Zinc-rich resin anticorrosion paint

A technology of anti-corrosion paint and resin, applied in anti-corrosion paint, coating and other directions, to achieve the effect of good waterproof and thermal insulation effect

Inactive Publication Date: 2019-03-05
陆文兰
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional products are gradually improved and new products are continuously developed and released. To adapt to the new standards and requir

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1

[0017] A zinc-rich resin anticorrosion paint, comprising the following raw materials in parts by weight: 10 parts of alkyl silicate, 25 parts of alkali silicate, 10 parts of zinc oxide, 2 parts of titanium dioxide and 1 part of zinc phosphate.

[0018] The raw materials also include 5 parts by weight of modified silicon dioxide, 2 parts of kaolin, and 5 parts of vitreous silicon dioxide.

Example Embodiment

[0019] Example 2

[0020] A zinc-rich resin anticorrosion coating, comprising the following raw materials in parts by weight: 40 parts of alkyl silicate, 55 parts of alkali silicate, 20 parts of zinc oxide, 3 parts of titanium dioxide and 3 parts of zinc phosphate.

[0021] The raw materials also include 10 parts by weight of modified silicon dioxide, 3 parts of kaolin, and 10 parts of vitreous silicon dioxide.

Example Embodiment

[0022] Example 3

[0023] A zinc-rich resin anticorrosion coating, comprising the following raw materials in parts by weight: 15 parts of alkyl silicate, 30 parts of alkali silicate, 12 parts of zinc oxide, 2.2 parts of titanium dioxide and 1.5 parts of zinc phosphate.

[0024] The raw materials also include 6 parts by weight of modified silicon dioxide, 2.5 parts of kaolin, and 7 parts of vitreous silicon dioxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses zinc-rich resin anticorrosion paint which belongs to the technical field of paint. The paint includes, by weight, the following raw materials: 10-40 parts of alkyl ester silicate, 25-55 parts of alkaline silicate, 10-20 parts of zinc oxide, 2-3 parts of titanium dioxide, and 1-3 parts of zinc phosphate. The zinc-rich resin anticorrosion paint utilizes the alkyl ester silicate as a film-forming material and utilizes a vitreous silica material, a special ceramic material, the zinc phosphate, and a fiber material as fillers to prepare heat preservation antisepsis anticorrosion paint; novel water proofing heat preservation paint is prepared from raw materials such as an elastic emulsion, hollow glass microbeads, kieselguhr, infrared reflection agents, and asbestos wool;and the paint is only applied by 2 mm thickness to achieve a good water proofing thermal insulation effect.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a zinc-rich resin anticorrosion coating. Background technique [0002] Anti-corrosion coatings, generally divided into conventional anti-corrosion coatings and heavy-duty anti-corrosion coatings, are an indispensable coating in paint coatings. Conventional anti-corrosion coatings play an anti-corrosion effect on metals under normal conditions and protect the service life of non-ferrous metals; A type of anti-corrosion coating that achieves a longer protection period than conventional anti-corrosion coatings. [0003] Nowadays, anti-corrosion coatings have become an important new force in the field of coatings. Anti-corrosion coatings are playing an increasingly important role, and their development prospects are promising. However, traditional products are gradually improved and new products are continuously developed and released. To adapt to the new standards and requirement...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D1/00C09D5/08C09D7/61C09D7/62
CPCC09D1/00C09D5/08
Inventor 陆文兰
Owner 陆文兰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap