Cold state steel slag recycling steelmaking technology
A cold steel slag recycling technology, applied in the cold steel slag recycling steelmaking process, can solve the problems of underutilization of cold steel slag and high production cost of semi-steel steelmaking, so as to reduce the pressure on environmental protection and reduce the site Effect of area and optimized feeding method
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0041] Steel of U71 steel type is smelted on a 120-ton converter in a steel factory. The actual weight of semi-steel molten iron entering the furnace is 132t, the weight of scrap steel is 5t, and the weight of steel tapping is 128.8t. Finally, put semi-steel molten iron and scrap steel into the converter. After starting blowing, add cold steel slag into the converter, and then add lime, high-magnesia lime and acid composite slag into the converter in batches. The composition and temperature of semi-steel molten iron are as follows As shown in Table 1, the actual amount of auxiliary materials added and the amount of oxygen blowing are shown in Table 2, and the tapping composition and tapping temperature are shown in Table 3 below. The slag is active in the steelmaking process and has strong dephosphorization ability. The conventional slag splashing process is adopted to protect the furnace after tapping, and the furnace wall hangs slag well. The activity is 500 ppm.
[0042] T...
Embodiment 2
[0049] The steel of Q235-DG steel is smelted on a 120-ton converter in a steel factory. The actual weight of semi-steel molten iron in the furnace is 141t, the weight of scrap steel is 0t, and the weight of steel is 131.56t. After the furnace is finished, put half of the molten steel into it. After blowing starts, add two-thirds of the cold steel slag within 6 minutes after the blowing starts, and add the remaining one-third of the cold steel slag within the next 4 minutes. Lime, high-magnesium lime and acidic composite slagging agent are added to the converter in batches, the composition and temperature of semi-steel molten iron are shown in Table 4 below, and the amount of auxiliary materials and oxygen blown actually added are shown in Table 5 , the tapping composition and tapping temperature are shown in Table 6 below. The slag is active in the steelmaking process and has a strong dephosphorization ability. The conventional slag splashing process is adopted at the end of t...
Embodiment 3
[0057] The steel of Q195 steel type is smelted on a 120-ton converter in a steel factory. The actual weight of semi-steel molten steel in the furnace is 130t, the weight of scrap steel is 6t, and the weight of steel is 125.12t. The specific operation is at the end of the last furnace. Finally, put semi-steel molten steel and steel scrap into it. After blowing starts, add two-thirds of the cold steel slag within 6 minutes after blowing starts, and add the remaining one-third of cold steel slag within the next 4 minutes. After that, add two-thirds of the total amount of lime, high-magnesium lime and acidic composite slagging agent into the converter, and the remaining one-third of the lime, high-magnesium lime and acidic composite slagging agent will be smelted in batches After adding during the process, the composition and temperature of the semi-steel molten iron are shown in Table 7 below, the actual amount of auxiliary materials added and the amount of oxygen blowing are show...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap