Method for preventing adhesion and clogging of mineral raw material
A technology of mineral raw materials and raw materials, applied in chemical instruments and methods, dry solid materials, transportation and packaging, etc., can solve problems such as pipe blockage, coal transportation efficiency reduction, thermal power plant power generation efficiency reduction, etc., to achieve effective transportation and prevent adhesion and clogging effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0061] (Example 1)
[0062] With respect to 1000 g of moist coal (water content of 15.5% by mass, particle size of 2 mm or less), 0.1% by mass of "KURILINE S-200" (manufactured by Kurita Industry Co., Ltd.; sodium polyacrylate) as a super absorbent resin is added and stirred uniformly After mixing, a sample of the raw material mixture was prepared.
[0063] Used in the upper part of the electric screen ("ANF-30", manufactured by Nitto Scientific Co., Ltd.), a simulated hopper is installed instead of the screen (input port: 200mm×200mm, discharge port: 30mm×50mm inverted quadrangular pyramid cone shape; made of steel ) Vibration test device, the adhesion evaluation test of the raw material mixture sample was carried out.
[0064] The adhesion evaluation was performed by putting the prepared raw material mixture sample into a simulation hopper of the vibration test device, and measuring the discharge time from the start of the input until it fell to the tray under the vibration test d...
Example
[0067] (Examples 2~4)
[0068] Except for changing the water content of coal and the addition amount of super absorbent resin as shown in Table 1 below, the discharge time of the raw material mixture sample was measured in the same manner as in Example 1.
Example
[0069] (Comparative Examples 1 and 2)
[0070] In Examples 1 and 3, except that the super absorbent resin was not added, the discharge time of the raw material mixture sample was measured in the same manner as in Example 1 except that the super absorbent resin was not added.
[0071] Table 1 shows the results of the adhesion evaluation test in each of the above-mentioned Examples and Comparative Examples.
[0072] [Table 1]
[0073] Table 1
[0074]
[0075] From the results shown in Table 1, it can be seen that by adding KURILINE S-200 to the wet coal, the discharge time of the raw material mixture sample from the simulated hopper was shortened, and it was confirmed that adhesion was suppressed.
[0076] In addition, visual observation of the upper part of the simulated hopper after the test confirmed that the adhesion amount of the raw material mixture sample was reduced.
[0077] It can be said that by adding KURILINE S-200 to wet coal, the adhesion of coal to the contact surface of th...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap