Heat insulating material and preparation method thereof

A heat insulation and modification technology, applied in the field of building materials, can solve the problems of wall mold, wall dampness, wall hanging water, etc., and achieve the effect of improving low temperature resistance, low cost, and improving heat preservation

Inactive Publication Date: 2019-03-19
徐州金盛贸易有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the ambient humidity is high, especially during the rainy season in the south, the wall will often appear "water hanging" phenomenon; when the wall insulation is not done well, resulting in a large temperature difference between indoor and outdoor, the water in the indoor air will be Condensation on the wall will cause the wall to be damp; the wall will be prone to mildew if it is wet for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A thermal insulation material, made of the following components by weight: 45 parts of Portland cement, 10 parts of hard polyurethane, 6 parts of expanded perlite, 13 parts of lightweight ceramsite, 8 parts of borax, and 10 parts of gypsum 12 parts of modified attapulgite, 10 parts of glass fiber, 10 parts of ceramic fiber, 6 parts of flame retardant, and 5 parts of antibacterial agent.

[0028] Its preparation method comprises the following steps:

[0029] (1) First, modify the nano-attapulgite, dissolve the silane coupling agent in absolute ethanol to make a solution of a certain concentration, add the nano-attapulgite to stir and heat, cool to room temperature after fully reacting, and centrifuge at a high speed , washing, drying, and crushing to obtain modified nano-attapulgite;

[0030] (2) polyurethane liquid nitrogen is frozen, then pulverized into granular form through pulverizer;

[0031] (3) Stir Portland cement, expanded perlite, lightweight ceramsite, bora...

Embodiment 2

[0035] A thermal insulation material, made of the following components by weight: 50 parts of Portland cement, 12 parts of polyurethane, 8 parts of expanded perlite, 16 parts of lightweight ceramsite, 10 parts of borax, 12 parts of gypsum, modified 10 parts of attapulgite, 15 parts of glass fiber, 15 parts of ceramic fiber, 8 parts of flame retardant, and 9 parts of antibacterial agent.

[0036] Its preparation method comprises the following steps:

[0037] (1) First, modify the nano-attapulgite, dissolve the silane coupling agent in absolute ethanol to make a solution of a certain concentration, add the nano-attapulgite to stir and heat, cool to room temperature after fully reacting, and centrifuge at a high speed , washing, drying, and crushing to obtain modified nano-attapulgite;

[0038] (2) polyurethane liquid nitrogen is frozen, then pulverized into granular form through pulverizer;

[0039] (3) Stir Portland cement, expanded perlite, lightweight ceramsite, borax, gyps...

Embodiment 3

[0043] A thermal insulation material, made of the following components by weight: Portland cement 40-50 parts, polyurethane 6-12 parts, expanded perlite 4-8 parts, lightweight ceramsite 10-16 parts, borax 5-10 parts, 8-12 parts of gypsum, 10-15 parts of modified attapulgite, 5-15 parts of glass fiber, 5-15 parts of ceramic fiber, 2-8 parts of flame retardant, and 3-9 parts of antibacterial agent.

[0044] Its preparation method comprises the following steps:

[0045] (1) First, modify the nano-attapulgite, dissolve the silane coupling agent in absolute ethanol to make a solution of a certain concentration, add the nano-attapulgite to stir and heat, cool to room temperature after fully reacting, and centrifuge at a high speed , washing, drying, and crushing to obtain modified nano-attapulgite;

[0046] (2) polyurethane liquid nitrogen is frozen, then pulverized into granular form through pulverizer;

[0047] (3) Portland cement, expanded perlite, lightweight ceramsite, borax,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heat insulating material and a preparation method thereof. The material is prepared from the following components in parts by weight: 40-50 parts of silicate cement, 6-12 parts of polyurethane, 4-8 parts of expanded perlite, 10-16 parts of lightwight ceramisite, 5-10 parts of borax, 8-12 parts of gypsum, 10-15 parts of modified attapulgite, 5-15 parts of glass fibers, 5-15 parts of ceramic fibers, 2-8 parts of flame retardant and 3-9 parts of an antibacterial agent. The heat insulating material is reasonable in raw material compatibility and low in cost, has excellentfracture resistance and tensile resistance, excellent flame retardance and antibacterial performance, and has simple preparation process and wide application.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a thermal insulation material and a preparation method thereof. Background technique [0002] Thermal insulation is to reduce heat loss, improve energy utilization, and ultimately achieve the goal of energy conservation. The development and progress of thermal insulation materials will help promote the implementation of energy-saving projects, meet the needs of national economic development for energy, and protect the national economy. Building a healthy and stable development has great social and economic significance. Therefore, it is necessary to vigorously develop the thermal insulation material industry and widely adopt high-quality thermal insulation materials. This is of great practical significance to the healthy and stable development of economic construction. [0003] As an important factor affecting building energy saving, wall insulation materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B24/12C04B24/16C04B103/63C04B103/67C04B103/69C04B111/28C04B111/20
CPCC04B28/04C04B40/0039C04B2103/63C04B2103/67C04B2103/69C04B2111/2092C04B2111/28C04B14/185C04B16/04C04B18/027C04B22/0013C04B22/143C04B14/102C04B14/42C04B14/46C04B24/02C04B22/16C04B24/128C04B14/204C04B22/06C04B24/16
Inventor 王禹
Owner 徐州金盛贸易有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com