Aqueous metallic color paste for latex balloon with metallic glitter effect and preparation method and latex balloon

A technology of metallic flash and metallic color, which is applied in the field of latex balloons to achieve the effect of increasing compatibility

Active Publication Date: 2022-07-29
绍兴奥唯特纳米科技有限公司
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although my country is the main production place of latex balloons, the technical problem of flatulence and gelation between the aluminum powder (hermaphrodite) and the natural latex (strongly alkaline) of the balloon raw material has not been solved in China due to the water-based aluminum paste, the raw material for making metal balloons. , which has been imported by foreign American pioneer companies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous metallic color paste for latex balloon with metallic glitter effect and preparation method and latex balloon

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A water-based metallic color paste for latex balloons with metallic glitter effect, the raw material formula of the color paste is composed of component A and component B in parts by weight; component A includes 20 parts of water-based aluminum pigment, 20 parts of water-based polyurethane resin, 10 parts of water-based 1 part of water-based acrylic emulsion, 1 part of water-based CAB, 10 parts of cosolvent, 0.5 part of compounding auxiliaries, 1 part of nano-silicon dioxide, 10 parts of deionized water; the remaining parts are component B, group Part B is an aqueous transparent pigment paste. The solid content of the water-based aluminum pigment is 50%, the fineness D90 is less than 30 μm, and the D50 is less than 15 μm. The water-based polyurethane resin is an anionic water-based aliphatic polyurethane resin with a solid content of 33%, a 100% modulus > 4mpa, and an elongation > 400%. The water-based acrylic emulsion is a water-based nano-pure acrylic emulsion with a...

Embodiment 2

[0035] A water-based metal color paste for latex balloons with metallic glitter effect, the raw material formula of the color paste is composed of component A and component B in parts by weight; component A includes 30 parts of water-based aluminum pigment, 30 parts of water-based polyurethane resin, 20 parts of water-based parts of water-based acrylic emulsion, 5 parts of water-based CAB, 15 parts of cosolvent, 3 parts of compounding auxiliary, 5 parts of nano-silica, 30 parts of deionized water; the remaining parts are component B, group Part B is an aqueous transparent pigment paste. The solid content of the water-based aluminum pigment is 80%, the fineness D90 is less than 30 μm, and the D50 is less than 15 μm. The water-based polyurethane resin is an anionic water-based aliphatic polyurethane resin with a solid content of 37%, a 100% modulus > 4mpa, and an elongation > 400%. The aqueous acrylic emulsion is an aqueous nano-pure acrylic emulsion with a solid content of 49%...

Embodiment 3

[0044] A water-based metal color paste for latex balloons with metallic glitter effect, the raw material formula of the color paste is composed of component A and component B in parts by weight; component A includes 25 parts of water-based aluminum pigment, 25 parts of water-based polyurethane resin, 15 parts of water-based 1 part of water-based acrylic emulsion, 3 parts of water-based CAB, 12 parts of cosolvent, 1 part of compounding auxiliary, 2 parts of nano-silica, 24 parts of deionized water; Component B is 16 parts of water-based transparent Pigment paste. The solid content of water-based aluminum pigment is 70%, the fineness D90 is less than 30μm, and the D50 is less than 15μm. The water-based polyurethane resin is an anionic water-based aliphatic polyurethane resin with a solid content of 35%, a 100% modulus > 4mpa, and an elongation > 400%. The water-based acrylic emulsion is a water-based nano-pure acrylic emulsion with a solid content of 48% and a particle size of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
elongationaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous metallic color paste for a latex balloon with a metallic glitter effect, a preparation method and a latex balloon. The water-based metal paste is composed of component A and component B in parts by weight; component A includes 1-5 parts of water-based CAB resin dispersion, 20-30 parts of water-based aluminum pigment, and 10-20 parts of water-based acrylic resin Emulsion, 20-30 parts of water-based polyurethane resin dispersion, 1-5 parts of nano-silica, 10-15 parts of cosolvent, 0.5-3 parts of auxiliary agent, 10-30 parts of deionized water; components B includes 10-30 parts of water-based transparent pigment paste. The novel water-based metal color paste prepared by the preparation method of the present invention effectively and completely solves the problem of adding aluminum pigments to the strong alkaline natural latex to gel, so that the prepared metal latex gas not only has a strong metal flash effect, but also The surface is smooth, does not lose aluminum pigment, and has the characteristics of good adhesion and flexibility of balloon products. At the same time, the latex metal balloon prepared with the water-based metal color paste of the present invention is non-toxic and tasteless.

Description

technical field [0001] The present invention relates to a water-based metallic color paste that can make latex pieces have a metallic glitter effect. The present invention also relates to a preparation method of a latex balloon using the above-mentioned color paste. Latex balloons. Background technique [0002] At present, the demand for metal balloons in foreign countries, especially in Europe, America and Southeast Asia, is gradually increasing. Because of its bright and bright colors, it is deeply loved by users. Although my country is the main producer of latex balloons, due to the fact that the water-based aluminum paste, which is the raw material for making metal balloons, has not been able to solve the technical problem of flatulence and gelation between aluminum powder (which is bisexual) and natural latex (strong alkaline), the raw material of balloons. , which has been imported by foreign American pioneer companies. Our company has overcome this problem through it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/04C08L33/04C08L1/14C08K3/08C08K3/36
Inventor 沈冠华
Owner 绍兴奥唯特纳米科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com