A preparation method of reversible wrinkle microstructure on the surface of an all-optical controlled azobenzene film

A technology of azobenzene and microstructure, applied in the field of preparation of smart surfaces, achieves the effect of easy operation

Inactive Publication Date: 2021-04-20
TIANJIN UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports on the intelligent regulation of reversible wrinkle microstructure using light as an external stimulus.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of reversible wrinkle microstructure on the surface of an all-optical controlled azobenzene film
  • A preparation method of reversible wrinkle microstructure on the surface of an all-optical controlled azobenzene film
  • A preparation method of reversible wrinkle microstructure on the surface of an all-optical controlled azobenzene film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for preparing a reversible wrinkle microstructure on the surface of an all-optical control azobenzene film, comprising the following steps:

[0026] Step 1, mix the PDMS prepolymer and crosslinking agent Sylgard 184 (purchased from Dow Corning, USA) at a mass ratio of 10:1, and fully stir with a glass rod to form a uniform prepolymer; put the above prepolymer in circulating water After degassing in a multi-purpose vacuum pump for 1 hour, pour it into a watch glass; heat it at 70°C for 4 hours to cure; obtain a PDMS soft substrate;

[0027] Step 2. The PDMS soft substrate obtained in step 1 is subjected to oxygen plasma surface activation treatment, and then spin-coated with 2wt% PDO 3 THF solution (spin-coating parameters: 3000rpm, 40s), degassed in a vacuum pump to remove residual organic solvents, to obtain PDMS / PDO 3 Soft and hard composite system.

[0028] Step 3, the PDMS / PDO obtained in step 2 3 Composite system at 2.46W / cm 2 450nm laser irradiation f...

Embodiment 2

[0032] A method for preparing a reversible wrinkle microstructure on the surface of an all-optical control azobenzene film, the preparation process of which is basically the same as in Example 1, the difference being that the 2.46W / cm 2 450nm laser irradiation 5s changed to 410mW / cm -2 Irradiated under white light for 60s, a maze-like surface wrinkle pattern is obtained, such as Figure 5 As shown in the light microscope diagram; 45mW / cm in step 4 2 450nm laser irradiation 10s changed to 15mW / cm -2 Irradiate under white light for 120s to regain a smooth azobenzene film, such as Image 6 shown in the light microscope diagram. In step 5, the number of repeated wrinkling / wrinkling is changed from 20 times to 10 times, and the surface wrinkle pattern obtained in step 3 for the 10th time is as follows Figure 7 As shown in the light microscope image, the wrinkle-free pattern on the surface obtained in step 4 for the 10th time is as follows Figure 8 shown in the light microsco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an all-optical control reversible surface wrinkle microstructure. The steps are: after mixing a PDMS prepolymer and a crosslinking agent at a mass ratio of 10:1, fully stirring to form a uniform prepolymer, and The above prepolymer was poured into a watch glass after being degassed in a vacuum pump, and heated at 70°C for 4 hours for thermal crosslinking and curing to obtain a PDMS elastomer; the PDMS elastomer was subjected to oxygen plasma surface activation treatment, and then spin-coated with a mass fraction of 2wt %PDO 3 Tetrahydrofuran solution, degassed in a vacuum pump to remove residual organic solvents, to obtain PDMS / PDO 3 Soft and hard composite system; then irradiate with high-intensity visible light to obtain a wrinkled azobenzene film on the surface; then irradiate with low-intensity visible light to gradually disappear wrinkles to obtain an azobenzene film with smooth surface; 20 crease / decrease cycles. The method of the invention is clean and efficient, and avoids the use of expensive instruments and cumbersome and complicated operation steps.

Description

technical field [0001] The invention relates to the preparation and research of an intelligent surface, in particular to a preparation method for a reversible wrinkle microstructure on the surface of an all-optical control azobenzene film. Background technique [0002] Surface wrinkling, as a spontaneous process of forming surface microstructures to adapt to changes in the system's stress field, has attracted particularly intense research interest from researchers in recent years. The appearance of wrinkling is considered to be a manifestation of stress instability. Making full use of the new enlightenment brought by the film wrinkling mechanism to actively promote the wrinkling of the material surface, and to seek its potential applications in the characterization of material properties, micro-nano structure construction and flexible devices, is one of the current research focuses on surface wrinkling. one. Among them, actively exploring the application of environmental s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/12C08J7/00C08L83/04
CPCC08J7/00C08J7/12C08J7/123C08J2383/04
Inventor 鲁从华汪娟娟
Owner TIANJIN UNIV