Thick high-strength ultra-wear-resistant non-energy absorbing floor material and preparation method thereof

A floor material and high-strength technology, applied in the field of thick floor materials and their preparation, can solve the problems that alloy wear-resistant floors are difficult to meet customer needs, the construction thickness is prone to hollowing, and the cleaning and sanitation are difficult. Good appearance quality, less impact damage to the floor, consistent overall color effect

Inactive Publication Date: 2017-05-31
黑龙江泽林科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing alloy wear-resistant floor has disadvantages such as insufficient strength, insufficient wear resistance, difficulty in cleaning and sanitation, short service life, and easy hollowing, cracking, delamination, and impact resistance when the construction thickness is high.
[0003] With the continuous improvement of people's requirements for clean production environment and high-strength wear-resistant, the current alloy wear-resistant floor is difficult to meet customer needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0019] Embodiment 1: A thick, high-strength, super wear-resistant and non-energy-absorbing floor material. The thick, high-strength, super-wear-resistant and non-energy-absorbing floor is composed of an integrated anti-aircraft drum air-permeable layer, high It is composed of strong non-energy-absorbing layer and high-strength surface layer;

[0020] The material of the air-proof drum air-permeable layer is composed of solid raw materials and water, and the solid raw materials of the air-proof drum air-permeable layer are composed of 90-110 parts by weight of high-grade PI Portland cement, 210-230 parts of 6-mesh emery , 55-60 parts of 8-mesh corundum, 5-7 parts of microsilica, 12-18 parts of ultra-fine powder, 0.6-1 part of water reducing agent, 1.2-2 parts of redispersible rubber powder, 8-11 parts of pigment, Composed of 0.1-0.5 parts of polypropylene fiber, 0.4-0.8 parts of titanium dioxide, 10-15 parts of tin-titanium alloy particles and 0.3-0.6 parts of water reducing ag...

specific Embodiment approach 2

[0023] Specific embodiment two: a kind of thick high-strength super wear-resistant non-energy-absorbing floor material described in specific embodiment one, the thickness of the thick high-strength super wear-resistant non-energy-absorbing floor is ≥ 8mm (the thickest energy-absorbing up to 50mm)

specific Embodiment approach 3

[0024] Specific embodiment three: the preparation method of the thick high-strength super wear-resistant non-energy-absorbing floor material described in specific embodiment one or two, the material preparation method of the air-proof drum air-permeable layer described is: first the above-mentioned parts by weight The microsilica fume, water reducer, redispersible rubber powder, polypropylene fiber, titanium dioxide, tin-titanium alloy particles and water reducer are added to the mixer for pre-mixing, and the mixture is evenly mixed to obtain the pre-mixed material of air-proof drum air-permeable layer , then add high-grade PI portland cement, 6-mesh corundum, 8-mesh corundum, superfine powder, pigments and solid raw materials for the air-proof drum air-permeable layer to the premix of the anti-aircraft drum air-permeable layer material 12% to 15% of the total weight of water is fully stirred and mixed to make the air-proof drum air-permeable layer material;

[0025] The mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Meshaaaaaaaaaa
Login to View More

Abstract

The invention relates to a thick high-strength ultra-wear-resistant non-energy absorbing floor material and a preparation method thereof, and belongs to the technical field of floor materials and preparation. A solid raw material of an anti-empty drum breathable layer consists of high-grade PI Portland cement, emery with 6 and 8 meshes, silica fume, superfine powder, a water-reducing agent, dispersible adhesive powder, a pigment, polypropylene fibers, titanium dioxide, tin and titanium alloy particles and a water-reducing agent; a solid raw material of a high-strength non-energy absorbing layer consists of high-grade PI Portland cement, emery with 6 and 8 meshes, emery with 40 and 70 meshes, tin and titanium alloy particles, silica fume, superfine powder, a pigment, titanium dioxide, a water-reducing agent and dispersible adhesive powder; a solid raw material of a high-strength surface layer consists of high-grade PI Portland cement, emery with 6 and 8 meshes, emery with 40 and 70 meshes, tin and titanium alloy particles, silica fume, superfine powder, a pigment, titanium dioxide, a water-reducing agent and dispersible adhesive powder. The thick high-strength ultra-wear-resistant non-energy absorbing floor material provided by the invention is used for preparing a thick high-strength ultra-wear-resistant non-energy absorbing floor.

Description

technical field [0001] The invention relates to a thick floor material and a preparation method thereof, belonging to the technical field of floor materials and preparation. Background technique [0002] As an economical and durable alloy wear-resistant material in floor engineering, it has good properties such as good impact resistance, strong weight resistance and strong anti-fouling ability. Widely used in various workshops, factories, parking lots, cargo loading and unloading areas, logistics centers and other places, the construction process is simple and fast, economical and applicable, can provide a variety of colors to meet the needs of different customers, and the color retention is also very good. However, the existing alloy wear-resistant floor has disadvantages such as insufficient strength, insufficient wear resistance, difficult cleaning and sanitation, short service life, and easy hollowing, cracking, delamination, and impact resistance when the construction t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00267C04B2111/00612C04B2111/60C04B2201/50C04B14/324C04B18/146C04B14/34C04B14/305C04B16/0633C04B2103/0057C04B2103/54C04B2103/302
Inventor 李云伟潘显兵
Owner 黑龙江泽林科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com