Machining method of die core surface of graphite die for glass hot bending

A technology of graphite molds and processing methods, applied in metal processing equipment, manufacturing tools, welding equipment, etc., can solve the problems of difficulty in ensuring the accuracy of the mold, difficulty in removing the machine, and inability to guarantee the accuracy, so as to avoid edge and surface collapse, The effect of improving the service life and improving the surface quality

Inactive Publication Date: 2018-11-23
LENS TECH CHANGSHA
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

First, the slight defects on the surface of the mold core after manual polishing will be enlarged and intuitively displayed on the hot-bent glass; due to the differences in the operator's personal techniques, it is difficult to guarantee the consistency of the polishing quality of the same type of mold; and the manual polishing process consumes The time is too long, and a single mold needs 2-3 hours to complete the polishing; and the corner position and dead corner of the graphite mold are more difficult to guarantee the quality
Second, it is difficult for graphite molds to remove defects after CNC by sandblasting; even if the defects can be removed by adjusting the sandblasting pressure, sand particle size, and sandblasting time, the surface of the mold core is prone to sagging and collapse. Therefore, the sandblasting process is generally not suitable for polishing graphite molds with curved surfaces.
Third, it is difficult to guarantee the precision of the graphite mold after drying, the sharp corners and rounded corners of the mold are easy to collapse, and the surface of the mold core is easy to oxidize after passing through the high temperature of the hot bending machine
[0005] The above-mentioned defects have always been the technical bottleneck that those skilled in the art need to break through. In order to overcome the problems of long time-consuming surface treatment of the existing graphite mold core, unstable surface quality of the mold core, and unguaranteed accuracy, a new glass hot-bending method is needed in this field. Surface processing method of mold core with graphite mold

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In the present invention, the core surface of the graphite mold can achieve a good polishing effect by adjusting the focal length of the laser, the irradiation lens, the energy ratio, the laser frequency, the number of irradiation passes, the laser step distance, and the irradiation method.

[0022] The focal length of the laser: the focal length of the infrared laser lens used in the present invention is generally 538 mm, and the mold core surface can be set within ± 2 mm of the focal length of the laser to achieve a good laser polishing effect.

[0023] Irradiation lens: Different lenses have different focal lengths, and different lenses have different concave and convex degrees. The energy emitted by the laser through the lens is also different, and the irradiation range (the range to which the laser light can move) is also different.

[0024] Energy ratio: After selecting a suitable type of infrared laser, the output energy ratio can be set. When the output energy ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a machining method of a die core surface of a graphite die for glass hot bending. The die core surface comprises a hook face structure, the machining method includes the step ofadopting a laser device to irradiate the die core surface of the graphite die so as to achieve the polishing effect on the dire core surface, the irradiation scope of the laser device is larger thanor equal to the projection scope of the die core surface on the horizontal face, the moving speed of irradiation burning of laser light on the die core surface is 200-20000 mm / s, all paths generated when the laser light moves on the die core surface each comprise a plurality of parallel straight lines, the number of times of irradiation burning of the laser light on the die core surface is two ormore, and the parallel straight lines of every two adjacent laser paths are crossed. By means of the machining method, the poor appearance generated after CNC of the graphite die can be removed, thedie accuracy is not influenced, the die polishing time is saved, the conditions such as edge collapse and face collapse on the die core surface are avoided, and the service life of the die is prolonged.

Description

technical field [0001] The invention relates to the field of graphite mold processing, in particular to a method for processing the core surface of a graphite mold for glass hot bending. Background technique [0002] In the processing of 3D touch screen glass for mobile phone panels, the hot bending process of glass can be regarded as the first process, and the quality of hot bending molds is directly related to the quality of glass products. Graphite is currently selected as the most suitable for hot bending of glass due to its characteristics. Material, graphite mold came into being. The core of the graphite mold refers to the part of the mold that is in direct contact with the glass. The surface of the core of the graphite mold contains a curved surface structure corresponding to the curvature of the target glass product for hot bending. [0003] Because during the hot bending process of the glass, all defects on the surface of the graphite mold core will be reflected on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K26/00B23K26/354B23K26/362
CPCB23K26/0006B23K26/354B23K26/361
Inventor 饶桥兵何崇跃
Owner LENS TECH CHANGSHA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products