Adhesive for tiles and preparation method of adhesive

A technology of tile adhesive and redispersed latex powder, which is applied in the field of building materials, can solve the problems of high hardness, easy cracking of brick surface, high alkalinity, etc., and achieve the effect of high bonding strength, good corrosion resistance and uniform distribution

Inactive Publication Date: 2019-05-14
陈谓清
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the tile glue used in the prior art has high alkalinity, which is easy to corrode the tiles and cause the tile surface to change color; and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive for tiles and preparation method of adhesive
  • Adhesive for tiles and preparation method of adhesive

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] Yet another embodiment of the present invention provides a kind of preparation method of above-mentioned tile glue, comprises the following steps:

[0041] Step 1: Preparation of powdery materials: take the Yellow River sediment, dry fine sand and silt and transport them to the feeder and pulverizer in turn, put them in the dryer for drying, and then sieve to obtain powdery materials of 200-300 mesh;

[0042] Step 2: Preparation of rosin saponification: Take rosin, sodium hydroxide and water and put them into a reaction kettle and heat at 160-190°C for 20-40 minutes to obtain a brown transparent paste. Put the paste into a vacuum of 93.3-98.6KPa. Dry the body in a vacuum oven at a temperature of 60-80°C for 5-7 hours, and then pulverize to obtain saponified rosin;

[0043] Step 3: Preparation of tile adhesive: Take the cement and the powdered material obtained in Step 1 and add them to the mixer, stir in a dry state for 1 to 2 minutes, then add water-soluble silicate, red...

Embodiment 1

[0046] Embodiment 1: a kind of tile adhesive, comprising the following raw material components in parts by weight: comprising the raw material components in the following parts by weight: 25 parts of Yellow River silt, 35 parts of dry fine sand, 10 parts of silt, 20 parts cement, 2 parts of rosin saponification, 5 parts of water-soluble silicate, 1 part of redispersible latex powder, 2 parts of micro-expansion agent, 0.5 part of water reducer, 0.2 part of superplasticizer, 5 parts of thickener and 0.1 part of anti-crack fiber.

[0047] Said rosin saponified product comprises parts by weight of 70 parts of rosin, 10 parts of sodium hydroxide and 120 parts of water; said micro-swelling agent is calcium magnesium oxide and calcium sulfoaluminate; said redispersible latex powder is Styrene-acrylic acid copolymer latex powder; the water reducer is melamine; the superplasticizer includes vinyl acetate-ethylene copolymer dry powder and polyethylene dry powder; the thickener includes ...

Embodiment 2

[0052] Embodiment 2: a kind of tile adhesive, comprising the following raw material components in parts by weight: comprising the following raw material components in parts by weight: 35 parts of Yellow River silt, 30 parts of dry fine sand, 20 parts of silt, 12 parts cement, 6 parts of rosin saponification, 3 parts of water-soluble silicate, 2 parts of redispersible latex powder, 1.5 parts of micro-expansion agent, 2 parts of water reducing agent, 1.5 parts of superplasticizer, 3 parts thickener and 1.4 parts anti-crack fiber.

[0053] Said rosin saponified product comprises parts by weight of 60 parts of rosin, 16 parts of sodium hydroxide and 89 parts of water; said micro-swelling agent is calcium magnesium oxide and calcium sulfoaluminate; said redispersible latex powder is Ethylene-vinyl acetate copolymer latex powder; the water reducer is polycarboxylic acid; the superplasticizer is polyacrylate dry powder; the thickener includes a mixture of polyacrylamide, polyvinyl al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of building materials, in particular to an adhesive for tiles and a preparation method of the adhesive. The adhesive comprises, by weight, 25-38 parts of Yellow River sediments, 20-35 parts of dry fine sand, 10-25 parts of sludge, 12-20 parts of cement, 2-10 parts of rosin saponified products, 1-5 parts of water-soluble silicate, 1-5 parts of re-dispersible latex powder and 0.2-2 parts of micro-expansion agents. The adhesive for the tiles has high bonding strength, water resistance, corrosion resistance and thermal aging resistance (70 DEC C), and can withstand tests in which wet and dry conditions alternate or freezing and thawing conditions alternate, completely solving the problems of whiskering, hollowing and peeling of the tiles.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a tile adhesive and a preparation method thereof. Background technique [0002] Tile glue, also known as ceramic tile adhesive, is mainly used to paste decorative materials such as ceramic tiles, facing tiles, and floor tiles. Its main features are high bonding strength, water resistance, freeze-thaw resistance, good aging resistance and convenient construction. It is a very ideal bonding material. Tile adhesives contain a variety of additives, specifically the functionality of tile adhesives. Generally, cellulose ethers that provide water retention and thickening effects are added to tile adhesives, as well as latex powders that increase the adhesion of tile adhesives. The most common latex powders are vinyl acetate / vinyl ester copolymers, vinyl laurate / ethylene / vinyl chloride Copolymer, acrylic and other additives, the addition of latex powder can greatly increase ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00
Inventor 陈谓清
Owner 陈谓清
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap