Process method for decreasing water content of chromic hydroxide

A technology of chromium hydroxide and moisture content, which is applied in the direction of lighting and heating equipment, drying, furnace type, etc., can solve the problem of large investment in drying equipment system for cement-like materials, easy bonding of chromium hydroxide wet base, moisture content, etc. Baking can not meet the requirements and other problems, to achieve the effect of shortening the construction time, avoiding excessive water content, improving production efficiency and heat utilization rate

Inactive Publication Date: 2019-10-01
四川聚力金属制品有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a process method for reducing the moisture content of chromium hydroxide, which has the advantages of reducing the moisture content of chromium hydroxide, etc., and solves the difficulty in equipment selection, which is prone to moisture baking Problems such as failure to meet the requirements and easy bonding of chromium hydroxide wet base seriously affect the normal production and processing, and the investment cost of the cement-like material drying equipment system is relatively large, generally about 4 million yuan, and the equipment covers a large area, and the construction The problem of long construction period

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0017] The invention provides a method for controlling the content of mud in the preparation of expanded slag ceramsite, comprising the following steps:

[0018] 1) Preparation work, prepare a waste slag cooler, dryer and fan, and let professional technicians survey the site on the existing site, and arrange the corresponding equipment according to the site conditions to ensure the equipment installation Reasonable;

[0019] 2) Preliminary improvement, using the original wast...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of production of chromic hydroxide, and discloses a process method for decreasing water content of chromic hydroxide. The method comprises the following steps: 1) preparing; 2) primarily improving; 3) upgrading equipment; and 4) improving discharging. According to the method, an original wasted and old slag cooling machine is reconstructed, so that theproduction cost is saved, and the construction time is reduced; and meanwhile, the area occupied by equipment is reduced; professionals make survey of a field and arrange corresponding equipment basedon the field condition, so that the equipment mounting reasonability is conveniently ensured; the problems of disordered equipment mounting and potential risk can be prevented; a discharging port ofthe wasted and cold slag cooling machine is improved and facilitates the feeding of materials, and thus the feeding capacity is high; the discharging port is prevented from being excessively small tocause material blockage; and a propelling device in the slag cooling machine is improved and facilitates the propelling of cement type materials.

Description

technical field [0001] The invention relates to the technical field of chromium hydroxide production, in particular to a process method for reducing the moisture content of chromium hydroxide. Background technique [0002] Chromium hydroxide, amphoteric hydroxide, is a gray-green powder, insoluble in water, easily soluble in acid to form trivalent chromium ions, soluble in strong alkali to form a bright green solution, begins to decompose at 400°C, and completely decomposes into chromium oxide green at 500°C , for the preparation of trivalent chromium salts and dichromium trioxide, chemical reagents, and also for paint pigments and wool treatment, etc., for the preparation of chromium pigments and chromium salts, etc., for the manufacture of chromium salts and pigments, the current domestic vanadium market The price continues to rise, and the price has reached the highest level in the past ten years. The company maximizes production and increases vanadium production, so as t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F26B3/04F26B17/00F26B21/00F26B25/22
CPCF26B3/04F26B17/00F26B21/004F26B25/22Y02P70/10
Inventor 彭望汤波向明勇唐运成
Owner 四川聚力金属制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products