Glass fiber asphalt material

A technology of glass fiber asphalt and asphalt material, applied in the direction of glass/slag layered products, layered products, synthetic resin layered products, etc., can solve the problems of tearing, material stretching, poor weather resistance, etc., to prolong the service life , the effect of reducing hollowing and enhancing ductility

Inactive Publication Date: 2018-10-09
桂林立竣建筑工业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

SBR modified asphalt asphalt material is a commonly used asphalt material, but because of its own characteristics, the weather resistance of the asphalt material is poor, and it is easy to cause material stretching and tearing due to changes in ambient temperature, which in turn causes water leakage, which affects the impermeability of the main structure Defensive measures cause damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber asphalt material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] 1. A glass fiber asphalt material, including (1) 0.2mm thick PE film layer, (2) 0.1mm thick shale fiber reinforced layer, (3) 2mm thick SBR modified asphalt asphalt material from top to bottom, ( 4) 1mm thick glass fiber felt base cloth.

[0014] 2. The above (1), (2), (3) and (4) structural layers are bonded together by (5) water-resistant cyanoacrylate adhesive.

[0015] figure 1 It is a structural schematic diagram of a specific embodiment of a glass fiber asphalt material of the present invention.

[0016] The meanings of reference marks in the figure: (1)—0.2mm thick PE film layer, (2)—0.1mm thick shale fiber reinforced layer, (3)—2mm thick SBR modified asphalt asphalt material, (4)—1mm Thick fiberglass felt base fabric, (5)—water-resistant cyanoacrylate binder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of building materials, and provides a glass fiber asphalt material, which sequentially comprises (1) a PE film layer with a thickness of 0.2 mm, (2) a shale fiber reinforced layer with a thickness of 0.1 mm, (3) a SBR modified asphalt material with a thickness of 2 mm, and (4) a glass fiber felt base cloth with a thickness of 1 mm from top to bottom. According tothe present invention, through the PE film protection and the rock wool fiber reinforcement treatment, the ductility of the asphalt material is enhanced, and the service life of the asphalt materialmain body is prolonged; various materials are adhered with the water-resistant cyano acrylate adhesive so as to reduce the occurrence of the hollowing phenomenon; and a variety of materials synergistically work so as to provide the advantages of the materials.

Description

technical field [0001] The invention belongs to the field of building materials and provides a self-adhesive modified asphalt asphalt material. Background technique [0002] Asphalt material is a common building construction material, which is widely used in the waterproof sealing of building roofs, basements and rooms with water. SBR modified asphalt asphalt material is a commonly used asphalt material, but because of its own characteristics, the weather resistance of the asphalt material is poor, and it is easy to cause material stretching and tearing due to changes in ambient temperature, which in turn causes water leakage, which affects the impermeability of the main structure Defensive measures cause damage. Contents of the invention [0003] In order to overcome the deficiencies of the prior art and enhance the ductility of the asphalt material, the present invention proposes a glass fiber asphalt material. [0004] Technical solutions [0005] 1. A glass fiber as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/32B32B27/12B32B9/00B32B9/04B32B17/02B32B11/10B32B7/10E04D5/10
CPCB32B27/32B32B7/10B32B11/10B32B27/12B32B2262/10B32B2262/101E04D5/10
Inventor 白克雯
Owner 桂林立竣建筑工业有限公司