A chair leg and bending technology, applied in the field of wooden chair leg bending, can solve the problems of low mechanical and mechanical strength, poor bending effect, increase production cost of enterprises, etc., and achieve scientific and reasonable operation steps, increased toughness and strength, and improved The effect of the bend effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0051] Embodiment 1 A kind of wooden chair chair leg bending method
[0052] A method for bending a wooden chair leg, comprising the following steps:
[0053] 1), chair leg pretreatment:
[0054] A. Anti-corrosion treatment:
[0055] Soak the chair legs in the antiseptic solution for 22 hours to ensure that all the chair legs are soaked in the antiseptic solution. After the treatment, place the chair legs in an oven at 105 degrees Celsius to dry; wherein, the antiseptic solution consists of the following parts by weight: Components: 30 parts of water-based epoxy resin emulsion, 4 parts of ammonium persulfate, 7 parts of chain extender HER, 15 parts of diacetone alcohol, 17 parts of nano-silica, 31 parts of deionized water;
[0056] B. Toughening treatment: soak the chair legs treated in step A in the soaking solution for toughening treatment for 10-14 hours to ensure that all the chair legs are soaked in the soaking solution. After the treatment, place the chair legs in an o...
Embodiment 2
[0063] Embodiment 2 A kind of wooden chair chair leg bending method
[0064] A method for bending a wooden chair leg, comprising the following steps:
[0065] 1), chair leg pretreatment:
[0066] A. Anti-corrosion treatment:
[0067] Soak the chair legs in the antiseptic solution for 20 hours to ensure that the chair legs are all soaked in the antiseptic solution. After the treatment, place the chair legs in an oven at 105 degrees Celsius to dry; wherein, the antiseptic solution consists of the following parts by weight: Components: 25 parts of water-based epoxy resin emulsion, 3 parts of ammonium persulfate, 6 parts of chain extender HER, 12 parts of diacetone alcohol, 14 parts of nano-silica, 30 parts of deionized water;
[0068] B. Toughening treatment: Soak the chair legs treated in step A in the soaking solution for toughening treatment for 10 hours to ensure that all the chair legs are soaked in the soaking solution. After the treatment, place the chair legs in an oven...
Embodiment 3
[0075] Embodiment 3 A kind of wooden chair chair leg bending method
[0076] A method for bending a wooden chair leg, comprising the following steps:
[0077] 1), chair leg pretreatment:
[0078] A. Anti-corrosion treatment:
[0079] Soak the chair legs in the antiseptic solution for 24 hours to ensure that all the chair legs are soaked in the antiseptic solution. After the treatment, place the chair legs in an oven at 105 degrees Celsius to dry; wherein, the antiseptic solution consists of the following parts by weight: Components: 35 parts of water-based epoxy resin emulsion, 5 parts of ammonium persulfate, 8 parts of chain extender HER, 18 parts of diacetone alcohol, 20 parts of nano-silica, 32 parts of deionized water;
[0080] B. Toughening treatment: Soak the chair legs treated in step A in the soaking solution for toughening treatment for 14 hours to ensure that all the chair legs are soaked in the soaking solution. After the treatment, place the chair legs in an oven...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com