Epoxy heating fiberglass mould and preparation method thereof

A glass fiber reinforced plastic mold and mold technology, which is applied to household appliances, other household appliances, household components, etc., can solve the problems of heating mode mold damage and other problems

Pending Publication Date: 2019-07-26
XIAMEN HANSHENG YACHT BUILDING
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the defects existing in the prior art, the present invention provides an epoxy heated FRP mold and its preparation method; on the premise of reducing the manufacturing cost of the hea

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy heating fiberglass mould and preparation method thereof
  • Epoxy heating fiberglass mould and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0114] In order to make the technical problems, technical solutions and beneficial effects to be solved by the present invention clearer and clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0115] Such as figure 1 - figure 2 Shown is an embodiment of the present invention.

[0116] An epoxy heated glass fiber reinforced plastic mold, comprising a mold body 6 that cooperates with each other, a silicone mold is attached to the upper surface of the mold body, wherein a heating device 7 is arranged in the mold body 6, and the silicone mold includes a concave mold 5 and a convex mold 1 that cooperate with each other , the die 5 is attached to the upper surface of the mold body 6, the punch 1 is arranged above the die 5, a vacuum cavity 8 is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an epoxy heating fiberglass mould and a preparation method thereof. The preparation method comprises the following steps including female mould manufacturing, mould structural manufacturing; gel coat manufacturing; topcoat manufacturing; heating layer manufacturing; structural reinforcing layer manufacturing; heat preservation layer manufacturing; framework support manufacturing; temperature control system manufacturing; and silica gel surface mould manufacturing. The epoxy heating mould meets the requirements that the high temperature deformation temperature is above 120 DEG C, the shrinking percentage is low, and heating is uniform, and the technical problem that local overheating damages the mould is solved.

Description

[0001] Technical field: [0002] The invention belongs to the field of glass fiber reinforced plastic manufacturing, and in particular relates to an epoxy heated glass fiber reinforced plastic mold and a preparation method thereof. [0003] Background technique: [0004] As the automobile industry and end customers have higher and higher requirements for automobiles, as well as high requirements for the strength and deformation of FRP in other high-end fields of composite materials, such high requirements need to be solved from at least three aspects: the first First, the problem of low shrinkage resin; second, the problem of molding process; third, the problem of curing degree during demoulding. [0005] To solve the three problems raised above, we need to start from the mold. Of course, the metal mold can best meet the above conditions. However, due to the high manufacturing cost, the products we are currently in contact with do not meet the batch manufacturing requirements o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C70/44B29C70/46B29C33/02B29C33/10B29C33/38B29L31/30
CPCB29C70/443B29C70/46B29C33/02B29C33/10B29C33/3842B29L2031/30
Inventor 刘观勋林贵阳吴家生
Owner XIAMEN HANSHENG YACHT BUILDING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap