Method for preparing water-permeable brick by using potassium feldspar tailings

A technology of permeable bricks and potassium feldspar, which is applied in the field of preparing permeable bricks from potassium feldspar tailings, which can solve the problems of high energy consumption and achieve the effects of less energy consumption, smooth surface and improved resource utilization

Inactive Publication Date: 2018-12-18
贺州市骏鑫矿产品有限责任公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent uses the firing method to process the potassium feldspar tailings to make permeable bricks. This method consumes a lot of energy. While solving the solid waste potassium feldspar tailings, it also creates new pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for preparing permeable bricks by utilizing potassium feldspar tailings, is characterized in that: comprises the following steps

[0022] S1: the bottom layer material includes the following parts by weight of raw materials: 50 parts of potassium feldspar tailings, 10 parts of lime, 3 parts of cement, 10 parts of adhesive, 3 parts of foaming agent and 20 parts of water; the surface layer material includes the following parts by weight of raw materials : 30 parts potassium feldspar tailings, 6-8 parts lime, 10 parts binder and 15 parts water;

[0023] S2: Crushing the bottom layer material and the surface layer material according to the weight ratio in step S1, respectively, put them into a mixer to stir and mix evenly, and put the evenly mixed surface layer material into the bottom of the mold for uniform distribution, and then pour the evenly mixed bottom layer material. Put into the mold for uniform distribution; vibrate and press for 3 minutes to obtain a mo...

Embodiment 2

[0031] A method of utilizing potassium feldspar tailings to prepare permeable bricks, comprising the steps of

[0032] S1: the bottom layer material includes the following parts by weight of raw materials: 55 parts of potassium feldspar tailings, 15 parts of lime, 4 parts of cement, 15 parts of adhesive, 4 parts of foaming agent and 25 parts of water; the surface material includes the following parts of raw materials by weight. : 35 parts potassium feldspar tailings, 7 parts lime, 12.5 parts binder and 17.5 parts water;

[0033]S2: Crushing the bottom layer material and the surface layer material according to the weight ratio in step S1, respectively, put them into a mixer to stir and mix evenly, and put the evenly mixed surface layer material into the bottom of the mold for uniform distribution, and then pour the evenly mixed bottom layer material. Put into the mold for uniform distribution; vibrate and press for 4 minutes to obtain a molded body, and the thickness ratio of t...

Embodiment 3

[0041] A method of utilizing potassium feldspar tailings to prepare permeable bricks, comprising the steps of

[0042] S1: the bottom layer material includes the following parts by weight of raw materials: 60 parts of potassium feldspar tailings, 20 parts of lime, 5 parts of cement, 20 parts of adhesive, 5 parts of foaming agent and 30 parts of water; the surface material includes the following parts by weight of raw materials : 40 parts potassium feldspar tailings, 8 parts lime, 15 parts binder and 20 parts water;

[0043] S2: Crushing the bottom layer material and the surface layer material according to the weight ratio in step S1, respectively, put them into a mixer to stir and mix evenly, and put the evenly mixed surface layer material into the bottom of the mold for uniform distribution, and then pour the evenly mixed bottom layer material. Put into the mold for uniform distribution; vibrate and press for 5 minutes to obtain a molded body, and the thickness ratio of the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a water-permeable brick by using potassium feldspar tailings, belonging to the technical field of building materials. The method comprises the followingsteps: S1, weighing the raw materials of a bottom-layer material and the raw materials of a surface-layer material, wherein the raw materials of the bottom-layer material are composed of, by weight, 50-60 parts of potassium feldspar tailings, 10-20 parts of lime, 3-5 parts of cement, 10-20 parts of an adhesive, 3-5 parts of a foaming agent and 20-30 parts of water, and the raw materials of the surface-layer material are composed of, by weight, 30-40 parts of potassium feldspar tailings, 6-8 parts of lime, 10-15 parts of an adhesive and 15-20 parts of water; S2, smashing the raw materials of the bottom-layer material and the surface-layer material according to the weight parts mentioned in the step S1, separately placing the smashed materials in a mixer, carrying out uniform mixing under stirring, and then carrying out shaking and compaction molding for 3 to 5 min so as to obtain a molded green body; and S3, maintenance: subjecting the obtained molded green body to maintenance under natural conditions for 5 to 10 days so as to obtain the finished water-permeable brick. The water-permeable brick prepared in the invention has the advantages of good water permeability, high strength, low cost, beautiful appearance, etc.; and the method of the invention can achieve zero emission and zero pollution in the production process, and has good economic and social benefits.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a method for preparing permeable bricks by utilizing potassium feldspar tailings. Background technique [0002] In the long-term urbanization development process in my country, large-scale impervious ground (concrete, cement ground) replaced the original forests, green spaces and fields, resulting in a great increase in the impervious area, making urban rainwater unable to enter the soil smoothly, resulting in groundwater replenishment The conservation is greatly reduced, and the peak flow is greatly increased. In many cities, in the event of a heavy rain, the rainwater on the road surface cannot leak quickly. When the drainage facilities are not smooth, it is easy to cause urban waterlogging. At the same time, the hardening of the ground weakens the breathing function of the urban environment, resulting in aggravated heat island effect, dust and noise, worsening the u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/10C04B38/10C04B18/12
CPCC04B28/10C04B2111/00284C04B2111/00612C04B18/12C04B7/00C04B24/281C04B24/42C04B24/02C04B2103/42C04B38/10C04B2103/54Y02W30/91
Inventor 邓培有
Owner 贺州市骏鑫矿产品有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products