after mixing nano-silver and sepiolite powder, add water 95 times the weight of sepiolite powder, heat and boil until there is no obvious moisture, then place it at 850°C for 18 minutes, and cool it down to 450°C. After keeping warm for 35 minutes, take it out and crush it to 60~70nm to get antibacterial sepiolite.

[0032] Described nanometer silver, weight is 11% of sepiolite weight.

[0033] Described stabilizer is graphene.

[0034] A method for preparing a wear-resistant inflatable swimming pool, comprising the following steps:

[0035] (1...

Embodiment 3

[0040] A wear-resistant inflatable swimming pool, made of the following raw materials in parts by weight: PVC resin 130, chlorinated paraffin 3, fumed white carbon black 2, nano titanium dioxide 2, zinc oxide 2, antibacterial sepiolite 2, stabilizer 0.9, poly Methyl methacrylate 0.9, aminophylline 0.5.

[0041] The fumed white carbon black is hydrophobic fumed white carbon black.

[0042] For the antibacterial sepiolite, after mixing nano-silver and sepiolite powder, add water 100 times the weight of sepiolite powder, heat and boil until there is no obvious moisture, then place it at 900 ° C for 20 minutes, and cool it down to 500 ° C. After keeping warm for 40 minutes, take it out and crush it to 60~70nm to get antibacterial sepiolite.

[0043] Described nano silver, weight is 12% of sepiolite weight.

[0044] Described stabilizer is graphene.

[0045] A method for preparing a wear-resistant inflatable swimming pool, comprising the following steps:

[0046] (1) Mix PVC re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention mainly relates to the technical field of high polymer materials and discloses a wear-resistant inflatable swimming pool. The wear-resistant inflatable swimming pool is prepared from thefollowing raw materials: PVC resin, chlorinated paraffin, fumed silica, nano-titania, zinc oxide, antibacterial sepiolite, a stabilizer, polymethyl methacrylate and aminophylline. The inflatable swimming pool is high in strength and wear resistance, germs are inhibited effectively, the service life of the swimming pool is enabled to reach 0.33-0.35 million people, and use demands of consumers aremet. The PVC resin, the chlorinated paraffin, the stabilizer graphene and polymethyl methacrylate are heated slowly to be mixed sufficiently, the heat-resistant temperature and the tensile strength ofthe PVC resin are enhanced, the wear resistance is improved, the flowability and the softness of the raw materials are enhanced, and later forming is facilitated; then the antibacterial sepiolite andthe aminophylline are added to a premix, the antibacterial sepiolite is promoted to be crosslinked with the PVC resin sufficiently, germ proliferation is inhibited, sepiolite swells after absorbing water, thickness of the swimming pool can be increased, wear resistance and bump resistance are improved, and the service life of the swimming pool is prolonged.

Description

technical field [0001] The invention mainly relates to the technical field of polymer materials, in particular to a wear-resistant inflatable swimming pool. Background technique [0002] Inflatable swimming pool is a portable swimming pool for children and families to bathe and entertain in summer. At present, the traditional inflatable swimming pool is made of PVC and mesh, which is relatively light. However, inflatable swimming pools are generally used outdoors, and the bumps and frictions on the swimming pool are serious. Therefore, air leakage often occurs and needs to be repaired, which affects the appearance and service life of the inflatable swimming pool. Moreover, when the swimming pool is used by a large number of people, coupled with external environmental pollution, it is easy to cause germs to multiply and cause skin allergies to users. The health of consumers is greatly endangered. Contents of the invention [0003] In order to remedy the defects of the prio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L33/12C08L91/06C08K13/06C08K3/36C08K3/22C08K3/34C08K3/04C08K5/3462
Inventor 刘辉
Owner 刘辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com