Artificial water-permeable cobblestone and preparation method thereof

A pebble and man-made technology, applied in the field of pebbles, can solve the problems of smooth and impermeable pebbles, achieve the effects of good water permeability, enhanced adhesion ability, and improved service life

Inactive Publication Date: 2019-08-09
GUANGDONG TSINGDA TONGKE ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide an artificial permeable cobblestone and its preparation method to solve the problem of smooth and impermeable cobblestone, thereby effectively improving the problem of water accumulation on the cobblestone pavement and improving the anti-skid effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An artificial permeable pebble, including an outer layer and an inner layer; the outer layer is prepared from the following raw materials: 50g of white pottery sand with a particle size of 0.2-0.4mm, 50g of black pottery sand, 25g of P.O 42.5 white cement, and redispersible latex Powder 2.5g, metakaolin 2g, polycarboxylate superplasticizer 0.2g, 1wt% polyvinyl alcohol solution 5g; the inner layer is prepared from the following raw materials: 2000g of stones with a particle size of 3-7mm, 400g of sand, P.O 42.5 grade ash 500g of cement, 5g of redispersible latex powder, 10g of silica fume, 2.5g of polycarboxylate superplasticizer, and 150g of water.

[0025] The preparation method of artificial permeable cobblestone in the present embodiment, comprises the following steps:

[0026] (1) Take the outer layer solid raw material and the inner layer raw material respectively according to the formula requirements, and the two are respectively mixed uniformly for use;

[0027]...

Embodiment 2

[0030] An artificial permeable pebble, comprising an outer layer and an inner layer; the outer layer is prepared from the following raw materials: 50g of red natural colored sand, 50g of white natural colored sand, and 50g of black natural colored sand with a particle size of 0.25-0.4mm, P. O52.5 white cement 36g, redispersible latex powder 3g, metakaolin 1.2g, naphthalene superplasticizer 0.3g, 1wt% polyvinyl alcohol solution 7.2g; the inner layer is prepared from the following raw materials: the particle size is 3 -7mm ceramsite 2000g, sand 500g, P.O 42.5 gray cement 600g, redispersible latex powder 3g, fly ash 15g, naphthalene superplasticizer 2.2g, water 120g.

[0031] The preparation method of artificial permeable cobblestone in the present embodiment, comprises the following steps:

[0032] (1) Take the outer layer solid raw material and the inner layer raw material respectively according to the formula requirements, and the two are respectively mixed uniformly for use; ...

Embodiment 3

[0036] An artificial permeable cobblestone, including an outer layer and an inner layer; the outer layer is prepared from the following raw materials: 60g of yellow ceramic spray granulation powder with a particle size of 0.15-0.4mm, 60g of white ceramic spray granulation powder, and black ceramic spray granulation powder. Granular powder 60g, P.O52.5 white cement 45g, redispersible latex powder 5.4g, fly ash 1.5g, aliphatic superplasticizer 0.3g, 1wt% polyvinyl alcohol solution 6g; the inner layer is prepared from the following raw materials Preparation: 2000g of ceramsite with a particle size of 3-7mm, 400g of sand, 600g of P.O 52.5 grade gray cement, 2g of redispersible latex powder, 24g of silica fume, 2.4g of polycarboxylate superplasticizer, and 110g of water.

[0037] The preparation method of artificial permeable cobblestone in the present embodiment, comprises the following steps:

[0038] (1) Take the outer layer solid raw material and the inner layer raw material re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to artificial water-permeable cobblestone and a preparation method thereof. The artificial water-permeable cobblestone comprises an outer layer and an inner layer, wherein the outer layer is prepared from the following raw materials by weight: 100 parts of outer layer aggregate, 25-45 parts of cement, 2.5-4 parts of redispersible latex powder, 0.2-3 part of a cement alkali inhibitor, 0.1-0.6 part of a water reducing agent, and 2-10 parts of a 1 wt% polyvinyl alcohol solution, the inner layer is prepared from the following raw materials by weight: 100 parts of inner layeraggregate, 20-45 parts of sand, 25-50 parts of cement, 0.1-0.8 part of redispersible latex powder, 0.5-3.5 parts of a cement alkali inhibitor, 0.1-0.8 part of a water reducing agent, and 6-28 parts ofwater, the particle size of the inner layer particles is 1-5 cm, and the outer layer has a coating thickness of 5-10 mm. According to the present invention, the outer layer aggregate is the sphericalparticles, such that the prepared water-permeable cobblestone has good water permeability, the water permeability coefficient is more than 2*10<-2> cm / s, the water accumulation problem on the cobblestone pavement is effectively improved, and the artificial water-permeable cobblestone of the present invention has anti-slip function compared with natural cobblestone pavement.

Description

technical field [0001] The invention relates to a pebble, in particular to an artificial permeable pebble and a preparation method thereof. Background technique [0002] In recent years, in order to get close to nature, there are more and more cobblestone pavements in cities, especially in park paths, garden pavements, square pavements, tourist mountain pavements, and community fitness ground pavements, etc. It is very common to use various cobblestone pavements. Because the cobblestone pavement can not only be configured with different patterns according to the needs, but also has a beautiful appearance and is closer to nature, and people walking on it has the effect of fitness. However, at present, water-blocking materials such as concrete and resin are used to pave cobblestone pavement, and the cobblestone itself is smooth and impermeable, which makes the cobblestone pavement easy to accumulate water in rainy days, and at the same time has poor slip resistance, and pedest...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B38/00C04B111/54C04B111/82
CPCC04B28/04C04B2111/00284C04B2111/00612C04B2111/0075C04B2111/542C04B2111/82C04B14/02C04B2103/0057C04B14/106C04B2103/302C04B24/2623C04B38/0041C04B14/06C04B18/146C04B24/226C04B18/08C04B24/166
Inventor 张宏生李伟雄胡毅耕贺新明
Owner GUANGDONG TSINGDA TONGKE ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com