Grinding aid specially used for phosphogypsum cement, and preparation method of grinding aid

The technology of grinding aid and phosphogypsum is applied in the field of cement admixtures, which can solve the problems of delayed setting time of cement and reduced cement strength, and achieve the effects of improving the speed of hydration reaction, improving the later strength and reducing the impact.

Active Publication Date: 2019-03-12
SHANDONG HONGYI TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the problems that the setting time of cement is delayed and the strength of cement is reduced after the use of phosphogypsum. The inventor provides a special grinding aid for phosphogypsum cement, through which calcium silicate hydrate absorbs and solidifies impurities in phosphogypsum. At the same time, through the grinding aid of the grinding aid components, the gradation of cement particles can be improved, the physical strength of cement can be improved, and many problems in the application of phosphogypsum in the cement industry can be solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Grinding aid specially used for phosphogypsum cement, and preparation method of grinding aid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A special grinding aid for phosphogypsum cement, which is prepared from the following raw materials in parts by weight: 10 parts of alcohol amine grinding aid components, 40 parts of calcium silicate hydrate seed crystals, 0.5 parts of thickening and dispersing agent, defoaming 0.1 part of agent, 20 parts of water; described calcium silicate hydrate crystal seed is made through the following steps:

[0029] (1) Configure A solution: weigh 5 parts of Ca(NO 3 ) 2 4H 2 O was dissolved in 10 parts of deionized water, stirred and dissolved to make A solution;

[0030] (2) Configuration B solution: weigh 4 parts of Na 2 SiO 3 9H 2 O was dissolved in 8 parts of deionized water and stirred to make solution B;

[0031] (3) Add 0.5 parts of polyvinyl alcohol and 20 parts of deionized water into the high-speed stirring tank, stir to dissolve, control the temperature at 20 ° C, and add solution A and B solution to the stirring tank at the same time, keep the constant temperat...

Embodiment 2

[0045] A special grinding aid for phosphogypsum cement, which is prepared from the following raw materials in parts by weight: 20 parts of alcohol amine grinding aid components, 50 parts of calcium silicate hydrate seed crystals, 0.5 parts of thickening dispersant, defoaming agent 0.1 part of agent, 30 parts of water; described calcium silicate hydrate crystal seed is made through the following steps:

[0046] (1) Configure A solution: weigh 8 parts of Ca(NO 3 ) 2 4H 2 O was dissolved in 12 parts of deionized water, stirred and dissolved to make A solution;

[0047] (2) Configuration B solution: weigh 5 parts of Na 2 SiO 3 9H 2 O was dissolved in 10 parts of deionized water and stirred to make solution B;

[0048] (3) Add 0.8 parts of polyvinyl alcohol and 25 parts of deionized water into the high-speed stirred tank, stir to dissolve, control the temperature at 20°C, and add solution A and B into the stirred tank at the same time, keep the constant temperature at 20°C, a...

Embodiment 3

[0062] A special grinding aid for phosphogypsum cement, prepared from the following raw materials in parts by weight: 30 parts of alcohol amine grinding aid components, 70 parts of calcium silicate hydrate seed crystals, 2 parts of thickening and dispersing agent, defoaming agent 0.5 part of agent, 40 parts of water; Described calcium silicate hydrate crystal seed is made through the following steps:

[0063] (1) Configure A solution: weigh 10 parts of Ca(NO 3 ) 2 4H 2 O was dissolved in 15 parts of deionized water, stirred and dissolved to make A solution;

[0064] (2) Configuration B solution: weigh 6 parts of Na 2 SiO 3 9H 2 O was dissolved in 12 parts of deionized water, stirred to make B solution;

[0065] (3) Add 1 part of polyvinyl alcohol and 30 parts of deionized water into the high-speed stirred tank, stir to dissolve, control the temperature at 20 ° C, and add solution A and B to the stirred tank at the same time, keep the constant temperature at 20 ° C, stir ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a grinding aid specially used for phosphogypsum cement, and a preparation method of the grinding aid, belonging to the technical field of cement additives. The grinding aid isprepared from the following raw materials in parts by weight: 10-30 parts of an alcohol amine-based grinding aid component, 40-70 parts of hydrated calcium silicate seed crystals, 0.5-2 parts of a thickening dispersing agent, 0.1-0.5 part of a defoaming agent and 20-40 parts of water. The prepared hydrated calcium silicate seed crystals are used as a substance for inducing cement hydration, so that the induction period of a cement hydration process is shortened, and the hydration reaction speed is accelerated; furthermore, the grinding acid also can absorb a water-soluble phosphorus compound in phosphogypsum, thereby accelerating the cement hydration and reducing the impact of phosphorus-containing impurities of the phosphogypsum on the cement hydration. The alcohol amine-based grinding aid component is also introduced, and all the substances have a synergistic effect, so that the problems such as later strength reduction caused by the impurities of the phosphogypsum are reduced to a certain extent. The product provided by the invention is in a liquid form, and has the advantages of being simple to use, convenient to transport, and the like.

Description

technical field [0001] The invention belongs to the technical field of cement admixtures, and in particular relates to a special grinding aid for phosphogypsum cement and a preparation method thereof. Background technique [0002] Phosphogypsum is a by-product of the wet-process phosphoric acid production process, and its main component is CaSO 4 2H 2 O and some other impurities. Generally, every 1t of wet-process phosphoric acid produced (in P 2 o 5 Total) 4~4.5t of phosphogypsum will be produced by-product. At present, the vast majority of phosphogypsum has not been comprehensively utilized, but is disposed of by discarding and stacking, which not only occupies land, pollutes the environment, but also wastes reusable resources. Considering the total amount of consumption and the impact on the environment, the preparation of building materials from phosphogypsum is one of the most suitable ways of utilization. Cement is currently the largest and most widely used bulk b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/12C04B103/52
CPCC04B40/0039C04B2103/52C04B24/122C04B22/00C04B2103/408C04B2103/44C04B2103/50
Inventor 李耀司宏振秦尤敏董芹玺宋南京冯恩娟张辉
Owner SHANDONG HONGYI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com