Waterborne epoxy resin emulsifier and preparation and use method thereof

A water-based epoxy resin and epoxy resin technology, applied in the field of emulsification additive production, can solve the problems of increased production cost, complicated use methods, and increased emulsification operation cost, and achieve the effects of energy saving, high efficiency, stable use and environmental protection

Pending Publication Date: 2019-01-15
沈阳东岩涂料装饰有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the complexity of the composition and usage of the existing emulsifiers, the cost of emulsifying epoxy resin is very high, resulting in an increase in production costs
At the same time, due to the unreasonable composition of the emulsifier and the unreasonable production method, the cost of the emulsifier has also increased, thereby indirectly increasing the cost of the emulsification operation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A kind of preparation method of water-based epoxy resin emulsifier, polyethylene glycol 6000, polyethylene glycol incense 4000, polysorbate-80, trimethylol propane glycidyl ether, 828 epoxy resin are put into reactor, Add boron trifluoride etherate complex dropwise, measure water solubility and epoxy value after standing still, then dilute with heated water, and finally filter.

[0026] The temperature in the reaction kettle is 90-110°C,

[0027] The dropping time of the boron trifluoride etherate complex is 2h,

[0028] The standing temperature is 90-120°C,

[0029] The time of standing still is 2h.

[0030] A method for using a water-based epoxy resin emulsifier, including adding a water-based epoxy resin emulsifier formula, an industrial production method, a laboratory experiment method,

[0031] The ingredients in the water-based epoxy resin emulsifier formula are liquid epoxy resin 828, water-based epoxy resin emulsifier DY-56, water-based bactericide, water-bas...

Embodiment 1

[0040] Put polyethylene glycol 6000, polysorbate-80, trimethylolpropane glycidyl ether, and 828 epoxy resin into the reaction kettle, raise the temperature to 90-110°C, and add boron trifluoride diethyl ether dropwise over 2 hours. Compound, keep warm at 90-120 degrees for 2 hours, measure water solubility and epoxy value, heat water to dilute after passing the test, and finally filter for later use.

Embodiment 2

[0042] During production, first put 20kg of water, 10kg of water-based epoxy resin emulsifier DY-56, and 0.25kg of water-based epoxy defoamer 154 into the dispersion tank, stir at 450r / min, and then put 50kg of liquid ring Add oxygen resin 828, stir at 1100r / min for 50min, finally add 18.45kg of water, 0.1kg of water-based bactericide, and 1.2kg of wetting agent DY-15, and stir for 15min at 800r / min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a waterborne epoxy resin emulsifier, which comprises: polyethylene glycol 6000, polysorbate-80, trimethylolpropane glycidyl ether, 828 epoxy resin and a boron trifluoride etherate complex. The invention has the beneficial effects that: the production is energy-saving and efficient, use of the emulsifier is stable and environment-friendly, traditional process equipment canachieve production, and refitting investment of equipment is unnecessary.

Description

technical field [0001] The invention relates to the production field of emulsifying additives, in particular to a water-based epoxy resin emulsifier and its preparation method and use method. Background technique [0002] Water-based epoxy emulsifiers are mainly used for emulsifying epoxy resins. They are mainly composed of epoxy-terminated polyetherketone double-word surfactants, which can quickly emulsify epoxy resins at medium or high temperatures. Due to the complicated composition and usage methods of the existing emulsifiers, the emulsification operation cost of epoxy resin is very high, resulting in the increase of production cost. At the same time, due to the composition of the emulsifier and the unreasonable production method, the cost of the emulsifier is also increased, thereby indirectly increasing the cost of the emulsification operation. Contents of the invention [0003] The purpose of the present invention is in order to solve the problems referred to abov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J3/03C08L63/00
CPCC08J3/03C08J2363/00C08L63/00C08L2201/54
Inventor 孟滨孟军
Owner 沈阳东岩涂料装饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com