Water-based solid vehicle polishing protection wax and preparation method thereof

A light protection, water-based technology, applied in chemical instruments and methods, wax coatings, polishing compositions, etc., can solve the problems of high product cost, environmental pollution, unpleasant taste, etc., achieve good protection, reduce costs, Long-lasting effect of glazing protection time

Inactive Publication Date: 2018-08-17
广东驰安汽车用品科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although pure solvent-based car glazing protection solid wax has good hydrophobicity, long-lasting protection time and stable product, due to the use of a large amount of solvent, the product cost is high and it is not environmentally friendly. There is a certain stimulation, and at the same time it will release a large amount of VOC (Volatile Organic Compounds), which will also pollute the environment, and there are great dangers in the process of storage and transportation. Therefore, on the basis of the existing car glazing protection wax , the technical problem to be solved is how to improve its environmental protection performance and reduce product cost on the basis of maintaining the hydrophobicity, durability and stability of solid automotive glazing wax

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based solid vehicle polishing protection wax and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] The preparation method of the water-based solid automobile glazing protection wax described in the present embodiment, its preparation steps are as follows:

[0020] One, take the total weight of the water-based solid automobile glazing protective wax as a benchmark, take by weighing polyethylene synthetic wax 6.0%, paraffin wax 3.0%, microcrystalline wax 5.0%, carnauba wax 5.0% and 30% to remove Ionized water, stir and mix and heat to 90-100°C until the material dissolves evenly;

[0021] 2. Taking the total weight of the water-based solid automotive glazing protective wax that is finally prepared as a benchmark, take by weighing 3.0% of methylphenyl silicone oil, 2.0% of fluorosilicone resin, 2.0% of acrylic acid copolymer, 1.0% of dispersant, poly Oxyethylene octylphenol ether-10 (OP-10) 1.0%, fatty alcohol polyoxyethylene ether (AEO-9) 0.4%, sodium lauryl sulfate (K12) 0.5% and deionized water of the remainder, stirring Heat to 90-100°C, mix evenly, and disperse an...

Embodiment 2

[0025] The water-based type solid automobile glazing protection wax described in the present embodiment is made up of the composition of following mass percent: polyethylene synthetic wax 8.0%, paraffin wax 3.0%, microcrystalline wax 4.0%, carnauba wax 6.0%, formazan 2.0% phenyl silicone oil, 2.0% fluorosilicone resin, 2.0% acrylic copolymer, 1.0% dispersant, 0.1% yellow pigment (HC Yellow 13), 0.5% polyoxyethylene octylphenol ether-10 (OP-10) , coconut oil fatty acid diethanolamide (6501) 0.5%, sodium dodecylbenzenesulfonate (LAS) 0.5%, deionized water 70.4%.

[0026] The preparation method of the water-based solid automobile glazing protection wax described in the present embodiment, its preparation steps are as follows:

[0027] One, take the total weight of the water-based solid automobile glazing protective wax as a benchmark, take by weighing polyethylene synthetic wax 8.0%, paraffin wax 3.0%, microcrystalline wax 4.0%, carnauba wax 6.0% and 30% to remove Ionized water,...

Embodiment 3

[0031] The water-based type solid automobile glazing protective wax described in this implementation, it is made up of the composition of following mass percent: polyethylene synthetic wax 7.0%, paraffin wax 3.0%, microcrystalline wax 5.0%, carnauba wax 7.0%, methyl Phenyl silicone oil 2.0%, fluorosilicone resin 2.0%, acrylic copolymer 2.0%, dispersant 1.0%, yellow pigment (HC Yellow 13) 0.1%, fatty alcohol polyoxyethylene ether (AEO-9) 0.5%, polyoxyethylene Sorbitan monooleate) (Tween-80) 0.5%, sodium oleate 0.5%, deionized water 69.4%.

[0032] The preparation method of the water-based solid automobile glazing protection wax described in the present embodiment, its preparation steps are as follows:

[0033] One, take the total weight of the water-based solid automobile glazing protective wax as a benchmark, take by weighing polyethylene synthetic wax 7.0%, paraffin wax 3.0%, microcrystalline wax 5.0%, carnauba wax 7.0% and 30% to remove Ionized water, stir and mix and heat ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-based solid vehicle polishing protection wax and a preparation method thereof, and relates to the technical field of vehicle maintenance, wherein the water-based solid vehicle polishing protection wax comprises, by mass, 5.0-10.0% of polyethylene synthetic wax, 3.0-8.0% of paraffin, 3.0-8.0% of microcrystalline wax, 5.0-10.0% of carnauba wax, 2.0-8.0% of methylphenylsilicone oil, 2.0-3.0% of fluorosilicone resin, 1.0-2.0% of an anionic surfactant, 1.0-2.0% of a nonionic surfactant, 40-60% of deionized water, 1.0-2.0% of a dispersing agent, 0.1% of a yellow pigment, and 1.0-5.0% of an acrylic copolymer. According to the present invention, the water-based solid vehicle polishing protection wax has the characteristics of good stability, excellent hydrophobicityand lasting polishing protection time of the general pure solvent type solid vehicle polishing protection wax, and further has characteristics of substantially-reduced cost, improved environment protection performance, improved storage safety and improved transportation safety.

Description

technical field [0001] The invention relates to the technical field of automobile maintenance, in particular to a water-based solid automobile glazing protective wax and a preparation method thereof. Background technique [0002] With the rapid development of the automobile industry, people pay more and more attention to automobile maintenance, and the market demand for automobile glazing wax and polishing agent products is strong. At present, the automotive glazing protective waxes widely used in the domestic market are mainly pure solvent-based solid automotive glazing protective waxes, oil-in-water (0 / W) emulsion liquids or paste automotive glazing protective waxes. Although pure solvent-based car glazing protection solid wax has good hydrophobicity, long-lasting protection time and stable product, due to the use of a large amount of solvent, the product cost is high and it is not environmentally friendly. There is a certain stimulation, and at the same time it will rele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D123/06C09D191/06C09D183/04C09D183/08C09D133/02C09G1/12
CPCC08L2205/025C08L2205/035C09D123/06C09D191/06C09G1/12C08L91/06C08L83/04C08L83/08C08L33/02C08L23/06
Inventor 刘祥海