Low-chlorine environment-friendly snow melt agent without salt dust and method for preparing low-chlorine environment-friendly snow melt agent

A snow-melting agent and environmental protection technology, applied in the field of snow-melting agent preparation, can solve the problems of easy formation of salt dust, high corrosion and destructiveness of snow-melting agent, secondary pollution of the environment, etc., to achieve the suppression of salt dust formation, good ice-melting effect, and low production cost low effect

Active Publication Date: 2018-11-13
金宝特兴(北京)科技开发有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a salt-dust-free, low-chlorine, environmentally friendly deicing agent and its preparation method to solve the technical problems in the prior art that the deicing agent is highly destructive in corrosion, easily forms salt dust, and causes secondary pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-chlorine environment-friendly snow melt agent without salt dust and method for preparing low-chlorine environment-friendly snow melt agent
  • Low-chlorine environment-friendly snow melt agent without salt dust and method for preparing low-chlorine environment-friendly snow melt agent
  • Low-chlorine environment-friendly snow melt agent without salt dust and method for preparing low-chlorine environment-friendly snow melt agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The technological process of preparation method of the present invention is as figure 1 As shown, specifically, the preparation method includes the following steps: 1). Preparation of anticoagulant: Take 1.56 grams of glycerol and 3 grams of boric acid, mix and heat to 160° C., maintain 160° C. for 1 hour, and keep stirring during the period. The stirring speed is 20 rpm. Take out the reactant, add 1.98 g of phosphoglyceride, 2 g of potassium formate, and 4 g of sodium acetate, mix and heat to 120° C., and keep it for 2 hours; keep stirring during the period, and the stirring speed is 25 rpm;

[0027] 2). Step 1) After the reaction is over, add 85 grams of sodium chloride, 0.5 grams of sodium hexametaphosphate as a slow-release antiscalant, stir evenly, extrude and granulate, and the extrusion pressure is 10 kg, and the finished product is produced. It is yellow-brown granular with a particle size of 0.3-0.6 cm.

Embodiment 2

[0029] This example is carried out on the basis of Example 1, the difference is that the amount of each reagent used is different, see Table 1 for the specific amount.

Embodiment 3

[0031] This example is carried out on the basis of Example 1, the difference is that the amount of each reagent used is different, see Table 1 for the specific amount.

[0032] Table 1. Amounts of reagents used in each example

[0033]

[0034]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-chlorine environment-friendly snow melt agent without salt dust and a method for preparing the low-chlorine environment-friendly snow melt agent. The low-chlorine environment-friendly snow melt agent and the method have the advantages that the low-chlorine environment-friendly snow melt agent is in the shape of yellowish-brown particles, the particle size of the low-chlorine environment-friendly snow melt agent is 0.3-0.6 cm, the chlorine content of the low-chlorine environment-friendly snow melt agent is lower than the chlorine content of common snow melt agentsby 15% or above, environmental hazards of the low-chlorine environment-friendly snow melt agent can be reduced by 30%-40%, the low-chlorine environment-friendly snow melt agent contains little chloride, and accordingly destruction and pollution on soil, plants and underground water resources due to the low-chlorine environment-friendly snow melt agent are far lower than destruction and pollution due to the common snow melt agents; earth surfaces are free of white salt spots after snow removal operation is carried out, salt dust formation can be effectively inhibited, and secondary pollution can be prevented.

Description

technical field [0001] The invention belongs to the technical field of snow-melting agent preparation, and in particular relates to a salt-dust-free, low-chlorine, environment-friendly snow-melting agent and a preparation method thereof. Background technique [0002] Snowfall and icing in winter often bring inconvenience to cities and transportation, and easily cause traffic accidents, especially on expressways, which are likely to be forced to close due to snow or icing, resulting in huge economic loss. At present, snow removal methods are mainly divided into mechanical snow removal and chemical snow removal. Among them, mechanical snow removal is flexible, fast, and has a wide range of applications, but there are deficiencies such as poor removal rate and easy damage to the road surface; the snow removal method of chemical deicing agent can make up for the shortage of mechanical snow removal, and is an effective means of melting snow and ice. Its use is irreplaceable. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/18
CPCC09K3/18
Inventor 李玉强魏大勇崔鹏
Owner 金宝特兴(北京)科技开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com