Component and preparation method of alkoxy magnesium particle
A technology of magnesium oxide and particles is applied in the field of components of spherical magnesium alkoxide particles, which can solve the problems of high cost, low bulk density, uneven large particles or fine powder, etc., and achieves reduction of production cost and particle sphericity. Good, narrow particle size distribution effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] Example 1
[0028] Fully replace the reactor with high-purity nitrogen, add 0.1 g of Viscoplex 1-156 (acrylate polymer content 40-44% wt), 20 ml of absolute ethanol and 0.1 g of iodine under the protection of nitrogen, stir to dissolve and raise the temperature, add 80 -150 mesh magnesium powder 1.0 g and 10 ml absolute ethanol, maintain reflux reaction, add 80-150 mesh magnesium powder 1.0 g and 10 ml absolute ethanol again at 20 minutes intervals, add 4.0 g magnesium powder and 55 ml in 4 times Anhydrous ethanol, keep refluxing reaction for 4 hours after adding the material, and then wash twice with anhydrous ethanol, the amount of anhydrous ethanol is 80ml each time, and then wash twice with hexane, the amount of hexane each time is 100 Ml, after washing is completed, dry to obtain off-white solid flowable powder, the specific results are shown in Table 1.
Example Embodiment
[0029] Example 2
[0030] The difference between this example and Example 1 is only: the "0.1 g Viscoplex 1-156 (acrylate polymer content 40-44% wt)" in Example 1 is adjusted to "0.5 g Viscoplex 1-156 (acrylate polymer Content 40-44%wt)".
Example Embodiment
[0031] Example 3
[0032] The difference between this embodiment and the embodiment 1 is only: the "0.1 g of iodine" in the embodiment 1 is adjusted to "0.4 g of iodine".
PUM
Property | Measurement | Unit |
---|---|---|
Bulk density | aaaaa | aaaaa |
Melt index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap