Fly ash based geopolymer high-strength grouting material and preparation method thereof

A fly ash and polymer technology, applied in cement production, etc., can solve problems such as the inability to meet the strength requirements of grouting materials, poor volume stability of finished products, etc., and achieve the effects of easy implementation, high fluidity and wide application range

Active Publication Date: 2018-08-21
GUANGDONG LIANCHENG RESIDENTIAL EQUIP INFORMATION TECH CO LTD
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the defect of this material is very obvious. Excessive use of mixed powder materials will inevitably lead to poor volume stability of the finished product. Secondly, its 28-day strength is only 21.16MPa, which cannot meet the strength requirements of grouting materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fly ash based geopolymer high-strength grouting material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] A fly ash-based polymer high-strength grouting material, comprising the following components and their parts by weight: 10-20 parts of alkali activator, 30-45 parts of fly ash, 2-10 parts of silica fume, 1-5 parts of plant ash, Sand: 30-45 parts, superfine powder: 1-5 parts, expansion agent: 0.1-5 parts, defoamer: 0.1-0.5 parts, water 3-8 parts; Coal ash, silica fume, plant ash and other active materials are used as cementing materials. After being activated by alkali activators, they are mixed with graded sand and then used together with a small amount of expansion agent and defoamer to prepare early strength, rapid hardening, high fluidity, and micro-expansion. high-strength grouting material.

[0032] As a specific scheme, the alkali activator adopts water glass and caustic soda powder with a modulus of 2.0 to 2.5, and is prepared at a mass ratio of 2: 1. The excitation effect of this composite activator is the best. Increasing the caustic soda content will speed up...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
activation indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fly ash based geopolymer high-strength grouting material which comprises the following components in parts by weight: 10-20 parts of an alkali activator, 30-45 parts of fly ash, 2-10 parts of silica fume, 1-5 parts of plant ash, 30-45 parts of sand, 1-5 parts of superfine powder, 0.1-5 parts of an expanding agent, 0.1-0.5 part of an antifoaming agent and 3-8 parts of water. According to the geopolymer high-strength grouting material provided by the invention, active materials such as the fly ash, silica fume, and plant ash serving as binders are activated by the alkali activator, mixed with graded sand and matched with a small usage amount of expanding agent, antifoaming agent and the like so as to prepare the high-strength grouting material with early strength, rapid hardening, high fluidity and micro expansion. The invention further discloses a preparation method of the fly ash based geopolymer high-strength grouting material. The preparation method is easyand rapid to implement, energy-saving and environmentally friendly.

Description

technical field [0001] The invention relates to the technical field of high-performance concrete, in particular to a fly ash base polymer high-strength grouting material and a preparation method thereof. Background technique [0002] With the emergence and development of high-strength and high-performance concrete, the emergence of high-strength grouting materials has made grouting materials no longer limited to equipment foundation grouting, and has rapidly expanded to building foundation reinforcement, building reinforcement, building beams, slabs, column reconstruction, Sleeve grouting and many other uses. At present, the widely used high-strength cement-based grouting material is easy to produce micro-cracks due to the large volume shrinkage of ordinary Portland cement, which leads to inconsistency under the bearing plate after the support is installed, and the strength of cement-based grouting material develops slowly , poor durability, will directly affect the structu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/70
CPCC04B28/006C04B2111/70C04B2201/05C04B2201/52C04B12/04C04B22/062C04B18/08C04B18/146C04B18/101C04B14/068C04B14/042C04B2103/0068C04B2103/50Y02P40/10
Inventor 不公告发明人
Owner GUANGDONG LIANCHENG RESIDENTIAL EQUIP INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap