A pasting film for improving the surface wrinkle of a soft-pack lithium ion battery and a film pasting method

A soft-pack lithium battery and soft-pack battery technology, which is applied in the manufacture of secondary batteries, non-aqueous electrolyte batteries, and electrolyte batteries, can solve problems such as battery wrinkles, high defective ratios, and structural deformation, and reduce accuracy and difficulty. The effect of reducing the use area and reducing the contact area

Active Publication Date: 2018-12-18
余姚市海泰贸易有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, in the process of using the commonly used PET film in the industry, there is a slight "wrinkle" or serious "hook" on the surface of the battery that causes structural deformation of the pouch battery during the final inspection, resulting in a large number of defective products and scrapped products.
Especially in the production of pouch batteries with large area and size, the defective ratio is even higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A pasting film for improving the surface wrinkle of a soft-pack lithium ion battery and a film pasting method
  • A pasting film for improving the surface wrinkle of a soft-pack lithium ion battery and a film pasting method
  • A pasting film for improving the surface wrinkle of a soft-pack lithium ion battery and a film pasting method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Take the 11216266-60Ah soft pack structure lithium battery as an example, such as figure 2 As shown, the customized width of the PET film is 206≤W1≤211mm, and the length of the automatic cutting is 246≤H1≤261mm. The PET film has been perforated with a pore diameter of 0.1mm, which meets the 140-mesh hole number standard, such as image 3 As shown, the pouch battery width W2 = 216mm, height H2 = 266mm, such as figure 1 As shown, the battery is processed through batching, coating, preparation of bare cells, encapsulation once, and then film application. The front and back sides of the centered cell are respectively filmed, leaving the 12 positions of the airbag belt completely. Put the film-attached cells into an oven for vacuum-90Kpa, 85°C process standard baking for 24 hours, then liquid injection, chemical formation, high-temperature storage at 45°C, storage time for 12 hours and other standardized treatments. After re-degassing, secondary molding, encapsulation, and...

Embodiment 2

[0025] Refer to Example 1 for the specific process. The difference from Example 1 is that the PET film is perforated, with a pore diameter of 0.3 mm, which meets the 50-mesh hole number standard. Record the batch appearance wrinkle failure rate, which is recorded as Example 2.

Embodiment 3

[0027] Refer to Example 1 for the specific process. The difference from Example 1 is that the PET film has been perforated with a pore diameter of 0.5 mm, which meets the 35-mesh hole number standard. Record the batch appearance wrinkle defect rate, and record it as Example 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pasting film for improving the surface wrinkle of a soft-pack lithium battery and a film pasting method, wherein the pasting film is a PET film with a plurality of small holes, the pore diameter of the PET film is 0.1-0.5 mm, the number of holes is 35-140 mesh, and the thickness of the PET film is 0.3-0.6 mm; The film pasting method comprises the following steps: after the soft-pack battery is encapsulated once, the perforated PET films are respectively centered and pasted on the front and back main bodies of the soft-pack battery after the first encapsulation, and the positions of the airbag strips are left. The invention punches the common PET film, The contact area between the PET film and the main aluminum-plastic film is reduced, and the problem that the heatshrinkage of the PET film and the heat shrinkage of the aluminum-plastic film are inconsistent in the high-temperature baking after the film pasting process is improved, and the thermal stress causedby the baking after the release process leads to the deformation of the aluminum-plastic film, thereby solving the problem of the wrinkle of the aluminum-plastic film.

Description

technical field [0001] The invention relates to the technical field of film sticking for soft-pack lithium-ion batteries, in particular to a film sticking method for improving surface wrinkles of soft-pack lithium-ion batteries and a film sticking method. Background technique [0002] Soft-pack batteries are one of the mainstream systems alongside battery structures such as cylinders, aluminum cases, and plastic cases, and are in great demand. Widely used in digital 3C products, and power and energy storage markets. The soft pack lithium battery is composed of positive and negative electrode materials, a separator, an electrolyte, and an aluminum-plastic film (nylon-aluminum layer-polypropylene) coated on the outermost layer. The use of aluminum-plastic film packaging for soft pack batteries has many advantages such as light weight, high battery energy density, changeable shape, easy size adjustment, and excellent cycle. However, the nylon layer on the outermost layer of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/058H01M10/0525
CPCH01M10/0525H01M10/058Y02E60/10Y02P70/50
Inventor 黄志勇余开明娄忠良陈建鹏崔俊葳徐伟
Owner 余姚市海泰贸易有限公司