Plugging injection mix for air leakage of furnace bottom foundation of hot-blast stove

A technology of press-feeding and hot blast furnace, which is applied in the field of refractory materials, can solve the problems of failure to meet the use requirements, slow curing at room temperature, large amount of liquid addition, etc., and achieve the effects of short construction time, long maintenance time and cost saving

Active Publication Date: 2018-11-02
中冶武汉冶金建筑研究院有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing press-in materials at home and abroad mainly include water glass bonded, phenolic resin bonded, etc. The above-mentioned pressed-in materials have their own shortcomings when used in this part, and they cannot meet the requirements for use.
For example, the water glass bonded press-in material has a large water content, a...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plugging injection mix for air leakage of furnace bottom foundation of hot-blast stove
  • Plugging injection mix for air leakage of furnace bottom foundation of hot-blast stove
  • Plugging injection mix for air leakage of furnace bottom foundation of hot-blast stove

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A plugging press-feed material used for air leakage at the bottom of a hot blast stove. The components and their mass percentages are: 48% of super-grade high-bauxite particles, 25% of super-grade high-bauxite powder, and active silica 2% of micropowder, 3% of active α-alumina micropowder, 0.2% of dispersant, 20% of furan resin, 1.8% of curing agent; its preparation method comprises the following steps: weighing super-grade high-alumina bauxite granules, super-grade high-alumina Bauxite powder, active silica micropowder, active aluminum oxide, and dispersant are weighed according to the proportion and added to a forced mixer to mix evenly. The resulting mixture is packed and transported in tons of bags; When used on site, put the mixture into a forced mixer, add furan resin and curing agent according to the proportion and stir for 5-8 minutes, and directly use the cement mortar pump to press into the leaking part to be sealed.

Embodiment 2

[0035] A plugging press-feed material used for air leakage at the bottom of a hot blast stove. The components and their mass percentages are: 42% of super-grade high-bauxite particles, 25% of super-grade high-bauxite powder, and active silica 2% micropowder, 3% active α-alumina micropowder, 0.2% dispersant, 25% furan resin, and 2.8% curing agent; Bauxite powder, active silica micropowder, active aluminum oxide, and dispersant are weighed according to the ratio and added to a forced mixer to mix evenly. The resulting mixture is packed and transported in tons of bags; When used on site, put the mixture into a forced mixer, add furan resin and curing agent according to the proportion and stir for 5-8 minutes, and directly use the cement mortar pump to press it into the leaking part to be sealed.

[0036] The performance test results of the plugging material obtained in Example 1 of the present invention are shown in Table 1, and the performance test results of Example 2 are equiv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a plugging injection mix for air leakage of a furnace bottom foundation of a hot-blast stove. The injecting mix comprises the following components by mass percentage: 40-50% ofa special grade high alumina bauxite granular material; 25-35% of special grade high alumina bauxite powder; 2-4% of active alpha-alumina micro powder; 2-4% of active silica micro powder; 0.05-0.5% of a dispersant; 19-25% of furan resin; and 1-3% of a curing agent. The injecting mix has the characteristics of easy mechanized construction, good fluidity, short construction time, strong bonding performance, curing at room temperature, high strength after curing, good volume stability and the like, can effectively improve the problems such as shrinkage cracking, great brittleness and the like existing in the existing online repair method, and has important industrialization and promotion values.

Description

technical field [0001] The invention belongs to the technical field of refractory materials, and in particular relates to a plugging press-feed material used for air leakage of the bottom foundation of a hot blast stove. Background technique [0002] After the hot blast stove attached to the blast furnace is put into use or used for a period of time, air leakage from the foundation of the hot blast stove often occurs, which not only causes the loss of power and heat energy, but also the leaked gas contains certain toxic components, which not only pollutes the environment but also damages the equipment. Maintenance personnel pose a safety hazard. In addition, the hot blast stove needs to be continuously produced after it is put into use, so it is difficult to rebuild the foundation of the hot blast stove, and the reconstruction cost is huge, so it needs to be repaired online. [0003] At present, the effective online repair method is to use the press-in material with the cha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/101
CPCC04B35/101C04B2235/3418C04B2235/447C04B2235/77C04B2235/96C04B2235/9615
Inventor 丛培源刘会永项冰
Owner 中冶武汉冶金建筑研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap