Decorated enameled part

A technology of enamel and parts, which is applied in the direction of decorative art and the process for producing decorative surface effects, etc. It can solve the problems of inconvenient decoration of the dial, and achieve the effect of reducing operation steps, reducing production costs, and conveniently taking materials

Inactive Publication Date: 2019-05-14
SHENZHEN ZHONGBAOYING JEWELRY TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a decorative enamelled part, which has the advantage of being easy to use and solves the problem of inconvenient decoration of the dial

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Decorated enameled part
  • Decorated enameled part

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The manufacturing method of the decorative enamel parts comprises the following steps: step 1: stamping the copper material into a copper plate 1 with a diameter of 32 mm through a stamping die, and then grinding the copper plate 1 by a grinding machine; step 2: spraying the copper plate 1 on the copper plate Evenly spray glaze on the upper surface of the copper plate 1 to form an underglaze layer 2; Step 3: put the copper plate 1 sprayed with the underglaze layer 2 into a dryer for drying, and wait for the underglaze layer 2 and the copper plate 1 When connected as a whole, the upper surface of the bottom glaze layer 2 is sprayed with glaze again by a spraying machine, and the top glaze layer 3 is formed on the top surface of the bottom glaze layer 2; Step 4: Put the copper plate 1 sprayed with the top glaze layer 3 into Drying in the dryer, when the surface glaze layer 3 and the bottom glaze layer 2 are connected as a whole, the upper surface of the surface glaze layer...

Embodiment 2

[0042] In embodiment 1, add following steps again:

[0043] In step 3, the drying temperature of the dryer is 20-60° C., and the drying time is 5-10 minutes.

[0044]The manufacturing method of the decorative enamel parts comprises the following steps: step 1: stamping the copper material into a copper plate 1 with a diameter of 32 mm through a stamping die, and then grinding the copper plate 1 by a grinding machine; step 2: spraying the copper plate 1 on the copper plate Evenly spray glaze on the upper surface of the copper plate 1 to form an underglaze layer 2; Step 3: put the copper plate 1 sprayed with the underglaze layer 2 into a dryer for drying, and wait for the underglaze layer 2 and the copper plate 1 When connected as a whole, the upper surface of the bottom glaze layer 2 is sprayed with glaze again by a spraying machine, and the top glaze layer 3 is formed on the top surface of the bottom glaze layer 2; Step 4: Put the copper plate 1 sprayed with the top glaze laye...

Embodiment 3

[0046] In embodiment 2, add following steps again:

[0047] In step 4, the drying temperature of the dryer is 30-70° C., and the drying time is 8-15 minutes.

[0048] The manufacturing method of the decorative enamel parts comprises the following steps: step 1: stamping the copper material into a copper plate 1 with a diameter of 32 mm through a stamping die, and then grinding the copper plate 1 by a grinding machine; step 2: spraying the copper plate 1 on the copper plate Evenly spray glaze on the upper surface of the copper plate 1 to form an underglaze layer 2; Step 3: put the copper plate 1 sprayed with the underglaze layer 2 into a dryer for drying, and wait for the underglaze layer 2 and the copper plate 1 When connected as a whole, the upper surface of the bottom glaze layer 2 is sprayed with glaze again by a spraying machine, and the top glaze layer 3 is formed on the top surface of the bottom glaze layer 2; Step 4: Put the copper plate 1 sprayed with the top glaze lay...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Depthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a decorated enameled part. The decorated enameled part comprises a copper plate, wherein a bottom glaze layer is arranged at the top of the copper plate, an over glaze layer isarranged at the top of the bottom glaze layer, a color glaze layer is arranged at the top of the over glaze layer, a groove is formed in the color glaze layer, and a top glaze layer is arranged in the groove. A method comprises the following steps that step 1, a copper material is punched into a copper plate with a diameter of 32 mm through a punching die, and then the copper plate is polished through a polishing machine; and step 2, glaze is uniformly sprayed on the upper surface of the copper plate through a spraying machine to form the bottom glaze layer on the upper surface of the copperplate. Compared with silk-screen printing and spray painting, operation difficulty and operation steps are greatly reduced through the floral design pressed by the die, decorated enameled part is thesame as production glaze powder in raw materials, material taking is facilitated, the matching problem of the glaze and the bottom glaze and the over glaze of a bottom blank is not required to be worried out, the polished production surplus is further be used for manufacturing the next workpiece, the production cost is effectively reduced, and the decorated enameled part is beneficial to people touse.

Description

technical field [0001] The invention relates to the technical field of decorative enamel parts, in particular to decorative enamel parts. Background technique [0002] Enamel, also known as Fulang, Fulang, and blue, is made of mineral silicon, red lead, borax, feldspar, quartz and other raw materials mixed in appropriate proportions, and various colored metal oxides are added respectively, and are roasted and ground. After being crushed into powdered color materials, they are filled or painted on the body of the metal tire according to the different methods of enamel technology, and then baked to become enamel products. High-temperature transparent enamel: it is melted at high temperature. Enamel fired with transparent glaze. [0003] With the rapid development of social economy and culture, people's life is changing from food and clothing to well-off, advocating humanity and fashion, and constantly shaping personality and charm have become people's pursuit. Now clocks are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C1/00B44C1/24
Inventor 赵国柱
Owner SHENZHEN ZHONGBAOYING JEWELRY TECH CO LTD