Porous dandelion-shaped Pd nanometer dendrite preparation method, material obtained with same, and application

A dandelion-like nano-technology, which is applied in nanotechnology, transportation and packaging, metal processing equipment, etc., can solve problems such as technical limitations and complex synthetic routes, and achieve a clear mechanism of the preparation process, a simple preparation method, and large-scale production. Effect

Active Publication Date: 2018-09-18
NANJING NORMAL UNIVERSITY
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are certain technical limitations in the preparation of hollow nanostructures in noble metal-based alloys by displacement reactions.
At the same time, the synthe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous dandelion-shaped Pd nanometer dendrite preparation method, material obtained with same, and application
  • Porous dandelion-shaped Pd nanometer dendrite preparation method, material obtained with same, and application
  • Porous dandelion-shaped Pd nanometer dendrite preparation method, material obtained with same, and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation method of porous dandelion-like Pd nano dendrites, comprising the following steps:

[0030] 1) Preparation of reaction solution: Accurately weigh 0.038mg N,N'-methylenebisacrylamide (MBAA), add 9.5mL H 2 O, make it fully dissolved, add 0.5mL 0.05M K 2 PdCl 4 Solution, fully ultrasonicated to make it evenly mixed.

[0031] 2) Preparation of porous dandelion-like Pd nanodendrites: the reaction solution was allowed to stand at room temperature (25°C) for 10 min to obtain a black precipitate. The black precipitate is centrifuged, washed, and dried to obtain the porous dandelion-like Pd nanodendrite.

Embodiment 2

[0033] A preparation method of porous dandelion-like Pd nano dendrites, comprising the following steps:

[0034] 1) Preparation of reaction solution: Accurately weigh 50 mg of N, N'-methylenebisacrylamide (MBAA), add 9.5 mL of H 2 O, make it fully dissolved, add 0.5mL 0.05M K 2 PdCl 4 Solution, fully ultrasonicated to make it evenly mixed.

[0035] 2) Preparation of porous dandelion-like Pd nanodendrites: the reaction solution was allowed to stand at room temperature (25°C) for 10 min to obtain a black precipitate. The black precipitate is centrifuged, washed, and dried to obtain the porous dandelion-like Pd nanodendrite.

Embodiment 3

[0037] A preparation method of porous dandelion-like Pd nano dendrites, comprising the following steps:

[0038] 1) Preparation of reaction solution: Accurately weigh 385.43 mg N, N'-methylenebisacrylamide (MBAA), add 9.5 mL H 2 O, make it fully dissolved, add 0.5mL 0.05M K 2 PdCl 4 Solution, fully ultrasonicated to make it evenly mixed.

[0039] 2) Preparation of porous dandelion-like Pd nanodendrites: the reaction solution was allowed to stand at room temperature (25°C) for 10 min to obtain a black precipitate. The black precipitate is centrifuged, washed, and dried to obtain the porous dandelion-like Pd nanodendrite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a porous dandelion-shaped Pd nanometer dendrite preparation method, a material obtained with the porous dandelion-shaped Pd nanometer dendrite preparation method, and the application using the material as an oxygen reduction cathode catalyst. According to the porous dandelion-shaped Pd nanometer dendrite preparation method, N,N'-methylene bisacrylamide (MBAA) is used as a complexing agent, a structure-directing agent and a reducing agent, and metal precursors are quickly reduced into porous dandelion-shaped Pd nanometer dendrites by adopting a standing reduction methodin one step. The porous dandelion-shaped Pd nanometer dendrites obtained with the method have the advantages of being regular in morphology, ultrafine in grain size, high in electrocatalytic activityand the like, and show high catalytic activity and stability when serving as the oxygen reduction cathode catalyst. The porous dandelion-shaped Pd nanometer dendrite preparation method is simple, efficient and universal.

Description

technical field [0001] The invention relates to a method for preparing porous dandelion-like Pd nano dendrites and the obtained materials and applications thereof, belonging to the technical field of Pd nano dendrites. Background technique [0002] Facing the problems of energy shortage and environmental pollution, a large number of scientific researchers are devoted to the development and development of clean energy technology. Unlike other energy conversion devices, fuel cells can directly convert chemical energy into electrical energy, and have the advantages of no pollution, zero emissions, high efficiency, wide application, and diversified fuels. It is expected to become the most potential energy supply device in the future. However, there are still some urgent problems to be solved on the road to commercialization of fuel cells, the most prominent of which is the design and synthesis of low-platinum or non-platinum electrocatalysts with high catalytic activity and good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F1/00B22F9/24B82Y40/00
CPCB82Y40/00B22F9/24B22F2009/245B22F1/0553B22F1/07B22F1/054
Inventor 唐亚文江娴黄祯娜邓思辉孙境泽付更涛徐林孙冬梅
Owner NANJING NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products