Preparation methods of high-temperature-resistant adhesive and high-temperature-resistant aluminum tape

An aluminum foil tape and adhesive technology, which is applied in the directions of adhesives, adhesive additives, polymer adhesive additives, etc., can solve the problems of environmental pollution, high preparation cost, limited use range of aluminum foil tapes, etc. Easy to operate, simple process effect

Active Publication Date: 2019-04-26
江阴美源实业有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, the preparation cost of aluminum foil tape is high, and the environment is polluted during the production process. The scope of use of the existing aluminum foil tape is limited, and it no longer meets the needs of the actual market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method of high temperature resistant adhesive, comprising the following steps:

[0029] Preparation of raw gum:

[0030] S1: The composition of the raw gum is as follows in parts by weight: 30 parts of isooctyl acrylate, 15 parts of butyl acrylate, 4 parts of acrylic acid, 3 parts of hydroxyethyl acrylate, and 48 parts of toluene;

[0031] S2: Accurately weigh the various raw materials in S1, stir the above-mentioned raw materials in the reactor at room temperature, raise the temperature of the reactor to 110°C, carry out the polymerization reaction at the reflux temperature of toluene, and the reaction time is 10 hours to obtain the original gum and recover the original Toluene in glue;

[0032] Preparation of the adhesive:

[0033] S3: The adhesive is composed as follows in parts by weight: 63 parts of the above-mentioned raw gum, 17 parts of rosin tackifying resin, 19 parts of toluene, and 1 part of crosslinking agent;

[0034] Wherein the crosslinki...

Embodiment 2

[0043] A preparation method of high temperature resistant adhesive, comprising the following steps:

[0044] Preparation of raw gum:

[0045] S1: The composition of the raw gum is as follows in parts by weight: 36 parts of isooctyl acrylate, 15 parts of butyl acrylate, 3 parts of acrylic acid, 1 part of hydroxyethyl acrylate, and 45 parts of toluene;

[0046] S2: Accurately weigh the various raw materials in S1, stir the above raw materials evenly in the reactor at room temperature, raise the temperature of the reactor to 115°C, and carry out the polymerization reaction at the reflux temperature of toluene. Toluene in glue;

[0047] Preparation of the adhesive:

[0048] S3: The adhesive is composed as follows in parts by weight: 50 parts of the above-mentioned raw gum, 18 parts of rosin tackifying resin, 20 parts of toluene, 2 parts of crosslinking agent, and 10 parts of chlorinated paraffin;

[0049] Wherein the crosslinking agent is composed as follows in parts by weight:...

Embodiment 3

[0057] A preparation method of high temperature resistant adhesive, comprising the following steps:

[0058] Preparation of raw gum:

[0059]S1: The composition of the raw gum is as follows in parts by weight: 30 parts of isooctyl acrylate, 20 parts of butyl acrylate, 3 parts of acrylic acid, 2 parts of hydroxyethyl acrylate, and 45 parts of toluene;

[0060] S2: Accurately weigh the various raw materials in S1, stir the above raw materials evenly in the reactor at room temperature, raise the temperature of the reactor to 120°C, and carry out the polymerization reaction at the reflux temperature of toluene. Toluene in glue;

[0061] Preparation of the adhesive:

[0062] S3: The adhesive is composed as follows in parts by weight: 50 parts of the above-mentioned raw gum, 18 parts of rosin tackifying resin, 20 parts of toluene, 2 parts of crosslinking agent, 5 parts of chlorinated paraffin, and 5 parts of antimony trioxide;

[0063] Wherein the crosslinking agent is composed a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
peel strengthaaaaaaaaaa
stay stickyaaaaaaaaaa
Login to view more

Abstract

The invention discloses preparation methods of a high-temperature-resistant adhesive and a high-temperature-resistant aluminum tape. The preparation method of the high-temperature-resistant adhesive comprises the following steps: preparation of a raw adhesive: S1, the raw adhesive is prepared from 30-40 parts of 2-ethylhexyl acrylate, 12-20 parts of butyl acrylate, 3-6 parts of acrylic acid, 1-5 parts of hydroxyethyl acrylate and 45-55 parts of toluene; S2, various raw materials are accurately weighed and uniformly stirred at normal temperature in a reactor, the reactor is heated to 110-120 DEG C, polymerization reaction is conducted at toluene reflux temperature for 8-12 h, and the raw adhesive is prepared; preparation of the adhesive: S3, the adhesive is prepared from the following components: 50-65 parts of the original adhesive, 15-18 parts of rosin tackifying resin, 18-22 parts of toluene and 0.5-2 parts of a crosslinking agent; S4, various raw materials in S3 are accurately weighed and uniformly stirred at normal temperature in the reactor for 5-8 h, and the high-temperature resistant adhesive is prepared. The aluminum tape prepared from the high-temperature resistant adhesive has high tensile strength, is easy to operate, green and environmentally friendly, can be pasted on site easily, improves pasting efficiency, and is suitable for machine pasting.

Description

technical field [0001] The invention relates to the technical field of adhesive materials, in particular to a preparation method of a high-temperature-resistant adhesive and a high-temperature-resistant aluminum foil tape. Background technique [0002] The tape is mainly composed of a base material and a layer of adhesive coated on one or both surfaces of the base material. By forming a bond between the adhesive molecules on the base material and the surface molecules of the object, the tape adheres on the surface of the item. Divided by function, tapes can be divided into high temperature tapes, pressure sensitive tapes, insulating tapes, special tapes, die-cut tapes, etc. [0003] Aluminum foil tape is a kind of metal foil tape with good viscosity, strong adhesion and good anti-aging performance. It is widely used in the joint bonding of all aluminum foil composite materials, the sealing of the punctured part of the insulation nail and the repair of the damaged part. It i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C09J193/04C09J11/04C09J11/08C09J11/06C09J7/28C09J7/30
CPCC08L2205/035C09J11/04C09J11/06C09J11/08C09J133/066C09J2400/163C09J2433/00C09J7/28C09J7/30C08L93/04C08L23/06C08L23/0869C08K5/29C08K3/042
Inventor 张惠民
Owner 江阴美源实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap