Preparation method of propellant slurry without precipitated bonding agent

A technology of bonding agent and slurry, applied in explosives and other directions, can solve problems such as hidden quality problems and surface spots on the powder column, and achieve the effect of good premixing effect, uniform uniformity and strong operability

Active Publication Date: 2018-12-21
XIAN AEROSPACE CHEM PROPULTION PLANT
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In order to overcome the problems of spots on the surface of the drug column and hidden quality problems existing in the prior art, the present invention proposes a method for preparing drug slurry without bonding agent precipitation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of propellant slurry without precipitated bonding agent
  • Preparation method of propellant slurry without precipitated bonding agent
  • Preparation method of propellant slurry without precipitated bonding agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] This embodiment is a preparation method of a slurry without binding agent precipitation.

[0039] The components of the present embodiment syrup are: 0.1% diethanolamine melamine complex, 10% octyl ferrocene, 5% N-N' diphenyl-p-phenylenediamine, 10% industrial quindiol Diisooctyl acid, 19.9% ​​spherical aluminum powder and 55% hydroxyl-terminated polybutadiene. The stated percentages are mass percentages.

[0040] The concrete process of this embodiment is:

[0041] Step 1, pre-baking.

[0042] Put the colloidal diethanolamine-melamine complex and viscous hydroxyl-terminated polybutadiene in a drying room at 50°C±10°C and heat for 12 to 24 hours to reduce the diethanolamine-melamine complex and terminal polybutadiene. The viscosity of hydroxypolybutadiene.

[0043] Step 2, mixing ingredients.

[0044] The pre-dried diethanolamine melamine complex and the hydroxyl-terminated polybutadiene are premixed into a premixed slurry. The mixture is mixed three times, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of propellant slurry without a precipitated bonding agent. The method comprises the steps of pre-baking hydroxyl-terminated polybutadiene and a diethanolamine melamine complex for 12h or more at 50+ / -10 DEG C so as to reduce the viscosity of the hydroxyl-terminated polybutadiene and the diethanolamine melamine complex; gradually mixing the hydroxyl-terminated polybutadiene with a viscous material by premixing in a small amount for a plurality of times so as to gradually achieve the purpose of evenly pre-mixing the materials; pouring the premixed slurry of the hydroxyl-terminated polybutadiene and the diethanolamine melamine complex into a premix container of the other raw materials for premixing, and fully and evenly mixing. The method guarantees the uniformity of the premixed propellant slurry in the weighing process by utilizing the existing hardware facilities of the process and by means of analysis, explosion and process improvement inthe aspects such as raw material preparation, a premixing process of the propellant slurry and the physical and chemical properties of the raw materials; the method has strong operability; furthermore, the uniformity of the premixed propellant slurry is basically the same, so that the quality of the propellant slurry is improved.

Description

technical field [0001] The invention relates to the field of solid rocket motors, in particular to a method for preparing a slurry without bonding agent precipitation. Background technique [0002] During the production process of a certain type of solid rocket motor, black and brown spots appeared on the drug surface many times, and a small amount of diethanolamine-melamine complex adhered to the material container after cleaning at the mixing station, and the diethanolamine-melamine complex was difficult to completely Problems such as uniform premixing have seriously affected the product quality and production progress of the powder column. [0003] The existing technology is: according to the process requirements, all the bonding agent diethanolamine melamine complexes with a viscosity greater than 20pa.s are added to the hydroxyl-terminated polybutadiene during premixing, and then other components are added, and then premixed by manual stirring , because the diethanolam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C06B27/00
CPCC06B27/00
Inventor 张博沈明韩晓娟张武卫曹巍
Owner XIAN AEROSPACE CHEM PROPULTION PLANT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products