Welding wire flux-cored powder, rutile type seamless flux-cored welding wire and preparation and application

A technology of seamless flux-cored welding wire and rutile type, applied in welding equipment, metal processing equipment, welding media, etc., can solve the problems of increasing the difficulty of formula design and the difference in the initial design of welding wire, and achieve stable mechanical properties of deposited metal and process Good performance and strong cold crack resistance

Active Publication Date: 2019-03-19
725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to its structural characteristics, the seamless flux cored wire must be annealed during its manufacturing process, and the annealing process will cause changes in the flux core powder, resulting in a certain difference between the final wire and the initial design, increasing the difficulty of formula design

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding wire flux-cored powder, rutile type seamless flux-cored welding wire and preparation and application
  • Welding wire flux-cored powder, rutile type seamless flux-cored welding wire and preparation and application
  • Welding wire flux-cored powder, rutile type seamless flux-cored welding wire and preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A welding wire flux core powder, comprising the following components by mass percentage:

[0047]

[0048] A rutile-type seamless flux-cored welding wire, comprising the above-mentioned welding wire flux core powder and welding wire sheath low-carbon steel strip (see Table 1 and Table 2 for composition and performance);

[0049] The preparation method of the rutile seamless flux-cored wire comprises the following steps:

[0050] (1) mixing the components of the welding wire flux core powder to obtain the welding wire flux core powder;

[0051] (2) The welding wire sheath low-carbon steel strip adopts the welding wire flux core powder obtained in step (1) to be added online synchronously, roll forming and welding to obtain the welding wire wire rod; then under the protection of inert gas argon, the welding wire wire rod Anneal at 950°C for 4 hours in a well-type annealing furnace; reduce the diameter of the wire rod after annealing, and obtain rutile-type seamless flux...

Embodiment 2

[0053] A welding wire flux core powder, comprising the following components by mass percentage:

[0054]

[0055] A rutile-type seamless flux-cored welding wire, comprising the above-mentioned welding wire flux core powder and welding wire sheath low-carbon steel strip (see Table 1 and Table 2 for composition and performance);

[0056] The preparation method of the rutile seamless flux-cored wire comprises the following steps:

[0057] (1) mixing the components of the welding wire flux core powder to obtain the welding wire flux core powder;

[0058] (2) The welding wire sheath low-carbon steel strip adopts the welding wire flux core powder obtained in step (1) to be added online synchronously, roll forming and welding to obtain the welding wire wire rod; then under the protection of inert gas argon, the welding wire wire rod Anneal at 750°C for 5.5 hours in a well-type annealing furnace; the diameter of the wire rod after annealing is reduced to obtain rutile-type seamles...

Embodiment 3

[0060] A welding wire flux core powder, comprising the following components by mass percentage:

[0061]

[0062] A rutile-type seamless flux-cored welding wire, comprising the above-mentioned welding wire flux core powder and welding wire sheath low-carbon steel strip (see Table 1 and Table 2 for composition and performance);

[0063] The preparation method of the rutile seamless flux-cored wire comprises the following steps:

[0064] (1) mixing the components of the welding wire flux core powder to obtain the welding wire flux core powder;

[0065] (2) The welding wire sheath low-carbon steel strip adopts the welding wire flux core powder obtained in step (1) to be added online synchronously, roll forming and welding to obtain the welding wire wire rod; then under the protection of inert gas argon, the welding wire wire rod Anneal at 600°C for 7 hours in a well-type annealing furnace; reduce the diameter of the wire rod after annealing, and obtain rutile seamless flux-co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of welding materials, and particularly relates to welding wire flux-cored powder, a rutile type seamless flux-cored welding wire and preparation and application. The welding wire flux-cored powder is prepared from the following components in percentage by mass: 30-40% of rutile, 0-5% of aluminum powder, 0-4% of silicon powder, 1-2% of aluminum-magnesiumalloy, 7-12 % of metal manganese, 1-2% of zircon sand, 1-2% of sodium carbonate, and the balance of iron powder. The rutile seamless flux cored welding wire further comprises the welding wire flux-cored powder, the welding wire has good processability, all-position welding under a suitable process specification can be realized, and the welding process is stable; and the mechanical properties of deposited metal is stable and the requirements of relevant standards are met, the rutile seamless flux cored welding wire is suitable for welding of 460MPa grade steel, and the welding wire deposited metal has low diffusion hydrogen content and high anti-cold crack ability.

Description

technical field [0001] The invention belongs to the technical field of welding materials, and in particular relates to a welding wire flux-cored powder, a rutile-type seamless flux-cored welding wire and its preparation and application. Background technique [0002] In recent years, the structural adjustment and product upgrading process of welding material products has been significantly accelerated. In the technical fields of marine engineering and shipbuilding, flux-cored welding wire has gradually replaced manual welding rods and solid welding wires due to its excellent manufacturability. In addition to the advantages of ordinary flux-cored wire, seamless flux-cored wire has great technical advantages in welding in shipbuilding, ocean engineering and other fields due to its excellent moisture resistance and good automation adaptability. . [0003] Due to its structural characteristics, the seamless flux cored wire must be annealed during the manufacturing process, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/368B23K35/30
CPCB23K35/0266B23K35/3053B23K35/368
Inventor 张文军王亚彬范会卿
Owner 725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com