A kind of permanent antistatic acrylonitrile-based copolymer and its fiber preparation method

An acrylonitrile-based copolymer fiber, acrylonitrile-based technology, used in the manufacture of conductive/antistatic filaments, fiber chemical characteristics, single-component synthetic polymer rayon, etc. The problem of electrostatic agent migration and precipitation can reduce the surface resistivity and improve the antistatic performance.

Active Publication Date: 2021-01-26
TIANJIN POLYTECHNIC UNIV
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although ionic liquids have excellent electrical conductivity, there are two main problems in using ionic liquids as a single antistatic agent for the production and development of antistatic products: on the one hand, as an ionic antistatic agent, ionic liquids are affected by environmental temperature and humidity. More serious; on the other hand, most ionic liquids with excellent performance are expensive, and the large addition ratio leads to high production costs
However, this patent only blends polyethylene glycol and polyacrylonitrile, which also has the problem of antistatic agent migration and precipitation, and cannot achieve permanent antistatic performance.
The use of polyethylene glycol as an antistatic agent mainly has the following problems: when the added amount is low, the antistatic performance is poor; when the added amount is too high, the water absorption effect is strong, resulting in too high surface viscosity of the material, which affects subsequent processing and use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of permanent antistatic acrylonitrile-based copolymer and its fiber preparation method
  • A kind of permanent antistatic acrylonitrile-based copolymer and its fiber preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Preparation of permanent antistatic acrylonitrile-based copolymer

[0030] Pour 1 L of dimethylformamide into the reaction kettle, then add 3.75 mol of acrylonitrile monomer, 0.3 mol of methyl acrylate, 0.45 mol of polyethylene glycol methacrylate 400, 0.5 mol of 1-allyl-3 -Butylimidazolium hexafluorophosphate and 0.1mol azobisisobutyronitrile were mixed evenly and then poured into the reaction kettle, heated to 65°C while stirring, reacted for 10 hours after the temperature was constant, and then poured the reaction solution into 5L distilled water Precipitation, standing still, suction filtration, and vacuum drying at 85°C to obtain an acrylonitrile-based copolymer with a melting point of 215°C;

[0031] (2) Preparation of permanent antistatic acrylonitrile-based copolymer fibers

[0032] After mixing 100 parts by mass of acrylonitrile-based copolymers, 0.2 parts by mass of dilauryl thiodipropionate, 0.3 parts by mass of zinc stearate, and 1 part by mass of cellu...

Embodiment 2

[0034] (1) Preparation of permanent antistatic acrylonitrile-based copolymer

[0035] Pour 0.5L dimethylformamide and 0.5L dimethyl sulfoxide into the reaction kettle, then add 3.5mol acrylonitrile monomer, 0.5mol methyl acrylate, 0.5mol polyethylene glycol monomethyl ether methacrylate 400, 0.5mol of 1-allyl-3-butylimidazolium chloride salt and 0.1mol of azobisisobutyronitrile were mixed evenly and then poured into the reaction kettle, heated to 60°C while stirring, and reacted for 10 hours after the temperature was constant , then pour the reaction solution into 7L distilled water for precipitation, let stand, filter with suction, and dry in vacuum at 80°C to obtain an acrylonitrile-based copolymer with a melting point of 188°C;

[0036] (2) Preparation of permanent antistatic acrylonitrile-based copolymer fibers

[0037] 100 parts by mass of acrylonitrile-based copolymers, 0.2 parts by mass of spiroethylene glycol bis[2,2'-methylenebis(4,6-di-tert-butylphenyl)] phosphite, ...

Embodiment 3

[0039] (1) Preparation of permanent antistatic acrylonitrile-based copolymer

[0040] Pour 1L of dimethylformamide into the reaction kettle, and then add 3.75mol of acrylonitrile monomer, 0.5mol of methyl acrylate, 0.25mol of polyethylene glycol acrylate 400, and 0.5mol of 1-allyl-3-butane Mix imidazole tetrafluoroborate and 0.1mol azobisisobutyronitrile evenly and pour it into the reaction kettle, heat up to 65°C while stirring, react for 10 hours after the temperature is constant, then pour the reaction solution into 5L distilled water for precipitation , stand still, filter with suction, and dry under vacuum at 85°C to obtain an acrylonitrile-based copolymer with a melting point of 202°C;

[0041] (2) Preparation of permanent antistatic acrylonitrile-based copolymer fibers

[0042] 100 parts by mass of acrylonitrile-based copolymers, 0.1 parts by mass of spiroethylene glycol bis[2,2'-methylenebis(4,6-di-tert-butylphenyl)] phosphite, 0.2 parts by mass Zinc stearate, 1.2 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a permanent antistatic acrylonitrile-based copolymer and a fiber preparation method thereof. The preparation principle of permanent antistatic acrylonitrile-based copolymer fibers is as follows: firstly, acrylonitrile is used to copolymerize monomers such as ionic liquids containing unsaturated double bonds and polyethylene glycol derivatives containing unsaturated double bonds to obtain permanent antistatic propylene fibers. The nitrile-based copolymer is subsequently processed directly by spinning to produce permanently antistatic acrylonitrile-based copolymer fibers. Since the antistatic agent used participates in the polymerization reaction, the problem of migration and precipitation of small molecules is solved, so the obtained acrylonitrile-based copolymer fiber has permanent antistatic performance.

Description

technical field [0001] The invention relates to the technical field of fiber preparation, in particular to a permanent antistatic acrylonitrile-based copolymer and a fiber preparation method thereof. Background technique [0002] The electrical properties of polymer materials mainly depend on two physical quantities, namely resistivity and dielectric constant. The lower the resistivity of the material, the stronger the ability to dissipate static electricity. The lower the dielectric constant, the easier it is to generate static electricity. However, most polymer materials have high surface resistivity (>10 12 Ω) and low dielectric constant, therefore, this type of material does not have antistatic properties, resulting in various problems and difficulties due to the accumulation of static electricity in practical applications. Random failures, malfunctions or operating errors may also cause breakdown and destruction of certain components (MOS circuits, bipolar circuits,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/54D01F1/09C08F283/06C08F220/14C08F220/44C08F230/06C08F226/04C08F226/06C08F220/06
CPCC08F283/065D01F1/09D01F6/54C08F230/06
Inventor 王宁李恒韩姗高亚雪陈洋周逢宇
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com