Copper braided wire manufacturing method

A technology of copper braided wire and production method, which is applied in cable/conductor manufacturing, electrical components, circuits, etc., can solve the problems of easy oxidation, blackening, and decreased electrical conductivity, and achieves strong anti-oxidation ability, high application value, and is not easy to be used. blackening effect

Inactive Publication Date: 2018-08-14
铜陵集思意特种编织线有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The current copper braided wire is easily oxidized and blackened during use, resulting in a gradual decline in its electrical conductivity over time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The copper braided wire manufacturing method is as follows:

[0022] Step 1. Pull the polished and cleaned red copper into an oxygen-free copper rod with a diameter of 6mm;

[0023] Step 2. Pull the oxygen-free copper rod with a diameter of 6mm into an inner wire with a diameter of 2.6mm;

[0024] Step 3. The inner withdrawing wire with a diameter of 2.6mm is first drawn into thick copper wire with a diameter of 1.0mm through the first wire drawing machine; then the thick copper wire with a diameter of 1.0mm is drawn into a diameter of 0.2 mm fine copper wire; and then through the third wire drawing machine, the thin copper wire with a diameter of 0.2mm is drawn into an ultra-fine copper wire with a diameter of 0.05mm;

[0025] Step 4. Twist several (such as 200) ultra-fine copper wire bundles with a diameter of 0.05mm into a strand according to customer requirements, and then compound and twist several strands (such as 10) into a composite blank wire;

[0026] Step 5...

Embodiment 1

[0032] The production method of the contrast copper braided wire is as follows:

[0033] Step 1. Pull the polished and cleaned red copper into an oxygen-free copper rod with a diameter of 6mm;

[0034] Step 2. Pull the oxygen-free copper rod with a diameter of 6mm into an inner wire with a diameter of 2.6mm;

[0035] Step 3. The inner withdrawing wire with a diameter of 2.6mm is first drawn into thick copper wire with a diameter of 1.0mm through the first wire drawing machine; then the thick copper wire with a diameter of 1.0mm is drawn into a diameter of 0.2 mm fine copper wire; and then through the third wire drawing machine, the thin copper wire with a diameter of 0.2mm is drawn into an ultra-fine copper wire with a diameter of 0.05mm;

[0036] Step 4. Twist several (such as 200) ultra-fine copper wire bundles with a diameter of 0.05mm into a strand according to customer requirements, and then compound and twist several strands (such as 10) into a composite blank wire;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a copper braided wire manufacturing method, including the following steps: drawing polished and cleaned red copper into an oxygen-free copper rod, drawing the oxygen-free copper rod into an internal annealing wire, drawing the internal annealing wire into superfine copper wires through multiple wire drawing machines, twisting the superfine copper wires into a stranded wire, and then combining and twisting the stranded wire into a composite blank wire; and annealing the composite blank wire to obtain a composite wire, braiding the composite wire on a braiding machine toform a semi-finished wire, and removing the oil stain on the surface of the semi-finished wire by using a centrifugal dryer to manufacture a copper braided wire. Through the optimization design of anexisting copper braided wire manufacturing process, a finished product manufactured by using the copper braided wire manufacturing method disclosed by the invention has a strong anti-oxidation ability, and the finished product is not easy to blacken, is good in tensile strength and high in product quality, and has high application values.

Description

technical field [0001] The invention relates to the technical field of electrical accessories, in particular to a method for manufacturing copper braided wires. Background technique [0002] Copper braided wire is made of oxygen-free copper or low-oxygen copper wire. The diameter of copper wire is divided into 0.05mm / 0.06mm / 0.08mm / 0.10mm / 0.12mm / 0.15mm / 0.20mm. The more flexible the product, the more resistant to bending. During the processing, it is toughened to make the product soft, bright and neat in appearance. [0003] Copper braided wires can be used for transformer installation, high and low voltage switchgear cabinets, vacuum appliances, closed busbars, generators and busbars, rectifier equipment, connections between rectifier cabinets and isolating switches, and connections between busbars. It can improve the conductivity, adjust the installation error of the equipment, and at the same time play the role of (shock absorption) work compensation, and facilitate the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/00H01B13/02
CPCH01B13/00H01B13/02
Inventor 俞克珍
Owner 铜陵集思意特种编织线有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com