Microalloyed Ti-Zr-Hf-V-Nb-Ta refractory high-entropy alloy and preparation method thereof

A ti-zr-hf-v-nb-ta, high-entropy alloy technology, applied in the field of metal materials, can solve problems such as poor plasticity of refractory high-entropy alloys, and achieve the effects of high strength, simple operation and good plasticity

Active Publication Date: 2018-06-29
北京中辰至刚科技有限公司
View PDF9 Cites 51 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problem of poor plasticity of existing refractory high-entropy alloys, the object of the present invention is to provide a microalloyed Ti-Zr-Hf-V-Nb-Ta refractory high-entropy alloy and its preparation method, mainly by adjusting the main composition The pr...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microalloyed Ti-Zr-Hf-V-Nb-Ta refractory high-entropy alloy and preparation method thereof
  • Microalloyed Ti-Zr-Hf-V-Nb-Ta refractory high-entropy alloy and preparation method thereof
  • Microalloyed Ti-Zr-Hf-V-Nb-Ta refractory high-entropy alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Ti 32 Zr 30 f 5 V 10 Nb 13 Ta 5 Al 5 The specific preparation steps of the refractory high-entropy alloy are as follows:

[0045] (1) Using elemental Ti, Zr, Hf, V, Nb, Ta and Al with a purity of more than 99.7wt% as raw materials, first remove the scale on the surface of the raw materials by grinding with a grinding wheel, and then use absolute ethanol to carry out ultrasonic vibration cleaning to obtain Clean raw materials, and according to the atomic percentage of Ti:Zr:Hf:V:Nb:Ta:Al=32:30:5:10:13:5:5, weigh out the clean raw materials with a total mass of (80±0.01)g raw material;

[0046] (2) Put the weighed elemental Hf, Nb and Ta into a water-cooled copper crucible in a high-vacuum non-consumable arc melting furnace, and then vacuumize until the vacuum in the melting furnace reaches 2.5×10 -3 After Pa, fill high-purity argon as a protective gas; before melting the alloy, first melt the pure titanium metal ingot to further reduce the oxygen content in the f...

Embodiment 2

[0051] Ti 42 Zr 15 f 15 Nb 12 Ta 10 Al 6 The specific preparation steps of the refractory high-entropy alloy are as follows:

[0052] (1) Using elemental Ti, Zr, Hf, Nb, Ta and Al with a purity of more than 99.7wt% as raw materials, first remove the scale on the surface of the raw materials by grinding with a grinding wheel, and then use absolute ethanol to carry out ultrasonic vibration cleaning to obtain clean Raw materials, and according to the atomic percentage of Ti:Zr:Hf:Nb:Ta:Al=42:15:15:12:10:6, weigh the clean raw materials with a total mass of (80±0.01) g;

[0053] (2) Put the weighed elemental Hf, Nb and Ta into a water-cooled copper crucible in a high-vacuum non-consumable arc melting furnace, and then vacuumize until the vacuum in the melting furnace reaches 2.5×10 -3 After Pa, fill high-purity argon as a protective gas; before melting the alloy, first melt the pure titanium metal ingot to further reduce the oxygen content in the furnace cavity, and then car...

Embodiment 3

[0058] Ti 30 Zr 8 f 20 Nb 8 Ta 30 Al 4 The specific preparation steps of the refractory high-entropy alloy are as follows:

[0059] (1) Using elemental Ti, Zr, Hf, Nb, Ta and Al with a purity of more than 99.7wt% as raw materials, first remove the scale on the surface of the raw materials by grinding with a grinding wheel, and then use absolute ethanol to carry out ultrasonic vibration cleaning to obtain clean Raw materials, and according to the atomic percentage of Ti:Zr:Hf:Nb:Ta:Al=30:8:20:8:30:4, weigh the clean raw materials with a total mass of (80±0.01) g;

[0060] (2) Put the weighed elemental Hf, Nb and Ta into a water-cooled copper crucible in a high-vacuum non-consumable arc melting furnace, and then vacuumize until the vacuum in the melting furnace reaches 2.5×10 -3 After Pa, fill high-purity argon as a protective gas; before melting the alloy, first melt the pure titanium metal ingot to further reduce the oxygen content in the furnace cavity, and then carry o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a microalloyed Ti-Zr-Hf-V-Nb-Ta refractory high-entropy alloy and a preparation method thereof, and belongs to the technical field of metal materials. The refractory high-entropy alloy is endowed with good plasticity and high strength mainly by adjusting the ratio of main components and adding a small amount of microalloyed elements, and the density can be adjusted in a relatively wide range; in addition, during a preparation process, Hf, Nb, Ta and microalloyed elements other than Al at high melting points are pre-alloyed and smelted first, and then Ti, Zr, V and Al are added for final alloying smelting, thereby facilitating uniform mixing of a plurality of components with large differences in melting point, and ensuring the excellent comprehensive performance ofthe prepared refractory high-entropy alloy.

Description

technical field [0001] The invention specifically relates to a microalloyed Ti-Zr-Hf-V-Nb-Ta refractory high-entropy alloy with high strength and good plasticity and a preparation method thereof, belonging to the technical field of metal materials. Background technique [0002] High-entropy alloys, also known as multi-principal alloys, are a new class of alloys developed in recent years. They are defined as alloys composed of five or more elements in equiatomic ratios or near equiatoms. The content of each major component is 5-35 at.%; In addition, other alloying elements can also be added for alloying, and the addition amount is less than 5 at.%. The multi-principal composition characteristics of high-entropy alloys are different from traditional alloys that have clear matrix elements (such as Fe-based alloys, Ti-based alloys, Al-based alloys, and Ni-based alloys, etc.), so they have a lot of properties in liquid or disordered solid solution states. High mixing entropy, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C30/00C22C1/02
CPCC22C1/02C22C30/00
Inventor 薛云飞曹堂清王本鹏王富耻王鲁刘旭东岳晗才鸿年
Owner 北京中辰至刚科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap