An ultra-fast cooling and process technology, which is applied in steel plates for subsea tunnels, high-strength bridge steel plates produced by ultra-fast cooling processes, and steel plates produced by ultra-fast cooling processes. It can solve the problems of high strength, high elongation, and impact resistance. , Difficult to adapt to high strength, high elongation, impact resistance, unable to meet the needs of high strength, etc., to achieve good comprehensive mechanical properties, save production technology, and save production costs

Active Publication Date: 2019-04-16
河北敬业中厚板有限公司
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] CN101135029 A records atmospheric corrosion-resistant steel with a yield strength of 700MPa and its manufacturing method, but its strength is low and cannot meet the high-strength requirements of different occasions
CN103114253 A records a production method of ultra-thin ultra-high-strength steel plates with a finished product thickness of 3-10mm. Although yield strength Rp0.2 can be obtained up to 950-1300MPa, tensile strength Rm: 1000-1500MPa, fracture Elongation A: 12-20%, -40°C impact absorption energy KV2: 80-270J, but the hot-rolled substrate has undergone two quenching + tempering heat treatment processes, which obviously affects production efficiency
CN103302255 A has recorded a kind of thin-strip continuous casting 700MPa level high-s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A method for producing steel plates by an ultra-fast cooling process, characterized in that: the components are C0.066%, Si 0.06%, Mn 1.52%, P≤0.01%, S≤0.004%, Nb 0.067%, Ti 0.023% by mass percentage %, V0.033%, Al≤0.050%, Cr 0.46%, Mo 0.36%, Ni 0.14%, Cu 0.06%, W 0.015%, rare earth 0.0005%, N 0.003%, the balance is Fe and unavoidable impurity elements ;

[0047] The process route includes: molten iron pretreatment → molten steel smelting → refining outside the furnace → continuous casting → heating and rolling → ultra-fast cooling process and coiling; the core steps are as follows:

[0048] (1) Hot metal pretreatment desulfurization;

[0049] (2) Converter smelting: Double slag operation, converter bottom blowing, carbon content target ≤0.055%, phosphorus content ≤0.015%, tapping temperature 1600-1650°C; double slag blocking tapping with slag blocking plug and slag blocking rod ;

[0050] (3) LF+RH refining process or RH or VD vacuum degassing;

[0051] (4) Continu...

Embodiment 2

[0056] A method for producing steel plates by an ultra-fast cooling process, characterized in that: the components are C0.068%, Si 0.08%, Mn 1.52%, P≤0.01%, S≤0.004%, Nb 0.067%, Ti 0.023% by mass percentage %, V0.032%, Al≤0.050%, Cr0.47%, Mo 0.37%, Ni 0.13%, Cu 0.06%, W 0.011%, rare earth 0.0007%, N 0.005%, the balance is Fe and unavoidable impurities element;

[0057] The process route includes: molten iron pretreatment → molten steel smelting → refining outside the furnace → continuous casting → heating and rolling → ultra-fast cooling process and coiling; the core steps are as follows:

[0058] (1) Hot metal pretreatment desulfurization;

[0059] (2) Converter smelting: Double slag operation, converter bottom blowing, carbon content target ≤0.055%, phosphorus content ≤0.015%, tapping temperature 1600-1650°C; double slag blocking tapping with slag blocking plug and slag blocking rod ;

[0060] (3) LF+RH refining process or RH or VD vacuum degassing;

[0061] (4) Continuo...

Embodiment 3

[0066] A method for producing steel plates by an ultra-fast cooling process, characterized in that: the components are C0.069%, Si 0.1%, Mn 1.55%, P≤0.01%, S≤0.004%, Nb 0.07%, Ti 0.025% by mass percentage %, V0.035%, Al≤0.050%, Cr0.48%, Mo 0.38%, Ni 0.15%, Cu 0.09%, W 0.01%, rare earth 0.001%, N 0.005%, the balance is Fe and unavoidable impurities element;

[0067] The process route includes: molten iron pretreatment → molten steel smelting → refining outside the furnace → continuous casting → heating and rolling → ultra-fast cooling process and coiling; the core steps are as follows:

[0068] (1) Hot metal pretreatment desulfurization;

[0069] (2) Converter smelting: Double slag operation, converter bottom blowing, carbon content target ≤0.055%, phosphorus content ≤0.015%, tapping temperature 1600-1650°C; double slag blocking tapping with slag blocking plug and slag blocking rod ;

[0070] (3) LF+RH refining process or RH or VD vacuum degassing;

[0071] (4) Continuous c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for producing a steel plate through the super-fast cooling technology. The method is characterized in that components comprise, by mass percent, 0.066%-0.069% of C, 0.05%-0.1% of Si, 1.5%-1.55% of Mn, smaller than or equal to 0.01% of P, smaller than or equal to 0.004% of S, 0.13%-0.2% of (Nb+Ti+V), smaller than or equal to 0.050% of Al, at least three of Cr, Mo, Ni, Cu, W and rare earth, and the balance Fe and inevitable impurity elements. According to the super-fast cooling technology, the finish rolling temperature of 845-850 DEG C is reduced to 360-365 DEGC through cooling at the cooling speed of 80-90 DEG C/s, and reeling is conducted at the temperature of 350-355 DEG C.

Description

technical field [0001] The invention belongs to the technical field of metal materials, and in particular relates to a method for producing steel plates by an ultra-fast cooling process, in particular to a method for producing high-strength steel plates for bridges and submarine tunnels by an ultra-fast cooling process. Background technique [0002] Atmospheric corrosion-resistant low-alloy structural steel is widely used in the field of outdoor steel structure manufacturing such as buildings, bridges, containers, and vehicles. It is based on low-carbon manganese steel, adding a small amount of low-alloy corrosion-resistant elements such as Cr, Cu, Ni, etc., to promote the change of the rust layer structure of the steel, which is beneficial to slow down the atmospheric corrosion rate and significantly improve the atmospheric corrosion resistance of the steel. [0003] CN101135029 A records atmospheric corrosion-resistant steel with a yield strength of 700MPa and its manufact...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/58C22C38/50C22C38/48C22C38/46C22C38/44C22C38/42C22C38/06C22C38/02C22C33/04C21D8/02C21D11/00
CPCC21D8/0205C21D8/0226C21D11/005C21D2211/005C21D2211/008C22C33/04C22C38/001C22C38/002C22C38/005C22C38/02C22C38/06C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50C22C38/58
Inventor 杨海西张少凯樊利智曹晓运
Owner 河北敬业中厚板有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap