CPVC composition for granulation-free injection molding
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of CPVC resin and composition, which is applied in the processing field of thermoplastics to achieve the effect of high smoothness and good physical properties
Active Publication Date: 2019-02-26
上海泉恩塑胶有限公司
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In order to solve the problem in the prior art that the CPVC composition needs to be granulated and preplasticized before injection molding, the purpose of the present invention is to provide a CPVC composition for granulation-free injection molding
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0031] Take 1000 g chlorine content as 66% CPVC resin, 40 g methyl mercaptan organotin stabilizer, 5 g AC-617A, 10 g AC-316A, 50 g impact modifier MBS TH-21, 30 g processing aid K-120P , 10g of antioxidant 1076, 20g of titanium dioxide, put into a high-speed mixer, heat up to 120°C, disperse evenly, discharge into a low-speed mixer and cool to 40°C, then discharge, and inject the obtained material to obtain a product.
Embodiment 2
[0033] Take 1000 g chlorine content as 65% CPVC resin, 50 g butylmercaptan organotin stabilizer, 15 g AC-617A, 5 g AC-316A, 60 g impact modifier MBS TH-21, 50 g processing aid K-120P , 10g of antioxidant 1076, 30g of titanium dioxide, put into a high-speed mixer, heat up to 120°C, disperse evenly, discharge into a low-speed mixer and cool to 40°C, then discharge, and inject the obtained material to obtain a product.
Embodiment 3
[0035] Take 1000 g chlorine content as CPVC resin with 68%, 60 g octyl mercaptan organotin stabilizer, 10 g AC-617A, 15 g AC-316A, 100 g impact modifier MBS TH-21, 60 g processing aid K-120P , 15g of antioxidant 1076, 50g of titanium dioxide, put into a high-speed mixer, heat up to 120°C, disperse evenly, discharge into a low-speed mixer and cool to 40°C, then discharge, and inject the obtained material to obtain a product.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
density
aaaaa
aaaaa
density
aaaaa
aaaaa
Vicat softening point
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a CPVC composition for granulation-free injection molding. The CPVC composition comprises the following components by weight: 100 parts of CPVC resin, 4-6 parts of a stabilizer, 0.5-1.5 parts of low-density non-oxidized polyethylene wax, 0.5-1.5 parts of high-density oxidized polyethylene wax, 5-10 parts of an impact modifier, 3-6 parts of a processing aid, 1-1.5 parts of an antioxidant and 2-5 parts of a filler. The CPVC composition for granulation-free injection molding in the invention does not need to undergo a granulation procedure and can be directly applied to injection molding to prepare a product with good physical properties and high smoothness.
Description
technical field [0001] The invention relates to the technical field of processing thermoplastics, in particular to a CPVC composition for granulation-free injection molding. Background technique [0002] Chlorinated polyvinyl chloride (CPVC) is a chlorinated product of polyvinyl chloride. It has better physical and chemical properties than polyvinyl chloride. The chlorine content of ordinary polyvinyl chloride (PVC) molecules is about 58%. Chlorinated polyvinyl chloride (CPVC) The chlorine content of the vinyl chloride molecule is 64-68%. The increased chlorine content improves the combustion-supporting and smoke-producing properties of PVC, increases the tensile strength and modulus, and retains its original good properties: outstanding dimensional stability, excellent chemical resistance and weather resistance , and good dielectric properties. However, CPVC melt has the problem of high viscosity and is easy to decompose, which greatly increases the processing difficulty ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.