Preparation method of non-woven material used for wiping cloth

A technology of non-woven materials and wiping cloth, which is applied in the direction of non-woven fabrics, textiles, and papermaking. It can solve the problems of lint and fluff on the cloth surface, non-wear resistance, and affect the wiping effect, so as to improve air permeability and wear resistance. Good, good wiping effect

Inactive Publication Date: 2018-10-16
史茜赟
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The technical problem to be solved by the present invention: Aiming at the problem that the existing non-woven wiping cloth is not wear-resistant during the repeated wiping process, it is easy to make the cloth surface lose lint and fluff, and affect the wiping effect, a method for preparing a non-woven material for wiping cloth is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0027] Take 60g of kapok fiber, 30g of fine denier polyester filament, and 80g of poplar velvet fiber, wash them twice with deionized water, heat and dry with 200W microwave for 30min, and mix them by multi-layer tiling for batching. Opening in the loosening machine, combing through the carding machine and laying the web, the surface density of the fiber web is controlled to be 60g / m 2 , to obtain a single-layer moisture-absorbing fiber web, get 50g nylon fiber, 40g polyester staple fiber, carry out batching by multi-layer tiling and mixing, send the mixed batching into the opener to open, and lay the net after combing by a carding machine. Control the surface density of the fiber web to 50g / m 2 , to obtain a single-layer wear-resistant fiber web, spread the single-layer moisture-absorbing fiber web on the single-layer wear-resistant fiber net, and send it into the spunlace machine, after 1 pass of pre-wetting and 5 passes of front spunlace, set the speed of the mesh delivery ...

example 2

[0029] Take 70g of kapok fiber, 40g of fine denier polyester filament, and 90g of poplar velvet fiber, wash them twice with deionized water, heat and dry with 250W microwave for 35min, and mix them by multi-layer tiling for batching. Opening in the loosening machine, carding through the carding machine and laying the web, the surface density of the fiber web is controlled to be 70g / m 2 , to obtain a single-layer moisture-absorbing fiber web, get 55g nylon fiber, 45g polyester staple fiber, carry out batching by multi-layer tiling and mixing, send the mixed batching into the opener to open, and lay the net after combing by a carding machine, Control the surface density of the fiber web to 55g / m 2 , to obtain a single-layer wear-resistant fiber web, spread the single-layer moisture-absorbing fiber web on the single-layer wear-resistant fiber net, and send it into the spunlace machine, after 1 pass of pre-wetting and 5 passes of front spunlace, set the speed of the mesh delivery ...

example 3

[0031] Get 75g kapok fiber, 50g fine denier polyester filament, 100g poplar velvet fiber, wash 3 times with deionized water respectively, and heat and dry with 300W microwave for 40min, carry out batching by multi-layer tiling mixing, the batching after mixing is sent into open Opening in the loosening machine, carding through the carding machine and laying the web, the surface density of the fiber web is controlled to be 80g / m 2, to obtain a single-layer moisture-absorbing fiber web, get 60g nylon fiber, 50g polyester staple fiber, carry out batching by multi-layer tiling and mixing, send the mixed batching into the opener to open, and lay the net after combing by a carding machine. Control the surface density of the fiber web to 60g / m 2 , to obtain a single-layer wear-resistant fiber web, spread the single-layer moisture-absorbing fiber web on the single-layer wear-resistant fiber net, and send it into the spunlace machine, after 1 pass of pre-wetting and 5 passes of front s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a non-woven material used for wiping cloth, and belongs to the technical field of the wiping cloth. In the preparation method, by adopting fine polyester filament yarn which is fine in capillary, large in amount and capable of remarkably enhancing the capillary wicking effect of a fabric and then improving the air permeability and the wet permeability of the fabric, with the combination of the structural characteristics of kawo kawo fibers and poplar floccus fibers that the longitudinal sections are cylindrical, the surface is smooth, the fibersare soft and lustrous, the cross sections are circular or elliptic, the walls of the fibers are thin, and the fibers are hollow, preparation is conducted through multi-layer laying and mixing, carding and web forming are conducted after opening, and a single-layer fiber web is prepared, wherein the single-layer fiber web is high in degree of hollowness, small in fineness, obvious in wicking effect, short in moisture sorption equilibrium time and high in wet permeability, the fiber surface contains cerolipoid, so that the fiber web has wettability resistance, and the fluffy performance and theelastic recovery performance of the fibers are high; the single-layer fiber web is combined with a single-layer wear-resistant fiber web, and the single-layer fiber web and the single-layer wear-resistant fiber web are bonded through an ultrasonic composite technology after spunlaced finishing.

Description

technical field [0001] The invention relates to a preparation method of a nonwoven material for wiping cloth, which belongs to the technical field of wiping cloth. Background technique [0002] The wipes market has undergone a dramatic transformation in recent decades. Non-woven wipes are inexpensive, easy to carry, functional, and have a variety of product forms. They have gradually replaced traditional wipes. The market is mainly concentrated in the two directions of consumer wipes and industrial wipes. With the improvement of non-woven technology and the continuous enrichment of raw materials, non-woven wipes will continue to expand their application fields. [0003] Non-woven wipes can be divided into consumer wipes and industrial wipes according to their uses; according to processing methods, they can be divided into needle-punched wipes, spunlace wipes, chemically bonded wipes, thermally bonded wipes, and solvent-sprayed wipes. Wipes, spunbond wipes, etc.; accor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D04H1/492D04H1/72
CPCD04H1/4382D04H1/492D04H1/72D10B2201/01D10B2331/02D10B2331/04D10B2401/02D10B2401/062D10B2503/00
Inventor 史茜赟张桂芳朱华
Owner 史茜赟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com