A kind of linear dialdehyde modified polyvinyl alcohol and its preparation method and application

A technology of polyvinyl alcohol and dialdehyde, which is applied in the field of straight-chain dialdehyde modified polyvinyl alcohol and its preparation, can solve the problems of excessive molecular weight distribution, poor product quality, and poor foam suppression performance, and achieve the goal of inhibiting Foaming during vinyl chloride polymerization, suppressing foaming, and excellent performance

Active Publication Date: 2021-07-02
CHINA PETROCHEMICAL CORP +2
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN151927A discloses that a modified polyvinyl alcohol dispersant is prepared by adding polyvinyl alcohol resin to a metal salt and other additives at a temperature of 175-250 ° C in an extruder for 1-15 minutes by melt kneading; the method Medium-modified polyvinyl alcohol will undergo severe dehydration and decarboxylation reactions, and at the same time, partial decomposition reactions will occur, the economic cost is high, the color of the obtained product is darker, and insoluble substances are produced, and the product quality is poor
Chinese patent CN101747459A discloses that the modified polyvinyl alcohol dispersant is obtained through bulk polymerization or solution polymerization for 8-14 hours, and then undergoes subsequent alcoholysis, drying and other processes to obtain a modified polyvinyl alcohol dispersant; The anti-foaming performance of the product is relatively poor; the modified polyvinyl alcohol product prepared by this method is also only used as an auxiliary dispersant in the suspension polymerization of vinyl chloride
Due to the high technical difficulty, there is currently no polyvinyl alcohol with good color hue, excellent foam suppression, colloid retention, and dispersibility as a dispersant and its preparation technology disclosure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of linear dialdehyde modified polyvinyl alcohol and its preparation method and application
  • A kind of linear dialdehyde modified polyvinyl alcohol and its preparation method and application
  • A kind of linear dialdehyde modified polyvinyl alcohol and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035]100 parts by weight of vinyl acetate, 100 parts by weight of methanol, 3.0 parts by weight of adipaldehyde and 0.072 parts by weight of azobisisobutyronitrile (AIBN) were added to the polymerization reactor. After replacing with nitrogen, the temperature began to rise, and the polymerization reaction began to count when there was reflux at about 60° C., and ended after 5 hours. Unreacted vinyl acetate is then removed to obtain a methanol solution of polyvinyl acetate. To the obtained polyvinyl acetate methanol solution (concentration 32-35%), add 10 millimoles of sodium hydroxide in methanol per mole of vinyl acetate unit. Carry out hydrolysis at 40°C for 35 minutes, add glacial acetic acid equivalent to sodium hydroxide to terminate the reaction, and obtain a methanol solution of PVA resin, and send the methanol solution of PVA resin evenly into a centrifuge protected by nitrogen through a screw pump for solidification Liquid separation, to obtain PVA resin (1# degree ...

Embodiment 2

[0037] 100 parts by weight of vinyl acetate, 80 parts by weight of methanol, 3.5 parts by weight of adipaldehyde and 0.072 parts by weight of azobisisobutyronitrile (AIBN) were added to the polymerization reactor. After replacing with nitrogen, the temperature began to rise, and the polymerization reaction began to count when there was reflux at about 60° C., and ended after 5 hours. Unreacted vinyl acetate is then removed to obtain a methanol solution of polyvinyl acetate. To the resulting polyvinyl acetate methanol solution (concentration 32-35%), add 10 millimoles of sodium hydroxide in methanol per mole of vinyl acetate unit. Hydrolyze at 40° C. for 35 minutes, add glacial acetic acid equivalent to sodium hydroxide to terminate the reaction, and obtain PVA resin (2# degree of polymerization 731, degree of alcoholysis 71.97 mol%) after centrifugation. The obtained PVA resin was dried in a vacuum drying oven at 110° C. for 2 hours under a vacuum degree of −0.01 MPa to obtai...

Embodiment 3

[0039] 100 parts by weight of vinyl acetate, 60 parts by weight of methanol, 4.5 parts by weight of adipaldehyde and 0.070 parts by weight of azobisisobutyronitrile (AIBN) were added to the polymerization reactor. After replacing with nitrogen, the temperature began to rise, and the polymerization reaction began to count when there was reflux at about 60° C., and ended after 5 hours. Unreacted vinyl acetate is then removed to obtain a methanol solution of polyvinyl acetate. To the resulting polyvinyl acetate methanol solution (concentration 32-35%), add 10 millimoles of sodium hydroxide in methanol per mole of vinyl acetate unit. Carry out hydrolysis at 40°C for 35 minutes, add glacial acetic acid equivalent to sodium hydroxide to terminate the reaction, and obtain a methanol solution of PVA resin, and send the methanol solution of PVA resin evenly into a centrifuge protected by nitrogen through a screw pump for solidification The liquid was separated to obtain PVA resin (3# ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
Login to View More

Abstract

The invention provides a linear divalent aldehyde modified polyvinyl alcohol. The linear divalent aldehyde is used to modify the polyvinyl alcohol. As the main dispersant for vinyl chloride suspension polymerization, it has good dispersion effect, can effectively inhibit foaming during vinyl chloride polymerization, and has both good adhesive retention and dispersion properties; it can be prepared with a viscosity of 107-112ml / g. Table The apparent density is 0.45-0.50g / ml, the plasticizer absorption is more than 20%, the PVC product with excellent performance and uniform particle size distribution. The preparation method of the invention is simple, the process time is short, large-scale equipment is not required, and the invention is suitable for industrial production.

Description

technical field [0001] The invention relates to modified polyvinyl alcohol, in particular to a straight-chain dialdehyde-modified polyvinyl alcohol and its preparation method and application. Background technique [0002] Polyvinyl alcohol (PVA), as the most commonly used dispersant for vinyl chloride suspension polymerization, plays a vital role in the performance index of vinyl chloride suspension polymerization and polyvinyl chloride products. However, with the application of large-scale polymerization reactors equipped with condensers in the vinyl chloride industry, the pressure near the reflux condenser drops due to the condensation of vinyl chloride monomer vapor, resulting in wet foam caused by dispersants and composed of PVC particles dry foam, resulting in a reduction in the effective volume in the polymerization vessel, a decrease in production efficiency, and fouling. Therefore, it is necessary to develop new polyvinyl alcohol as a dispersant. [0003] In the de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F118/08C08F8/12C08F2/20C08F114/06
CPCC08F2/20C08F8/12C08F114/06C08F118/08
Inventor 侯双燕陆春因郭永松李永江
Owner CHINA PETROCHEMICAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com