A method for preparing bio-oil by ball milling pretreatment microcrystalline cellulose pyrolysis

A microcrystalline cellulose and pretreatment technology, which is applied in the preparation of biofuels, biological raw materials, liquid hydrocarbon mixtures, etc., can solve the problems of cumbersome processing and achieve the effect of high economic value

Active Publication Date: 2020-12-01
ANHUI UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These effective methods all need to add minerals, solvents, etc., and the processing is relatively cumbersome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing bio-oil by ball milling pretreatment microcrystalline cellulose pyrolysis

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1, preparation of bio-oil by pyrolysis of microcrystalline cellulose

[0030] Get 1 part of microcrystalline cellulose, when the furnace temperature rises to 400 °C, slowly add cellulose (the size of the feed is related to the reaction device, for the experimental device used in the embodiment, the feed is 0.10g / min, nitrogen The purging speed is 30ml / min), so that the cellulose is pyrolyzed through the high temperature zone, and the products of cellulose pyrolysis are separated to obtain liquid, gas and solid products.

Embodiment 2

[0031] Example 2, preparation of bio-oil by pyrolysis of microcrystalline cellulose

[0032] The operation of this embodiment is the same as that of Embodiment 1, except that the temperature of the furnace in this embodiment is 420°C.

Embodiment 3

[0033] Embodiment 3, preparation of bio-oil by pyrolysis of microcrystalline cellulose

[0034] The operation of this embodiment is the same as that of Embodiment 1, except that the temperature of the furnace in this embodiment is 450° C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing biological oil by ball milling pretreatment and pyrolysis of microcrystalline celluloses. The method comprises the steps: S1, carrying out ball millingpretreatment on microcrystalline celluloses; S2, gradually adding the celluloses into a pyrolysis device for a pyrolysis reaction under the temperature condition of 400-600 DEG C and at the protectiveatmosphere of inert gases; and S3, ending the reaction, separating and collecting a product. The celluloses are subjected to ball milling treatment, so that the crystallinity of the celluloses is reduced, the highest yield of the biological oil can be obtained at 450 DEG C, the pyrolysis temperature is lowered, the energy consumption is reduced, and the pyrolysis efficiency is increased.

Description

technical field [0001] The invention belongs to the field of organic chemical industry, and in particular relates to a method for preparing bio-oil by pyrolysis of ball-milling pretreated microcrystalline cellulose. Background technique [0002] Today, the exploitation and use of a large number of fossil resources emits a large amount of carbon dioxide, sulfur dioxide and other gases. The emission of these gases has not only caused increasingly serious environmental problems, but also the extensive exploitation and use of fossil resources has made the fossil resources such as coal, oil and natural gas that can be developed and utilized on the earth less and less. Therefore, it is necessary to look for and develop renewable Resources are very necessary, and biomass resources can just solve these problems. At present, biomass is the only renewable energy that can obtain liquid fuel, and it has received extensive attention from all over the world. As the main component of bio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10G3/00C10B53/02C10L3/06
CPCC10B53/02C10G3/00C10L3/06Y02E50/10Y02P30/20
Inventor 赵岩杨丽群刘银
Owner ANHUI UNIV OF SCI & TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com