Preparation method of waterproof flame-retardant textiles

A technology for flame-retardant textiles and textiles, applied in textiles and papermaking, flame-retardant fibers, improved hand-feeling fibers, etc., can solve the problems of poor washing resistance of textiles, short duration of waterproof and flame-retardant performance of textiles, and decreased mechanical properties of textiles. , to achieve excellent waterproof and flame retardant performance, environmental protection, good cross-linking effect

Inactive Publication Date: 2019-04-23
余姚市立帅印染有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the traditional flame retardants are organophosphorus flame retardants, but the free formaldehyde content in the finished textiles is high, which is harmful to the human body, and the mechanical properties of the textiles have also declined. T

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of waterproof flame-retardant textiles
  • Preparation method of waterproof flame-retardant textiles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The preparation method of waterproof flame-retardant textile, comprises the following steps:

[0024] (1) Pretreatment of textiles: Soak the textiles to be treated in clear water, ultrasonic for 10 minutes, take out, dry at 60°C, and set aside;

[0025] (2) Put the pretreated textiles into low-pressure plasma equipment for processing. During the processing, the discharge frequency of the plasma is 20MHZ, and the discharge power is 180W. The front and back sides of the textiles are treated 80 times, and the processing time is 30min. take out for use;

[0026] (3) Mix 3 g of flame retardant, 5 g of polyacrylate, 1 g of crosslinking agent, 1 g of dispersant and 40 g of deionized water, and ultrasonicate for 60 minutes to obtain a waterproof and flame retardant finishing agent;

[0027] (4) Immerse the textile after the plasma treatment into the waterproof and flame-retardant finishing agent obtained in step (3), perform two dipping and two rolling, and the excess rate is ...

Embodiment 2

[0029] The preparation method of waterproof flame-retardant textile, comprises the following steps:

[0030] (1) Pretreatment of textiles: Soak the textiles to be treated in clear water, ultrasonicate for 30 minutes, take them out, dry them at 80°C, and set aside;

[0031] (2) Put the pretreated textiles into low-pressure plasma equipment for processing. During the processing, the discharge frequency of the plasma is 20MHZ, and the discharge power is 180W. The front and back sides of the textiles are treated 80 times, and the processing time is 80min. take out for use;

[0032] (3) Mix 3g of flame retardant, 5g of polyacrylate, 1g of crosslinking agent, 1g of dispersant and 40g of deionized water, and ultrasonicate for 100min to obtain a waterproof and flame retardant finishing agent;

[0033] (4) Immerse the textiles after plasma treatment into the waterproof and flame-retardant finishing agent obtained in step (3), perform two dipping and two rolling, the excess rate is 80%...

Embodiment 3

[0035] The preparation method of waterproof flame-retardant textile, comprises the following steps:

[0036] (1) Pretreatment of textiles: Soak the textiles to be treated in clear water, ultrasonicate for 15 minutes, take them out, dry at 65°C, and set aside;

[0037] (2) Put the pretreated textiles into low-pressure plasma equipment for processing. During the processing, the discharge frequency of the plasma is 20MHZ, and the discharge power is 180W. The front and back sides of the textiles are each processed 80 times, and the processing time is 40min. take out for use;

[0038] (3) Mix 3 g of flame retardant, 5 g of polyacrylate, 1 g of crosslinking agent, 1 g of dispersant and 40 g of deionized water, and ultrasonicate for 70 minutes to obtain a waterproof and flame retardant finishing agent;

[0039] (4) Immerse the textiles after plasma treatment into the waterproof and flame-retardant finishing agent obtained in step (3), perform two dipping and two rolling, the excess ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of waterproof flame-retardant textiles. The method comprises the following steps: pretreating the textiles; subjecting the pretreated textiles to plasma treatment; preparing a waterproof flame-retardant finishing agent, soaking the plasma treated textiles in the prepared waterproof flame-retardant finishing agent, and carrying out twice-soaking twice-rolling until the rolling remaining rate is 80%; taking out the textiles, cleaning the textiles with clean water for 2 to 3 times, carrying out drying and carrying out baking, thereby obtaining the waterproof flame-retardant textiles. The waterproof flame-retardant textiles prepared by the method have excellent waterproof and flame retardant properties, are free of off odors, good in washing resistance, free of toxic substances and safe to human bodies and are soft and comfortable.

Description

Technical field: [0001] The invention relates to the technical field of textile finishing, in particular to a finishing method of waterproof and flame-retardant textiles. Background technique: [0002] In recent years, with the rapid increase in the consumption of decorative textiles, the fires caused by textiles are increasing, among which the fires of bedding and home decoration cloth are one of the main reasons. After the burning textiles come into contact with the human body, it will cause skin burns at the slightest level and endanger life at the severest level. During the burning of textiles, a large amount of harmful gases released will also endanger people's health, including various gases such as carbon monoxide, carbon dioxide, hydrogen cyanide and aldehydes, which will cause people to suffocate and die. Therefore, while preventing fires, how to improve the flame-retardant properties of textiles and reduce the losses caused by fires has become an important topic i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M10/02D06M15/263D06M11/44D06M13/419D06M13/262D06M13/256
CPCD06M10/025D06M11/44D06M13/256D06M13/262D06M13/419D06M15/263D06M2200/12D06M2200/30D06M2200/50
Inventor 周静
Owner 余姚市立帅印染有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap