Doped strontium titanate thin film-based low-power-consumption resistor switch storage unit and preparation method and application thereof

A resistive switch and storage unit technology, applied in the field of information storage, can solve the problems of no major breakthrough in reducing power consumption, small on/off current ratio, high set/reset voltage, etc., so as to reduce power consumption and improve on/off Effect of OFF current ratio and lower set/reset voltage

Inactive Publication Date: 2018-08-24
SOUTHWEST UNIVERSITY
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it has been reported in the literature that strontium titanate films doped with Fe, Cr, Nb and other metals have a resistance switching effect, but from the current research results, the strontium titanate films doped with metals are amorphous or polycrystalline films. In the application of switching memory, there are still problems such as high set / reset voltage and small on / off current ratio, and there is still no major breakthrough in reducing power consumption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Doped strontium titanate thin film-based low-power-consumption resistor switch storage unit and preparation method and application thereof
  • Doped strontium titanate thin film-based low-power-consumption resistor switch storage unit and preparation method and application thereof
  • Doped strontium titanate thin film-based low-power-consumption resistor switch storage unit and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1, a method for preparing a low power consumption resistive switch memory cell based on a doped strontium titanate thin film, which includes the following steps:

[0037] Step 1: Select a conventional semiconductor Si single crystal substrate as the substrate, and prepare the lower electrode layer by DC magnetron sputtering in an argon atmosphere. The process conditions are: metal Pt is used as the sputtering target, and the sputtering gas is Argon gas, the sputtering pressure is 2.7Pa, the sputtering temperature is 350°C, the sputtering power is 35W, a bias voltage of -100V is applied, and the growth rate is 10-15nm / min;

[0038] In step 2, the substrate with the lower electrode layer is preheated at a temperature of 600° C., and then the Fe / strontium titanate thin film resistive layer is prepared on the lower electrode layer by radio frequency magnetron sputtering. The process conditions are: : Strontium titanate ceramic target with a purity of 99.9% and a ...

Embodiment 2

[0041] Embodiment 2, a method for preparing a low power consumption resistive switch memory cell based on a doped strontium titanate thin film, which includes the following steps:

[0042] Step 1: Select a conventional semiconductor Si single crystal substrate as the substrate, and prepare the lower electrode layer by DC magnetron sputtering in an argon atmosphere. The process conditions are: metal Pt is used as the sputtering target, and the sputtering gas is Argon gas, the sputtering pressure is 2Pa, the sputtering temperature is 300°C, the sputtering power is 25W, a bias voltage of -100V is applied, and the growth rate is 10-15nm / min;

[0043] In step 2, the substrate with the lower electrode layer is preheated at a temperature of 800° C., and then the Fe / strontium titanate thin film resistive layer is prepared on the lower electrode layer by radio frequency magnetron sputtering. The process conditions are: : Strontium titanate ceramic target with a purity of 99.9% and a Fe...

Embodiment 3

[0046] Embodiment 3, a method for preparing a low power consumption resistive switch memory cell based on a doped strontium titanate thin film, which includes the following steps:

[0047] Step 1: Select a conventional semiconductor Si single crystal substrate as the substrate, and prepare the lower electrode layer by DC magnetron sputtering in an argon atmosphere. The process conditions are: metal Pt is used as the sputtering target, and the sputtering gas is Argon gas, the sputtering pressure is 1Pa, the sputtering temperature is 400°C, the sputtering power is 45W, a bias voltage of -100V is applied, and the growth rate is 10-15nm / min;

[0048] In step 2, the substrate with the lower electrode layer is preheated at a temperature of 300° C., and then the Fe / strontium titanate thin film resistive layer is prepared on the lower electrode layer by radio frequency magnetron sputtering. The process conditions are: : Strontium titanate ceramic target with a purity of 99.9% and a Fe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a doped strontium titanate thin film-based low-power-consumption resistor switch storage unit and a preparation method and an application thereof. The resistor switch storage unit comprises a substrate layer, a lower electrode layer, a resistive random layer and an upper electrode layer which are arranged from the bottom up in sequence; the resistive random layer is a Fe / strontium titanate thin film resistive random layer which dopes Fe in the strontium titanate thin film; and the doping amount of Fe is 1-10at%. The resistor switch storage unit is low in setting / resetting voltage, high in on / off current ratio, and high in resistor switch stability.

Description

technical field [0001] The invention relates to the technical field of information storage, in particular to a low-power consumption resistance switch memory unit based on a doped strontium titanate thin film and its preparation method and application. Background technique: [0002] Resistive switch memory has become one of the most promising new-generation memories because of its advantages of fast read and write speed, low power consumption, high integration and good compatibility with today's semiconductor technology. The commonly used materials for the resistive switch layer in existing resistive switch memory cells mainly include perovskite-type multi-component inorganic oxides and organic oxides, such as SrZrO 3 , SrTiO 3 、CH 3 NH 3 PB 3 , binary transition metal oxides with simple structures, such as NiO, TiO 2 , V x o y , ZrO 2 , HfO 2 And graphene, etc., these materials have the disadvantages of high set / reset voltage or large ON state operating current, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01L45/00
CPCH10N70/24H10N70/8836H10N70/043H10N70/026
Inventor 邱晓燕江雪魏明龙
Owner SOUTHWEST UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com