Novel electrode slice and preparation method thereof, and solid-state battery equipped with the same

An electrode sheet, a new type of technology, applied in the direction of electrode manufacturing, battery electrodes, secondary batteries, etc., can solve problems such as easy to break, cannot change the diaphragm, and has no protective effect, so as to reduce the probability of spontaneous combustion and improve safety. Effect

Active Publication Date: 2019-05-03
ZHEJIANG FUNLITHIUM NEW ENERGY TECH CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the most common way to improve safety is to use ceramic diaphragms. Ceramic diaphragms can improve the thermal shrinkage performance of the diaphragm to a certain extent, but they cannot change the nature of the diaphragm shrinking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel electrode slice and preparation method thereof, and solid-state battery equipped with the same
  • Novel electrode slice and preparation method thereof, and solid-state battery equipped with the same
  • Novel electrode slice and preparation method thereof, and solid-state battery equipped with the same

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0033] Example one:

[0034] A method for preparing a novel negative electrode sheet includes the following steps:

[0035] Step 1. Preparation of coating one and two slurry:

[0036] Weigh the negative active material natural graphite, conductive agent SuperP, binder powder CMC and SBR, where the mass ratio of natural graphite: SP: CMC: SBR = 94:1:1:1, first dissolve CMC with deionized water, Then add natural graphite and SP respectively, and finally add SBR. When these components are completely dispersed and uniform, add deionized water to adjust the solid content of the slurry to 40%, and finally perform vacuum degassing for 4 hours to complete the coating-2 slurry Preparation;

[0037] Step two, preparation of coating two and three slurry:

[0038] a. Mix NMP and DMP at a mass ratio m(NMP): m(DMF)=1:1 to complete the preparation of mixed solvent one;

[0039] b. Stir the mixed solvent one at 500-1000 rpm, and add PVDF powder at a uniform speed according to the mass ratio m (mixed s...

Example Embodiment

[0054] Embodiment two:

[0055] A method for preparing a novel positive electrode sheet includes the following steps:

[0056] Step 1. Preparation of coating slurry:

[0057] Weigh the positive active material NCM, the conductive agent KS-15, the powdered cellulose acetate butyrate and cyanoethyl sucrose as the binder, wherein the mass ratio is NCM: KS-15: cellulose acetate butyrate: cyanoethyl sucrose = 48:1:1:1, first dissolve cyanoethyl sucrose with deionized water, then add NCM and KS-15 respectively, and finally add cellulose acetate butyrate. When these components are completely dispersed, add deionized water. Adjust the solid content of the slurry to 50%, and finally perform vacuum degassing for 4 hours to complete the preparation of the coating slurry;

[0058] Step 2: Preparation of the second coating slurry:

[0059] a. Mix DMAc and acetone at a mass ratio of m(DMAc): m(acetone)=1:1 to complete the preparation of mixed solvent one;

[0060] b. Stir the mixed solvent one at 50...

Example Embodiment

[0065] Embodiment three:

[0066] A method for preparing a novel negative electrode sheet includes the following steps:

[0067] Step 1. Preparation of coating slurry:

[0068] Weigh the negative active material silicon-carbon material, conductive agent Ketjen Black, and binder powder PMMA and PVA. Among them, the mass ratio of silicon-carbon material: Ketjen Black: PMMA: PVA = 95: 1.5: 1.5: 1.5, use first Dissolve PVA in deionized water, then add silicon carbon material and Ketjen Black, and finally add PMMA. When these components are completely dispersed, add deionized water to adjust the solid content of the slurry to 45%, and finally perform vacuum degassing for 4 hours , So as to complete the preparation of the coating slurry;

[0069] Step 2. Preparation of coating three slurry:

[0070] (1) In an environment with a dew point of less than -20°C, mix DMAc and tetrahydrofuran with a mass ratio of m(tetrahydrofuran): m(DMAc)=1:1 to complete the preparation of mixed solvent two;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel electrode slice, which relates to the field of a lithium ion solid state battery. The electrode slice mainly comprises a current collector and a coating layer I appliedto both side surfaces of the current collector; the outer side of the coating layer I is coated with one or two of a coating layer II or a coating layer III; the coating layer I contains an electrodeactive material, a binder and a conductive agent; the coating layer II contains a lithium ion conducting material, inert powder, and the binder; and the coating layer III contains a lithium salt andthe binder. The coating II and the coating III can synchronously expand and contract with the coating I, and so, the probability of breakage is reduced, and the coating II and the coating III can actas a diaphragm, thereby reducing danger brought by fragmentation of the diaphragm, and the service life of the solid-state battery is also guaranteed. In addition, the preparation method is also relatively simple and is suitable for scale performing, and a cell of the solid-state battery prepared by the method is strong in safety and in service life.

Description

technical field [0001] The invention relates to the field of lithium-ion solid-state batteries, more specifically, it relates to a novel electrode sheet, a preparation method thereof and a solid-state battery with the electrode sheet. Background technique [0002] Lithium-ion secondary battery is a clean and high-performance energy source, which has the advantages of no memory effect, long cycle life, high energy density, high working voltage, small self-discharge, light weight, etc., so it is more and more widely used. At present, more and more automobile companies have begun to release and produce electric vehicles, and the safety performance of batteries is becoming more and more important. [0003] At present, the most common way to improve safety is to use ceramic diaphragms. Ceramic diaphragms can improve the thermal shrinkage performance of the diaphragm to a certain extent, but cannot change the nature of the diaphragm shrinking when heated. Moreover, when the ambie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/13H01M4/139H01M4/04H01M10/0525
CPCY02E60/10
Inventor 林久徐忠伟许晓雄夏旭东
Owner ZHEJIANG FUNLITHIUM NEW ENERGY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap