A kind of preparation method of anti-ultraviolet polyester fabric suitable for outdoor operation

An anti-ultraviolet and outdoor operation technology, which is applied in the field of preparation of anti-ultraviolet polyester fabrics, can solve the problems that the anti-ultraviolet performance needs to be improved and the requirements for anti-ultraviolet performance are very high, and achieve good anti-ultraviolet performance, good anti-ultraviolet effect, and improved breaking strength Effect

Active Publication Date: 2021-10-01
杭州新尚科技咨询有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The fiber has good wearing performance and flame retardant performance, but outdoor operations generally require very high anti-ultraviolet performance, and the effect of this fiber in terms of anti-ultraviolet performance needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of an anti-ultraviolet polyester fabric suitable for outdoor operations is carried out according to the following steps:

[0031] A, the raw vermiculite is ground to powder, and the raw vermiculite powder of the micron scale is screened out;

[0032] B. Dry the raw vermiculite powder at 55°C for 14 hours to remove the moisture on the surface of the raw vermiculite powder;

[0033] C. Add the raw vermiculite powder into the polyester chips, heat and stir, and control the process of heating from room temperature to 205°C for 4-8 hours;

[0034] D. Continue heating to 315°C and keep it warm for 30 minutes to obtain molten modified polyester;

[0035] E. The modified polyester chips are spun at high speed on a spinning machine to make nascent fibers. The specific process conditions are: spinning temperature 335°C, spinning speed 1380m / min;

[0036] F, the as-spun fiber is adopted parallel drawing machine to carry out shaping, obtains polyester fiber, ...

Embodiment 2

[0045] A preparation method of an anti-ultraviolet polyester fabric suitable for outdoor operations is carried out according to the following steps:

[0046] A, the raw vermiculite is ground to powder, and the raw vermiculite powder of the micron scale is screened out;

[0047] B. Dry the raw vermiculite powder at 60°C for 12 hours to remove the moisture on the surface of the raw vermiculite powder;

[0048] C. Add the raw vermiculite powder into the polyester chips, heat and stir, and control the process of heating from room temperature to 210°C for 4 hours;

[0049] D. Continue heating to 310°C and keep it warm for 40 minutes to obtain molten modified polyester;

[0050] E. The modified polyester chips are spun at high speed on a spinning machine to make nascent fibers. The specific process conditions are: spinning temperature 320°C, spinning speed 1450m / min;

[0051]F, the as-spun fiber is adopted parallel drawing machine to carry out shaping, obtains polyester fiber, and...

Embodiment 3

[0060] A preparation method of an anti-ultraviolet polyester fabric suitable for outdoor operations is carried out according to the following steps:

[0061] A, the raw vermiculite is ground to powder, and the raw vermiculite powder of the micron scale is screened out;

[0062] B. Dry the raw vermiculite powder at 50°C for 16 hours to remove the moisture on the surface of the raw vermiculite powder;

[0063] C. Add the raw vermiculite powder into the polyester chips, heat and stir, and control the process of heating from room temperature to 200°C for 8 hours;

[0064] D. Continue heating to 320°C and keep it warm for 25 minutes to obtain molten modified polyester;

[0065] E. The modified polyester chips are spun at high speed on a spinning machine to make nascent fibers. The specific process conditions are: spinning temperature 350°C, spinning speed 1300m / min;

[0066] F, the as-spun fiber is adopted parallel drawing machine to carry out shaping, obtains polyester fiber, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of an anti-ultraviolet polyester fabric suitable for outdoor operations, which is carried out according to the following steps: the raw vermiculite is ground to a powder state, and the raw vermiculite powder of the micron scale is screened out; The raw vermiculite powder is heated and dried; the raw vermiculite powder is added to the polyester chip, heated and stirred; the heating is continued and the heat is kept to obtain a molten state modified polyester; the modified polyester chip is spun at a high speed on a spinning machine to form a primary fiber; adopt the parallel drawing machine to shape the nascent fiber to obtain polyester fiber; weave the polyester fiber into polyester fabric by conventional method; dye the polyester fabric to obtain the finished polyester fabric. The invention utilizes the special performance and structure of vermiculite and adopts a special fiber preparation method to obtain polyester fabrics with good ultraviolet resistance, and adds ternary copolymerization silicone softener for post-finishing, which can improve the color fixing effect and is suitable for dark colors. The color fixing effect of polyester fabrics is particularly remarkable.

Description

technical field [0001] The invention relates to the field of functional clothing fabrics, in particular to a method for preparing an anti-ultraviolet polyester fabric suitable for outdoor operations. Background technique [0002] As the most widely used chemical fiber, polyester fiber has good fiber-forming and mechanical properties, high strength, good light resistance, heat resistance and acid and alkali resistance, good processability and spinnability, and can be purely spun or blended and interweave. Polyester fabrics are washable, wear-resistant, non-ironing and wrinkle-resistant, and are widely used in clothing, home textiles, decoration and product applications. However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor anti-static ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fiber. In order to improve the wearing comfort of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10D06P1/34D06P3/52D06P5/08D06M15/643D06M101/32
Inventor 芦美玲
Owner 杭州新尚科技咨询有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com