A technology of composite materials and surgical packs, which is applied in the field of surgical pack materials, can solve the problems that the surgical pack materials are difficult to meet the functional requirements, and achieve the effects of reduced sterilization links, good toughness, and simple preparation process

Inactive Publication Date: 2019-06-07
安徽汉邦希瑞医疗器械有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a kind of composite material and its method for making elastic surgical bag, to solve the above-mentioned background technology when in use, need external fire prevention, waterproof, the effect of internal drying and sterilization, and in material selection It is necessary to ensure softness and toughness to avoid hand-wringing and easy tearing. The existing surgical bag materials are difficult to meet the above functional requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite material for manufacturing elastic operating instrument sets, and preparation method thereof
  • Composite material for manufacturing elastic operating instrument sets, and preparation method thereof
  • Composite material for manufacturing elastic operating instrument sets, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The specific steps of the preparation method for making the composite material of the elastic surgical bag are as follows:

[0042] S1: Coat the raw material of styrene-butadiene rubber evenly on the surface of the carrier: use smooth stainless steel as the carrier, apply anti-stick oil film coating on the surface of the stainless steel carrier in advance, and evenly coat the heated styrene-butadiene rubber raw material on the carrier On the surface of the styrene-butadiene rubber and cis-butadiene rubber mixed raw materials are cooled and formed to obtain the styrene-butadiene rubber base layer, and the thickness of the styrene-butadiene rubber base layer is 0.1mm;

[0043] S2: Pave nano-silver antibacterial coating on the formed styrene-butadiene rubber base: uniformly spray hot-melt adhesive on one side surface of the styrene-butadiene rubber base obtained in step S1, and spray nano-silver antibacterial coating on the hot-melt adhesive, The thickness of nano-silver a...

Embodiment 2

[0048] The specific steps of the preparation method for making the composite material of the elastic surgical bag are as follows:

[0049] S1: Coat the raw material of styrene-butadiene rubber evenly on the surface of the carrier: use smooth stainless steel as the carrier, apply anti-stick oil film coating on the surface of the stainless steel carrier in advance, and evenly coat the heated styrene-butadiene rubber raw material on the carrier On the surface of the styrene-butadiene rubber and cis-butadiene rubber mixed raw materials are cooled and formed to obtain the styrene-butadiene rubber base layer, and the thickness of the styrene-butadiene rubber base layer is 0.175mm;

[0050] S2: Pave nano-silver antibacterial coating on the formed styrene-butadiene rubber base: uniformly spray hot-melt adhesive on one side surface of the styrene-butadiene rubber base obtained in step S1, and spray nano-silver antibacterial coating on the hot-melt adhesive, The thickness of nano-silver a...

Embodiment 3

[0055] The specific steps of the preparation method for making the composite material of the elastic surgical bag are as follows:

[0056] S1: Coat the raw material of styrene-butadiene rubber evenly on the surface of the carrier: use smooth stainless steel as the carrier, apply anti-stick oil film coating on the surface of the stainless steel carrier in advance, and evenly coat the heated styrene-butadiene rubber raw material on the carrier On the surface of the styrene-butadiene rubber and cis-butadiene rubber mixed raw materials are cooled and formed to obtain the styrene-butadiene rubber base layer, and the thickness of the styrene-butadiene rubber base layer is 0.25mm;

[0057] S2: Pave nano-silver antibacterial coating on the formed styrene-butadiene rubber base: uniformly spray hot-melt adhesive on one side surface of the styrene-butadiene rubber base obtained in step S1, and spray nano-silver antibacterial coating on the hot-melt adhesive, The thickness of nano-silver ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of operating instrument set materials, and concretely relates to a composite material for manufacturing elastic operating instrument sets, and a preparation method thereof. The composite material for manufacturing elastic operating instrument sets comprises an elastic layer, and a fireproof layer and a sterilizing layer which are respectively arranged on two sidewalls of the elastic layer, a waterproof layer is arranged on the other surface of the fireproof layer, and a water absorbing layer is arranged on the other surface of the sterilizing layer.The preparation method of the composite material for manufacturing elastic operating instrument sets concretely comprises the following steps: S1, uniformly coating the surface of a carrier with an elastic layer raw material; S2, laying the sterilizing layer on the formed elastic layer; S3, bonding the water absorbing layer to the sterilizing layer; S4, arranging the fireproof layer on the othersurface of the elastic layer; and S5, arranging the waterproof layer on the surface of the fireproof layer. The preparation process is simple, and the finished product has the characteristics of goodtoughness and softness.

Description

technical field [0001] The invention relates to the technical field of surgical pack materials, in particular to a composite material for manufacturing elastic surgical packs and a method thereof. Background technique [0002] With the continuous development of clinical medicine, biomedical elastomer materials have been more and more widely used. Surgical packs are usually composed of large cloth, surgical drapes and Meiya bags, and other surgical accessories are added according to surgical requirements. Surgical drapes are the core of the entire surgical package. The materials used for surgical drapes are composite materials; their main characteristics are good water resistance (water-blocking non-woven fabric), good water absorption (water-absorbent non-woven fabric), high hydrostatic pressure, and flexibility. Good strength, less lint, imported adhesive (non-allergic), antistatic, anti-alcohol, anti-plasma, anti-oil, etc.; but the existing surgical kits have the problems...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B25/10B32B33/00B32B37/00B32B37/06B32B37/10B32B37/12A61B46/20
Inventor 靳呈标王艳艳陈志云许会国张启超张丹丹夏秀芳
Owner 安徽汉邦希瑞医疗器械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap